key: cord-0777898-dqoqf770 authors: De Monte, Cristina; Locritani, Marina; Merlino, Silvia; Ricci, Lucia; Pistolesi, Agnese; Bronco, Simona title: An In Situ Experiment to Evaluate the Aging and Degradation Phenomena Induced by Marine Environment Conditions on Commercial Plastic Granules date: 2022-03-10 journal: Polymers (Basel) DOI: 10.3390/polym14061111 sha: 4c6ec2041889cf59d58f3dc38f4bffdd28bb6b38 doc_id: 777898 cord_uid: dqoqf770 In this paper, we present two novel experimental setups specifically designed to perform in situ long-term monitoring of the aging behaviour of commercial plastic granules (HDPE, PP, PLA and PBAT). The results of the first six months of a three year monitoring campaign are presented. The two experimental setups consist of: (i) special cages positioned close to the sea floor at a depth of about 10 m, and (ii) a box containing sand exposed to atmospheric agents to simulate the surface of a beach. Starting from March 2020, plastic granules were put into the cages and plunged in seawater and in a sandboxe. Chemical spectroscopic and thermal analyses (GPC, SEM, FTIR-ATR, DSC, TGA) were performed on the granules before and after exposure to natural elements for six months, in order to identify the physical-chemical modifications occurring in marine environmental conditions (both in seawater and in sandy coastal conditions). Changes in colour, surface morphology, chemical composition, thermal properties, molecular weight and polydispersity, showed the different influences of the environmental conditions. Photooxidative reaction pathways were prevalent in the sandbox. Abrasive phenomena acted specially in the sea environment. PLA and PBAT did not show significant degradation after six months, making the possible reduction of marine pollution due to this process negligible. The United Nations Environment Programme (UNEP) defines "marine litter" as "any persistent, manufactured or processed solid material discarded, disposed of, or abandoned in the marine and coastal environment", including items made of metals, wood, glass, polymeric materials and some other materials [1] . The amount of marine litter has increased enormously since the middle of the twentieth century, when the awareness of the problem first started to grow, so much so that its size is tentatively considered as one of the factors defining the time boundaries of a new geological era. Many studies confirm that plastic is the main component of marine litter [2] [3] [4] . However, this quantity can be roughly estimated only and existing reports lead to different results [5] . In 2020, Napper and Thompson established that more than 75% of "marine litters" are plastics [6] . Polymers by their nature do not chemically degrade significantly in the marine environment and, transported by currents, end up accumulating and being deposited on beaches, in the sea (surface, seabed and water column) and even in Arctic Sea ice, depending on the specific density of the materials [7] [8] [9] [10] . For decades, plastic debris in the oceans, coastlines and sea floor has been of great concern as a conspicuous form of pollution [11] [12] [13] [14] [15] [16] [17] [18] . In 2021, Ali et al. analysing many studies in recent years, related the abundance of use of various plastics to the abundance of plastic waste dispersed in the environment (air, soil, water) and the consequent negative impact on the environment, animals (in terms of health and food chain), humans (inhalation, ingestion, food chain) and human health [19] . The exposure of macro and meso-plastics (>5 mm) to mechanical, chemical, and biological degradation can lead to their breakdown into smaller pieces at the scale of microplastics, defined as plastic particles with a size of 1 µm to 5 mm [20] , or even nanoparticles <1 µm [6, 13, [21] [22] [23] [24] [25] [26] . Photooxidation, in particular, leads to the weakening and fracturing of polymers, giving rise to so called "second generation microplastics". There are also "first generation microplastics" ( [5, 11, 22, 27] ) that are directly introduced into the marine environment in the form in which they were industrially produced (e.g., microbeads, resin pellets or pre-production granules) [28] . Micro and nanoplastic can be composed of different plastic polymers, such as, among others: polyethylene terephthalate (PET); high-density polyethylene (HDPE); polyvinyl chloride (PVC), which can also vary as rigid PVC, flexible PVC, and polyvinyl acetate (PVAc); low-density polyethylene (LDPE); polypropylene (PP); and polystyrene (PS). Moreover, such plastic is found in a wide variety of structures and shapes, being classified principally as fragments, pellets, filaments, films, foam plastic, granules, and styrofoam [16, 29] . The small size of the fragments leads to greater complexity in their recovery and identification, and challenges in the accuracy of the analyses that need to be performed on them [30] . The presence of microplastics in the coastal and marine environment has been widely reported worldwide [18, 29] , see also [20, [31] [32] [33] [34] [35] [36] [37] [38] [39] [40] [41] [42] [43] . In addition to physical damage (e.g., entanglement, suffocation, hypoxia, anoxia [15, 39, [44] [45] [46] [47] [48] [49] [50] [51] [52] ), several studies have reported toxicological damage caused by the presence of contaminants in the environment (e.g., pesticides, phthalates, PCBs and bisphenol A), adsorbed and released by the plastic debris ingested by the biota and their possible movement along the food chain, with consequences that are still not completely understood [24, [53] [54] [55] [56] [57] [58] [59] [60] [61] [62] [63] [64] [65] [66] [67] [68] [69] [70] . In addition, several plastic items are composed of hazardous monomers and additives (e.g., plasticizer, stabilizer, flame retardants, antioxidants, etc. ( [67, 71] ), and/or they adsorb chemical pollutants from aquatic environments [53, [72] [73] [74] [75] [76] [77] . To date, detrimental effects of microplastics have been reported in fishes [78] , mussels [79] , meiofauna [80] , shrimps [81] , crabs [82] , and seabirds [83] . In recent years, experimental studies have also focused on the mechanisms of object (especially plastic) degradation [84] , and on the connections between degradation and pollutant absorption/desorption mechanisms. The topic is extremely important, because, in addition to its scientific interest, a better understanding of these phenomena could contribute to the development of mitigation actions. It has been stressed by several authors that there are several factors in the sea that lead to a reduction in the speed of degradation. These include lower solar radiation exposure, lower temperatures and changes in salinity [7, 22] . Fouling by micro-organisms, limiting the exposure of the surface to UV light, blocks surface photodegradation [85] , and reduces the buoyancy of the objects [84] , causing a further reduction in exposure to direct sunlight. An understanding of the degradation mechanisms of abandoned plastics in the environment, and in particular in the marine environment, is complicated by variability of the plastics in question, the complexity and extent of the environmental matrix and the boundary conditions. Other issues that cannot be neglected are the mobility and determination of the exact residence times of the materials to be studied. For example, polyethylene resin pellets kept for eight weeks in the dark, in saltwater under mechanical stirring, showed more morphological and structural changes than under UV exposure [86] . The properties and characteristics of the various polymeric species are related to the mechanisms of chemical and physical degradation (e.g., thermal degradation, photo degradation, hydrolysis) and biological degradation, and the climatic and environmental factors that can affect them, although there is currently no process capable of degrading waste plastic [19] . Several solutions have been proposed in an effort to curb the problem of the increasing presence of plastics in the sea. These include replacing traditional plastics with so-called "bio-plastics" or "compostable plastics". In part, this has already been implemented in the European Union as a result of EU Directive 2019/904. The goal of the directive was to reduce the consumption of standard single-use plastic items, but, in fact, resulted in the replacement of traditional plastic disposables with biodegradable/compostable plastic disposables. This kind of action does not solve the problem, if it is not accompanied by other equally important actions, such as improving waste management (e.g., sorting, chemical recycling, pyrolysis), preventing waste reaching the sea (e.g., barriers in rivers, improving the transport system and landfills, etc.), and environmental education (e.g., recognizing different types of materials, raising awareness of reuse before recycling). In fact, with implementation of the law, the type of material arriving in the sea changed, with little effect on its quantity. The assumption behind the decision was that biodegradable materials in the sea degrade much faster than traditional materials. However, is this really the case? Some recent studies, focusing on the behaviour of different biodegradable polymers in the environment, cast serious doubt on this. In 2010, O'Brine and Thompspon [87] compared marine degradation (in Devon, UK) of different plastics, including compostable Mater Bi, two oxo-degradable polyethylenes, and traditional PE, partially from recycled plastics, and observed discharge of 100% of the mass of Mater Bi in 24 weeks, with minimal change observed in the other plastics after 40 weeks. They note that fragmentation of Mater-Bi caused its dispersion in free seawater with no debris being recovered for analysis. In 2017, Bagheri et al. [88] carried out a study on biodegradable polyesters, including PLGA, PCL, PLA, PHB, Ecoflex and the non-biodegradable polyester polymer PET, maintaining them in artificial seawater and freshwater under controlled conditions for one year. They observed 100% loss only for PLGA, while the other polymers remained intact over 400 days, and concluded that so-called biodegradable polymers do not degrade in water under natural conditions. In 2020, Kliem et al. [10] analysed the biological degradation of certain polymers under specific conditions of temperature and pH that simulate natural environments, such as soil, fresh water and seawater. They showed that PLA, a biodegradable polymer currently used in industry, does not decompose significantly in seawater or fresh water, but only after industrial composting, with temperature together with battery activity being the most important factors affecting and enabling degradation. Experimental investigations involving biodegradability comparison of chitosan, PBAT (Ecoflex) and HDPE, were carried out in saltwater at the Aquarius underwater laboratory in 2020 [89] , with good biodegradation observed for chitosan, 16% of biodegradation for PBAT, and only 7.8 % for HDPE, with FTIR used to evidence structural changes. Numerous degradation experiments and studies have been performed under controlled conditions and in simulated environments, with only a small number conducted in seawater; however, even in a laboratory environment, it is possible to evaluate photodegradation and thermal-degradation. Among first generation microplastics, in the millimetre range (from 1 to 5 mm) "resin pellets" represent a significant proportion. Pellets are granules of different polymer types, used to produce macroplastic objects, through melting followed by extrusion and moulding. Since there is still no strict regulation for the adoption of measures to prevent the possible loss of these millimetre-sized plastics during their transport, storage and processing, the pellets are easily dispersed in the environment, and are now present in many regions, including the polar regions [90] . Recent studies have shown that their percentage content ranges from 3% [91] to about 30% of all microplastics surveyed on beaches [40, 92] . The occurrence of hydrophobic contaminants in marine plastic pellets has been widely reported, and their measurement has established a global association between pollutants and plastic pellets discarded at sea [72] [73] [74] 77, [93] [94] [95] [96] [97] [98] [99] [100] [101] . Laboratory experiments, theoretical modelling and several field experiments have been performed to investigate how the physical and chemical properties of each type of polymer (e.g., surface area, diffusivity, and crystallinity) influence the sorption of chemicals by resin pellets [53, 72, 95, 98, 102, 103] . The results of these studies confirm that the sorption patterns are dependent on the properties of the particular compound considered (e.g., hydrophobicity, molecular weight (MW)) and on the polymer type, but also on the environmental conditions, such as weathering and water salinity. In many studies, polyethylene (PE) has been shown to present a larger surface area than polypropylene (PP) and to have an affinity for a wide range of organic contaminants varying in hydrophobicity [72, 104, 105] . PE, together with PP, is produced in very large quantities in west European countries and represents a significant proportion of plastic debris in the environment [75] . This evidence led to the decision to use PE pellets as passive samplers of POP pollution in the International Pellet Watch project [94, 97] . Predictive modelling for low-density polyethylene (LDPE) acting as a passive sampling device suggests that the time to reach saturation could vary from days to months, depending on the chemical and environmental conditions considered [97] , but also on the sorption/desorption models used, and on the weathering state of the sample [53, 95, 102] . Most of these studies were carried out in the laboratory, i.e., with the application of precise doses of contaminants in the case of adsorption experiments, or the establishment of controlled conditions of temperature and pressure for degradation experiments. For example, Da Costa et al. [87] studied morphological and thermic variation (using FTIR-ATR analysis, RAMAN spectra, TGA analysis, SEM images) in PE pellets maintained in artificial seawater for eight weeks under controlled temperature, light exposure and movement conditions, and observed quantifiable chemical and physical impacts on the structural and morphological characteristics of granules. They recommended this type of approach to investigate the degradation and behaviour of microplastics. Such controlled experiments, on the other hand, overlook many factors dependent on environmental and unpredictable weather conditions. Moreover, in laboratory experiments the use of organic-free water prevents a proper assessment of the role of dissolved organic material in the marine environment, for example, by favouring the transfer of chemicals into the pellets, extending the equilibrium time scale for pollutants sorption [103] , or influencing weathering mechanisms at the pellet surface. With respect to the few experiments conducted in free seawater, some of them measured sorption of POPs onto previously uncontaminated plastic pre-production pellets ( [73, 104] ), others focused on degradation of the polymeric matrix [106] , while still others focused of the colonization by microorganisms of traditional-plastic and bio-plastic pre-production pellets [107] [108] [109] . The importance of weathering is emphasized in all these studies. Rochmann et al. [103] focused on the importance of weathering influencing the diffusion behaviour of chemical compounds within the pellets in marine environments. Weathering, leading to an increase of the surface area and pore size of the polymer, promotes an even greater diffusivity in PE pellets, allowing them to sorb a higher quantity of substance. In 2016, Brandon et al. [110] focused only on pellet degradation processes, considering pellets weathered in dry or seawater simulated environment, both in darkness and sunlight conditions. Their results showed non-linear changes in chemical bonds with exposure time to selected environmental conditions. The long-term effect of atmospheric agents on the mechanisms of degradation of plastics (and, in particular, bioplastics and compostable plastics) in the marine environment, and the connection between degradation and the uptake of chemicals, appears to be a still evolving field of study. Based on the background described above, our experiment sought to investigate the behaviour of plastic items in the marine environment. These items were both artefacts and pellets of commonly used plastic materials. They were made up of traditional and biodegradable polymers contained in special structures built for the purpose and placed in seawater, or on a simulated beach, and left to age for a minimum of three years. At intervals of a few months, the materials were sampled, and the necessary measurements were taken, to verify any intervening structural and morphological changes. The experiment is still in progress after twenty four months from the positioning of the granules in both environments. In the Materials and Methods section, we describe the setup of the experiment, the preparation of the cages and samples, the sampling of a portion of the granules of each material after six months, and the types of analyses performed on the samples. The remainder of the granules was left for further sampling in the following months. In the Results section, we report the data obtained for all materials introduced into both the cages and the sandbox, as well as the first results obtained after six months from deployment. In the Discussion section, we comment on these results in the light of what is currently available in the literature. In the Conclusion section, we summarize what has been described above, and describe what our future objectives will be with respect to continuation of the analyses of the material obtained to date, and to continuation of the experiment itself. Two types of standard polymer pellets (high density polyethylene-HDPE, Auser Polimeri, Coreglia Antelminelli (LU), Italy, and polypropylene-PP, PoliEko, Celje, Slovenia) were used, together with two types of biodegradable polymer pellets (polylactic acid-PLA, Ingeo 2002D ® , NatureWorks, Plymouth, MN, USA, and polybutylene adipateco-terephthalate-PBAT, Ecoflex ® F Blend C1200, BASF, Ludwigshafen, Germany). They were used as received. The experiment was carried out in the Bay of Santa Teresa, a small bay inside the tourist and commercial Gulf of La Spezia, Italy ( Figure 1 ). The site hosts precious marine and terrestrial ecosystems and lies in very close proximity to the headquarters of the research institutes of the National Research Council (CNR), the National Institute of Geophysics and Volcanology (INGV) and the National Agency for New Technologies, Energy and Sustainable Economic Development (ENEA), which has made the bay a natural laboratory in which to undertake research and evaluate technology. Within this framework, the "Smart Bay Santa Teresa" (https://smartbaysteresa.com/, accessed on 7 February 2022) initiative was inaugurated, a collaboration platform that hosts different scientific projects and an underwater observatory called LabMARE. The site hosts precious marine and terrestrial ecosystems and lies in very close proximity to the headquarters of the research institutes of the National Research Council (CNR), the National Institute of Geophysics and Volcanology (INGV) and the National Agency for New Technologies, Energy and Sustainable Economic Development (ENEA), which has made the bay a natural laboratory in which to undertake research and evaluate technology. Within this framework, the "Smart Bay Santa Teresa" (https://smartbaysteresa.com/, accessed on 7 February 2022) initiative was inaugurated, a collaboration platform that hosts different scientific projects and an underwater observatory called LabMARE. This underwater multi-parametric platform was developed by the Ligurian Cluster of the Marine Technologies (DLTM), in collaboration with the INGV, CNR, ENEA, the Hydrographic Institute of the Navy with the support of the Municipality of Lerici and the Cooperative Mitilicoltori Associati, as part of the LabMARE project funded by the Liguria Region. The main aim of the underwater observatory is experimentation with new technologies and environmental status monitoring. LabMARE is equipped with sensors for monitoring environmental parameters (temperature and salinity) and special cages for studying the degradation of plastics in the marine environment ( Figure 2 ). The main aim of the underwater observatory is experimentation with new technologies and environmental status monitoring. LabMARE is equipped with sensors for monitoring environmental parameters (temperature and salinity) and special cages for studying the degradation of plastics in the marine environment ( Figure 2 ). The underwater observatory was deployed on 3 March 2020 at 44 • 4 55.08 N -9 • 52 50.46 E at 10 m depth, about 60 m from the coast ( Figure 1 ) and provides real time temperature data through the underwater cable connected to the land station and via transmission of data by internet connection. The two special cylindric cages (about 40 cm × 30 cm, Figure 2 ) installed on the structure of the underwater observatory were self-produced by the researchers in stainless steel 318, each one containing three "baskets" (about 15 cm × 10 cm, Figure 2 in stainless steel wire mesh (AISI 316, mesh 0.24 mm)), electropolished and with anodic passivation. The cages were closed with plastic ties and anchored to the underwater observatory with large plastic ties. Different types of plastic objects, both macro and micro, made of both standard polymers and biopolymers, were placed inside the cages ( Table 1 ). The choice to use metal, avoiding any plastic material to build the cage and baskets was made to prevent any possible contamination, such as possible release of additives from the plastic material (Plastic Additive Standards Guide. AccuStandard, 2018 [106] ) or interference with the pellets in the process of absorbing chemicals from the seawater. Despite the presence of sacrificial anodes placed at one end of each of the two cages, as well as at the end of each of the inner baskets, during August and September 2020, the metal of the cages was affected by corrosion due to a galvanic currents effect. This rapid corrosion was probably due to the large presence of cation metals in the port area. On November 2020, the cages and baskets were changed with new ones constructed by the researchers in collaboration with an enterprise expert in the industrial and naval field (Vamp s.nc., La Spezia): two large cages in stainless steel 316 (size: 70 × 30 cm), 6 small cages in stainless steel 316 (size: 20 × 15 cm) and 8 baskets in stainless steel 316 with meshed net of 1 mm of two different sizes (size: 19 × 14 cm and 14 × 14 cm). Each was equipped with sacrificial anodes to avoid galvanic corrosion. Cages were closed with plastic ties and anchored to the underwater observatory with large plastic ties. The underwater observatory was deployed on 3 March 2020 at 44° 4′55.08"N − 9°52′50.46"E at 10 m depth, about 60 m from the coast ( Figure 1 ) and provides real time temperature data through the underwater cable connected to the land station and via transmission of data by internet connection. A sandbox containing sand taken from the Gulf of La Spezia (Le Grazie Bay) was set up near the dock where the cages were located, and the same materials introduced into the cages were placed in it, in order to carry out a comparative study of the degradation and absorption of chemicals at sea and on a "simulated beach". Due to the COVID-19 health emergency, and the consequent total lockdown that prevented free circulation in Italy from February to June 2020, the sandbox was promptly transported to an area near the home (44 • 7 51.04 N; 9 • 57 28.88 E, in Sarzana) of one of the authors, where it was possible to check that it was not tampered with or damaged. The sampling campaign started on 3 March 2020, corresponding to point zero contextually of the first deployment of the LabMARE station and the cages, for all inserted objects, both in the sea cages and in the simulated beach. The experiment was designed to last three years in total. The objects placed in the cages were of different type, size and material: polymer pellets (see Section 2.1), coffee capsules, single use tableware, personal protective equipment and cigarettes. In order to study the evolution of ageing of the objects in the different environments, samples were taken on the same day from the cages in the sea and from the sandbox every few months. The sampling dates for the first two years of the experiment were as follows: September 2020, November 2020, March 2021, June 2021, October 2021 and the next sampling is scheduled for the first week of March 2022. All the samples taken in the sea and in the sandbox were washed with ultra-pure water and dried in air before being analysed. In this investigation, comparison between the characteristics and properties of the raw materials (four types of pellets) and those placed in the two different environments for six months (sampled on September 2020) is discussed. This is the period during which a biodegradable material should be able to biodegrade, according to the UNI EN ISO 14855-2:2018, although the legislation considers composting conditions. The sampling of material contained in the cages was performed with the support of scubadivers of Dipartimento Polizia di Stat-Centro Nautico Sommozzatori of La Spezia (Italy). The marine station LabMARE was equipped with the sensor SBE37SM (supplied by Sea-Bird Scientific) just before the lockdown due to SARS-CoV-2 to record data every 10 min from March 2020. All the data collected were evaluated by calculation of monthly averaged values from the average daily temperatures with relative standard deviations and the maximum and minimum temperatures for each month. A hygrometer thermometer wireless Bluetooth sensor supplied by ORIA was put in a sandbox located at the CNR research area of Pisa to record the temperature data every 10 min from March 2021. All the data collected were evaluated by calculation of monthly averaged values from the average daily temperatures with relative standard deviations and the maximum and minimum temperatures for each month. Attenuated total reflectance (ATR) spectra were registered using a Fourier Transform -InfraRed Jasco 6200 (Jasco, Tokyo, Japan) equipped with a PIKE MIRacle (Madison, WT, USA) accessory. Each sample underwent 64 scans from 4000 to 650 cm −1 , after the collection of background data. Thermogravimetric analysis (TGA) was performed with an SII TG/DTA 7200 EXSTAR Seiko analyser (Seiko, Chiba, Japa), under heating from 30 to 700 • C, at 10 • C /min rate. Air was fluxed at 200 mL/min during all measurements. The sample amount used for TGA was 5-10 mg. The first derivative (DTG) for each curve was recorded for the different samples and analysed. T onset (temperature corresponding to starting degradation) and residue amount at 700 • C were determined from each TGA profile. T max (temperature at which the maximum rate of mass loss occurs) was calculated from each DTG curve. Differential scanning calorimetry (DSC) analysis was carried out in order to assess any effects induced by the degradation processes triggered during the months of immersion and in the sandbox relating to plasticisation phenomena or changes in crystallinity. DSC analysis was performed using a Seiko SII ExtarDSC7020 calorimeter (Seiko, Chiba, Japan) with a different thermal programme for each type of polymer (Table 1) . Each measurement was carried out on approximately 5-10 mg of materials. The software associated with the instrument was used to determine the values of glass transition temperature (T g ), thermal capacity variation associated with the glass transition (∆C p ), melting temperature (T m ) with relative enthalpy of fusion (∆H m ), and cold crystallization temperature (T cc ), with relative enthalpy (∆H cc ) estimated from the second heating scan. The degree of crystallinity (χ%) was determined using the following Equations (1) and (2) [107]: with ∆H m = mean enthalpy of fusion of the sample, ∆H 0m = enthalpy of fusion of material 100% crystalline and ∆H cc enthalpy of cold crystallization. GPC measurements were carried out on PLA and PBAT polymers using an HPLC Agilent 1260 Infinity (Agilent, Santa Clara, CA, United States) equipped with a three-way valve as the injection system and a styrene-divinylbenzene resin as the stationary phase, at an operating pressure of 80 bar, with CHCl 3 as eluent at 0.3 mL/min and a refractometer as a detector. Solutions were prepared by dissolving the materials in CHCl 3 (HPLC grade) with a concentration of 3 mg/mL and filtered two times with an Agilent filter with a porosity of 2 µm. SEM images were recorded with an FEI Quanta 450 ESEM FEG scanning electron microscope (Thermo Fisher, Waltham, MA, USA) at CISUP Laboratories (Centro per la Integrazione della Strumentazione) at University of Pisa. The specimens were analysed on the external surface without any specific manipulations. As stated in Section 2, the results obtained from the above-mentioned analyses on standard (HDPE and PP) and biodegradable (PLA and PBAT) polymeric granules during the first six months of the study were reported. The choice of six months was not accidental. The idea was to follow modification due to aging and eventual degradation occurring to the granules in a marine environment (direct immersion in sea or deposition on the surface of the sand in the sandbox) in the first six months after positioning, the period during which a biodegradable material should be able to biodegrade. The results obtained on each kind of "bio" material were compared with the corresponding results for standard polymer granules. Analysis of the temperatures reached in the sea and in the sandbox in the period under review (March 2020-August 2020) was considered important in order to provide data on whether this variable could affect the characteristics of the aged samples. Table 2 shows the result of the analysis of the data collected at the LabMARE station. Unfortunately, it was not possible to place a similar sensor in the sandbox near Sarzana (La Spezia). The following were considered in this case. The temperature data were collected in the period from March 2021 to August 2021 using the sensor in the sandbox at CNR and are reported here in Table 3 according to the same analysis carried out for the data in Table 2 . In a similar way, the temperatures of the air recorded in Pisa in the period from March 2021 to August 2021 by the San Giusto Weather Station were compared with the data recorded in Sarzana in the period from March 2020 to August 2020 as measured by the Sarzana Luni Weather Station and reported on the website https://www.ilmeteo.it/portale/archivio-meteo, accessed on 7 February 2022 and in Table 4 . No significant differences were observed from one year to the other in the air temperatures; the data recorded in the sandbox in Pisa in 2021 were considered consistent with those of the Sarzana sandbox in 2020 in the same months. Given this premise, the analysis of the results indicated that in both the sandbox and the sea similar average temperatures were reached. The substantial difference was the thermal excursion during the day with a maximum of 51 • C in the sandbox and 25 • C in the sea and the corresponding standard deviations. As a consequence, the materials in the sandbox were more thermally stressed than the same materials in the sea. HDPE pellets left in the two different environments (sand and seawater) were analysed using the different techniques described above. The photos collected of the starting granules and of the sampled granules of HDPE after six months in both environments (HDPE_6SW for seawater and HDPE_6S for sand) are compared in Figure 3a . A colour deviation towards yellow/amber was apparent. For all kinds of gran considered in this experiment, this was much more pronounced in the sea sample detail, the effect of an aggressive attack from the environment was evident from comparison of SEM images (Figure 4a) . Modification of the surface morphology ta place correlated with the different action of the sea compared to sand, with formatio an evident porous surface in samples kept in the sea. A colour deviation towards yellow/amber was apparent. For all kinds of granules considered in this experiment, this was much more pronounced in the sea samples. In detail, the effect of an aggressive attack from the environment was evident from the comparison of SEM images (Figure 4a) . Modification of the surface morphology taking place correlated with the different action of the sea compared to sand, with formation of an evident porous surface in samples kept in the sea. These effects were correlated with chemical modification of the polymer chain the surface of the granules and/or eventual chemical absorption by ATR analyses. absorption peaks appeared in the region of OH stretching (at about 3400 cm −1 ), betw 1740-1550 cm −1 due to the stretching mode of carboxyl groups and double bonds in HDPE_6SW and HDPE_6S (Figure 5a) . A large and intense peak between 900-1200 (centred at about 1010 cm −1 ) was also observed after six months in both environmen the stretching Si-O region. These effects were correlated with chemical modification of the polymer chains on the surface of the granules and/or eventual chemical absorption by ATR analyses. New absorption peaks appeared in the region of OH stretching (at about 3400 cm −1 ), between 1740-1550 cm −1 due to the stretching mode of carboxyl groups and double bonds in both HDPE_6SW and HDPE_6S (Figure 5a) . A large and intense peak between 900-1200 cm −1 (centred at about 1010 cm −1 ) was also observed after six months in both environments in the stretching Si-O region. As far as thermal properties are concerned, TGA and DSC analyses were carried out on the HDPE series. The thermal profiles TGA and DTG are compared in Figure 6a ,b and the characteristic temperatures calculated from the thermal curves are summarized in Table 5 . A decrease in the thermal stability of the polymer, associated with a decrease in the degradation starting temperature (T onset ) was observed for both the sea and sand samples after six months. T max decreased only for seawater samples. A slight decrease in the melting temperature for both the seawater and sand samples was observed, as well as in the crystallinity percentage results from the analysis of the second heating scan in the DSC thermogram (Figure 7a and Table 5 ). The effect was more apparent for HDPE_6SW, as in the TGA results. As far as thermal properties are concerned, TGA and DSC analyses were carried out on the HDPE series. The thermal profiles TGA and DTG are compared in Figure 6a ,b and the characteristic temperatures calculated from the thermal curves are summarized in Table 5 . A decrease in the thermal stability of the polymer, associated with a decrease in the degradation starting temperature (Tonset) was observed for both the sea and sand samples after six months. Tmax decreased only for seawater samples. A slight decrease in the melting temperature for both the seawater and sand samples was observed, as well as in the crystallinity percentage results from the analysis of the second heating scan in the DSC thermogram (Figure 7a and Table 5 ). The effect was more apparent for HDPE_6SW, as in the TGA results. * ∆H 0 m = 293 J/g [108] ; χ% = ∆Hm ∆H 0m × 100. The PP granules (Figure 3b ) showed a light colour deviation towards yellow which was more pronounced in the seawater sample (PP_6SW) than in the sand sample (PP_6S), as for HDPE. The appearance of some cracks on the surface of the granules was evident in the SEM images of PP_6S (Figure 4b) . Formation of absorption bands in the carbonyl and double bond region was observed in the ATR spectra (Figure 5b ) and the disappearance of the peak at 1744 cm −1 was noticeable. Absorption peaks appeared in the region of OH stretching (centred at about 3420 cm −1 ), both for the sample PP-6SW and PP-6S. As for the HDPE samples, a large and intense peak appearing between 900-1200 cm −1 (centred at about 1005 cm −1 ) also formed after six months in both the materials in the stretching Si-O region. A decrease in T onset and T max with time in both seawater and in sand was observed by comparison of the TGA thermal analyses. An increase in the TGA residue was measured for the PP_6S sample with respect to the other samples (Figure 6c ,d and Table 6 ). A splitting of the T m peak of PP_6S with respect to PP with the presence of a shoulder and a decrease in the crystallinity was measured in the DSC profiles (Figure 7b and Table 6 ). The PP granules (Figure 3b ) showed a light colour deviation towards yellow which was more pronounced in the seawater sample (PP_6SW) than in the sand sample (PP_6S), as for HDPE. The appearance of some cracks on the surface of the granules was evident in the SEM images of PP_6S (Figure 4b) . Formation of absorption bands in the carbonyl and double bond region was observed in the ATR spectra ( Figure 5b ) and the disappearance of the peak at 1744 cm −1 was noticeable. Absorption peaks appeared in the region of OH stretching (centred at about 3420 cm −1 ), both for the sample PP-6SW and PP-6S. As for the HDPE samples, a large and intense peak appearing between 900-1200 cm −1 (centred at about 1005 cm −1 ) also formed after six months in both the materials in the stretching Si-O region. A decrease in Tonset and Tmax with time in both seawater and in sand was observed by comparison of the TGA thermal analyses. An increase in the TGA residue was measured for the PP_6S sample with respect to the other samples (Figure 6c ,d and Table 6 ). A splitting of the Tm peak of PP_6S with respect to PP with the presence of a shoulder and a decrease in the crystallinity was measured in the DSC profiles (Figure 7b and Table 6 ). * ΔH 0 m=293 J/g [108] ; χ% 100. * ∆H 0 m = 207 J/g [108] ; χ% = ∆Hm ∆H 0m × 100. PLA granules showed a colour deviation towards yellow especially for the sea samples (PLA_6SW) compared to the sand samples (PLA_6S), as previously described for standard polymers (Figure 3c ). Noticeable changes in morphology after six months were not observed in both degradative environments (SEM images in Figure 4c ). These results were confirmed by ATR analysis. Only a small difference in the spectrum of seawater samples was observed due to the presence of a large peak centred at about 3400 cm −1 in the region of -OH stretching (Figure 5c) . A broad band between 1700 and 1550 cm −1 was detectable in this spectrum with an absorption band also at 1039 cm −1 . The results from the ATR and SEM images were confirmed by TGA and DSC analyses (Figures 6e,f and 7c , and Table 7 ). In the DSC profiles, similarly, the samples showed only minimal variations in the characteristic T g , T m and crystallinity degree, statistically not different from those of the PLA. The molecular weight of the samples and the polydispersity index are given in Table 6 . In all cases there was an invariance in polydispersity, even though an improvement in Mn and Mw values was measured for PLA_6S. In the case of the PBAT polymer, the effect of the environment on the colour of the pellets was more marked. The pellets developed an amber colour both in the sea (PBAT_6SW) and sand (PBAT_6S) (Figure 3d ). The surface of the PBAT granules showed grooves that ran through the granule (Figure 4d) . The appearance of a large band in the -OH stretching region (3380 cm −1 ) was evident from ATR analyses (Figure 5d ). The presence of additional peaks in the region 1640-1550 cm −1 of the double C=C bond was observed in both aged materials, but was more pronounced in the PBAT_6S samples. An intensive peak was also present at 1011 cm −1 in the seawater sample. Regarding the TGA results, the DTG curves in all cases showed two main peaks: the first can be considered the principal degradative step and was used to calculate T max , while the second, at higher temperatures, represents a subsequent degradation step which occurred with definitely lower speed. The degradation (Figure 6g ,h and Table 8 ) of the polymer started at a lower temperature for the materials aged in both seawater and in sand. A higher percentage of residue was measured of PBAT_6S. Some effects were also evident in the GPC results, especially for PBAT_6S, where the polydispersity increased from 2.2 of starting material to 2.8 with a decrease in Mn and Mw (Table 9 ). The DSC results (Figure 7d and Table 8 ), however, did not undergo significant change [89] . The polymers chosen for this investigation can be classified, in relation to their chemical structure, into two large families: the C-C backbone and C-O backbone polymers, as reported in Figure 8 . HDPE and PP belong to the C-C backbone polymers while PLA and PBAT belong to the C-O backbone polymers. The polymers chosen for this investigation can be classified, in relation to their chemical structure, into two large families: the C-C backbone and C-O backbone polymers, as reported in Figure 8 . HDPE and PP belong to the C-C backbone polymers while PLA and PBAT belong to the C-O backbone polymers. Overall, this classification translates into a differentiation of properties and chemical behaviour from the point of view of the possibility of being prone to hydrolysis for C-O backbone polymers (PLA and PBAT) or being non-hydrolysable for C-C backbone polymers (HDPE or PP). HPDE and PP are traditional non-biodegradable plastics and are mainly fossil-fuel based and partly bio-based, as in bio-PE, bio-PP, and bio-PET. However, PLA and PBAT are biodegradable bioplastics, bio-based in the case of PLA (such as PHA or PBS), and fossil-fuel based in the case of PBAT [111] . The effects of the two environments investigated (seawater and sandbox) on the selected materials in the form of granules during the six months are illustrated well by the photos reported in Figure 3 . The change in colour can be attributed to several factors, as reported by Andrady et al. [22] and Ali et al. [19] , and increased with time of exposure, as observed by Brandon [110] . The colouring (yellowing) of the granules can be mainly related to the start of the degradation process (i.e., photo-oxidation, hydrolysis) or the absorption of pollutants by the surrounding environment [73] . Overall, photo-oxidation and hydrolysis mechanisms lead to the scission of chains with decrease in molecular weight and formation of double bonds C=C and C=O, or the formation of OH groups. Endo et al. [73] hypothesized that the colour change of the granule surface may be due to the facilitated absorption of additives due to the formation of a porous surface with aging. The more pronounced colour deviation towards yellow/amber, found in our study for all sea samples compared to sand samples, seems to indicate that in the first environment the processes causing yellowing are enhanced (whatever they are). Anyway, noticeable changes in morphology were already evident after six months from the comparison of SEM images (Figure 4 ) for all the polymers tested in both sea and in sand, with the exception of PLA. The different effects induced by sea or sand conditions on the change in the surface morphology was evident. The formation of a porous surface, or, at least, areas with cavities due to the effect of abrasive phenomena [112] , was confirmed in HDPE_6SW and PP_6SW, but particularly in PBAT_6SW. The formation of grooves that ran through the granule observed on the surface of PP_6S granules and PBAT_6S granules can be correlated with the greater exposure of the granule to solar radiation and to the higher temperature reached in the sand environment, which increases with seasonality very differently from sea-water. The ATR analyses helped to better understand which processes occurred in both granule environments. The absorption at about 3400 cm −1 highlighted in many spectra could be attributed to OH-stretching and was assumed to be the result of a hydrolysis reaction in the polymer chains with an increase in hydroxyl groups. The peak at about 1010-1030 cm −1 , shown in the spectra can, alternatively, can be attributed to contamination by sand absorbed on the granule surface (stretching Si-0). With respect to the standard polymers, the HDPE and PP samples, the appearance of the bands due to the stretching mode of double C=C bond or C=O, that occurred more intensely in PP_6S than HDPE_6S, can be attributed to a more extensive photodegradation process, occurring preferentially in sand compared to seawater. The presence of the methyl sidechain of PP allows β-scission reactions to occur more easily with formation of unsaturated bonds and decrease in molecular weight [113] . The disappearance of the peak at 1744 cm-1 from raw PP can be attributed to additives present in the pristine polymer. The results appeared to be different for both biodegradable polymers PLA and PBAT. Both PLA_6SW and PLA_6S did not show new peaks, with the exception of that around 3500 cm −1 . The invariance of the ATR spectra was confirmed by GPC results. The value of molecular weight remained quite similar, even when the measurements were carried out not by sampling of the surface but on the entire solubilised granule. The percentage of degraded material was low compared to the bulk and did not affect the average molecular weight value [10, 88] . Weak peaks appeared in the ATR spectra of the PBAT samples between 1550 and 1640 cm −1 which could be associated with C=C stretching, attributable to Norrish II mechanisms [19] , and were more intense in the sand environment than in the sea environment. Materials is not transferred from the surface of the granules to the surface of the crystals after the recording of the ATR spectra and this result indicates the low extent of contamination of the surface of the granules after six months GPC analysis confirmed these results. An evident decrease was observed in both samples after six months with an increase in polydispersity, especially for the sample in the sandbox. From the results of the TGA thermal analyses, a decrease in thermal stability was observed for all samples in the sea and in the sandbox, with the greatest degradation occurring for the sandbox samples. These results confirm the higher photodegradation extent occurring for the samples in the sandbox than for those in the sea. The increase in residue percentage for PP_6S (as for PBAT_6S) can be attributed to photo-oxidised samples as reported by Contact-Rodrigo [114] . The DSC results confirmed the findings from the TGA analyses. The splitting of the melting peak in the PP_6S sample and the decrease in the crystallinity can be hypothesized to reflect a possible decrease in the length of the macromolecular chains which could affect the crystallization capacity of the system and therefore give rise to less ordered crystalline forms [114] . On the other hand, Brandon associated increase in brittleness of the material with progression in the environmental exposure time and observed greater action precisely on the PP [110] . The average temperature evolution and temperature values reached during the entire experimental period could explain the limited molecular weight variation for PLA compared to that of PBAT. In the six months of the experiment, the maximum recorded temperature did not exceed 25.24 • C for the sea and 51.63 • C for the sandbox, with a maximum monthly average that reached a maximum only in August 2020 with a value of 23.68 • C (seawater) and 29 .06 • C (sandbox). The temperatures recorded remained very far from both the Tg of PLA and Tm temperatures of both polymers. Unfortunately, while several experiments have been carried out on the biodegradation of PLA (almost always in film form) following the standardized procedures required by international standards (ASTM, UNI EN, ISO) [115] [116] [117] [118] , there are few studies regarding the biodegradation of PLA in the marine environment that show little evidence of microbial degradation observed in such environments, temperature conditions and type of microbial species present [119, 120] . Although PBAT showed good biodegradation in soil, even at low temperatures [121] , PLA showed good biodegradation in compost at 58 • C, at 60% relative humidity and with maintenance of aerobic conditions through oxygen insufflations, while, in contrast, in free soil, its degradation was not significant [118] . Furthermore, in a 100-day experiment to investigate the influence of temperature and type of soil substrates variation on the biodegradation of pure PLA, Gil Castel et al. [116] concluded that chain scission occurring as a function of time and temperature was the main effect influencing the degradation processes of PLA. The results of the present study were obtained from the exposure of different types of pre-production pellets to natural sunlight and seawater/beach conditions for six months. At the end of this experiment, we will be able to collect data from a three-year in situ weathering study of standard and bioplastic pellets in the marine environment. Compared to previous studies, based on experiments that accelerated pellet weathering in laboratory or simulated environmental condition, this long-term field experiment represents a more realistic assessment of the aging processes that these particular widespread microplastics experience in the marine environment. As far as we know, this is the first such kind of experiment conducted in the Mediterranean Sea. In this study, two metal cages containing commercial and commonly used industrial filament plastic granules were placed on a multi-parameter platform at a depth of 10 m in seawater; this was flanked by a sandbox with the same granules placed on the sand surface (simulated beach). The behaviour during aging in the marine environment of both traditional plastics, such as HDPE and PP, and bioplastics, such as PLA and PBAT, was compared. After six months of experiment (from March to September 2020) the materials immersed in the sea result had been subjected to less thermal stress than the corresponding materials in the sandbox, because of the lower solar radiation and reduced thermal excursion. Prolonged exposure to intense solar radiation and the temperature reached in the sand produced much more visible effects than those produced on samples placed in the depths of the sea in terms of photooxidation by Norrish I and II degradation reactions. On the other hand, the formation of a porous surface and cavities on all six-months-aged seawater samples (except for PLA) was indicative of abrasive phenomena that could induce a greater increase in the absorption of chemicals dissolved in seawater that could, in turn, affect the observed change in colour. Concerning the biopolymer pellets, the percentage by weight of lost material was low compared to the raw material and did not affect the gravimetric weight value. The molecular weight of PLA remained practically unchanged both in sea and in sand; PBAT, in contrast, showed a decrease of about 40% of the initial molecular weight and less than 10% for the sample in sea. The environmental conditions of the sandbox significantly modified the thermal properties of the materials. A decrease in thermal stability was observed, with the greatest degradation for sandbox samples in all cases and in both environments. In the two substrates of the experiment (sandbox and sea), the degree of degradation of PLA and PBAT remained low when compared to what was detected for the biodegradation process under composting conditions. Anthropocene" Our plastic age Anthropocene, the plastic age and future perspectives The pollution of the marine environment by plastic debris: A review Plastic Debris in the Marine Environment: History and Future Challenges Persistence of Plastic Litter in the Oceans Plastics in marine ecosystem: A review of their sources and pollution conduits Accumulation and fragmentation of plastic debris in global environments Review on the Biological Degradation of Polymers in Various Environments Plastics on the Sargasso sea surface Below the surface: Twenty-five years of seafloor litter monitoring in coastal seas of North West Europe Concentrations of floating plastic debris in the Mediterranean Sea measured during MedSeA-2013 cruise Plastic debris in the open ocean Impacts of Discarded Plastic Bags on Marine Assemblages and Ecosystem Functioning Spatio-temporal variation of anthropogenic marine debris on Chilean beaches Synthetic polymers in the marine environment: A rapidly increasing, long-term threat Distribution and abundance of small plastic debris on beaches in the SE Pacific (Chile): A study supported by a citizen science project Degradation of conventional plastic wastes in the environment: A review on current status of knowledge and future perspectives of disposal The Mediterranean Plastic Soup: Synthetic polymers in Mediterranean surface waters Microplastics in the marine environment The plastic in microplastics: A review Monitoring the impact of litter in large vertebrates in the Mediterranean Sea within the European Marine Strategy Framework Directive (MSFD): Constraints, specificities and recommendations Microplastic as a Vector for Chemicals in the Aquatic Environment: Critical Review and Model-Supported Reinterpretation of Empirical Studies Nanoplastics in the Aquatic Environment. Critical Review. In Marine Anthropogenic Litter Microplastics: Finding a consensus on the definition Are We Speaking the Same Language? Recommendations for a Definition and Categorization Framework for Plastic Debris Microplastics as contaminants in the marine environment: A review Microplastics pollution on Colombian Central Caribbean beaches Progress in quantitative analysis of microplastics in the environment: A review Microplastics in Beaches of the East Frisian Islands Spiekeroog and Kachelotplate Microplastics in sediments: A review of techniques, occurrence and effects Micro-and nano-plastics in marine environment: Source, distribution and threats-A review Preferential accumulation of small (<300 mm) microplastics in the sediments of a coastal plain river network in eastern China Influence of environmental and anthropogenic factors on the composition, concentration and spatial distribution of microplastics: A case study of the Bay of Brest Multi-temporal surveys for microplastic particles enabled by a novel and fast application of SWIR imaging spectroscopy-Study of an urban watercourse traversing the city of Microplastic content variation in water column: The observations employing a novel sampling tool in stratified Baltic Sea Abundance and distribution of microplastics on sandy beaches of Lima Spatial distribution of marine litter along italian coastal areas in the Pelagos sanctuary Spatial and Temporal Distribution of Chemically Characterized Microplastics within the Protected Area of Pelagos Sanctuary Microplastic pollution in the surface waters of the Bohai Sea Anticyclonic eddies increase accumulation of microplastic in the North Atlantic subtropical gyre Litter impacts on marine birds: The Mediterranean Northern gannet as case study Monitoring plastic ingestion by the northern fulmar Fulmarus glacialis in the North Sea Litter in submarine canyons off the west coast of Portugal Effects of fishing rope strength on the severity of large whale entanglements Presence of plastic debris in loggerhead turtle stranded along the Tuscany coasts of the Pelagos Sanctuary for Mediterranean Marine Mammals (Italy) As main meal for sperm whales: Plastics debris Entanglement of Antarctic fur seals at Bird Island, South Georgia Deleterious Effects of Litter on Marine Life Incidence of entanglements with marine debris by northern gannets (Morus bassanus) in the non-breeding grounds Plastic leachates impair growth and oxygen production in Prochlorococcus, the ocean's most abundant photosynthetic bacteria Transport and release of chemicals from plastics to the environment and to wildlife Ingested Microscopic Plastic Translocates to the Circulatory System of the Mussel, Mytilus edulis (L.) A critical analysis of the biological impacts of plasticizers on wildlife Human body burdens of chemicals used in plastic manufacture Phthalates and other additives in plastics: Human exposure and associated health outcomes Large filter feeding marine organisms as indicators of microplastic in the pelagic environment: The case studies of the Mediterranean basking shark (Cetorhinus maximus) and fin whale (Balaenoptera physalus) Are baleen whales exposed to the threat of microplastics? A case study of the Mediterranean fin whale (Balaenoptera physalus) A Review of Plastic-Associated Pressures: Cetaceans of the Mediterranean Sea and Eastern Australian Shearwaters as Case Studies. Front Ingested plastic transfers hazardous chemicals to fish and induces hepatic stress Accumulation of plastic-derived chemicals in tissues of seabirds ingesting marine plastics The impact of polystyrene microplastics on feeding, function and fecundity in the marine copepod Calanus helgolandicus Pollutants bioavailability and toxicological risk from microplastics to marine mussels Virgin microplastics cause toxicity and modulate the impacts of phenanthrene on biomarker responses in African catfish (Clarias gariepinus) The physical impacts of microplastics on marine organisms: A review A Horizon Scan of research priorities to inform policies aimed at reducing the harm of plastic pollution to biota Detailed Review Study on Potential Effects of Microplastics and Additives of Concern on Human Health Deposit-and suspension-feeding sea cucumbers (Echinodermata) ingest plastic fragments Components of plastic: Experimental studies in animals and relevance for human health Hazardous Substances in Plastic Materials Plastic Resin Pellets as a Transport Medium for Toxic Chemicals in the Marine Environment Concentration of polychlorinated biphenyls (PCBs) in beached resin pellets: Variability among individual particles and regional differences Persistent organic pollutants carried by synthetic polymers in the ocean environment Potential for Plastics to Transport Hydrophobic Contaminants Environmental and health hazard ranking and assessment of plastic polymers based on chemical composition Organic micropollutants in marine plastics debris from the open ocean and remote and urban beaches Ingestion of microplastics by demersal fish from the Spanish Atlantic and Mediterranean coasts Microplastics in mussels along the coastal waters of China In situ ingestion of microfibres by meiofauna from sandy beaches Can the Atlantic ghost crab be a potential biomonitor of microplastic pollution of sandy beaches sediment? Occurrence of plastic debris in the stomach of the invasive crab Eriocheir sinensis Microplastic accumulation in the gastrointestinal tracts in birds of prey in central Florida Biofouling on buoyant marine plastics: An experimental study into the effect of size on surface longevity Early microbial biofilm formation on marine plastic debris Degradation of polyethylene microplastics in seawater: Insights into the environmental degradation of polymers Degradation of plastic carrier bags in the marine environment Fate of So-Called Biodegradable Polymers in Seawater and Freshwater Biodegradability in aquatic system of thin materials based on chitosan, PBAT and HDPE polymers: Respirometric and physical-chemical analysis Polystyrene spherules in coastal waters Marine litter in the central Atlantic coast of Morocco Mediterranean dirty edge: High level of meso and macroplastics pollution on the Turkish coast Organic pollutants in marine plastic debris from Canary Islands beaches International Pellet Watch: Global monitoring of persistent organic pollutants (POPs) in coastal waters. 1. Initial phase data on PCBs, DDTs, and HCHs Testing phenanthrene distribution properties of virgin plastic pellets and plastic eroded pellets found on Lesvos island beaches (Greece) Measurement of persistent organic pollutants (POPs) in plastic resin pellets from remote islands: Toward establishment of background concentrations for International Pellet Watch Critical Review of Low-Density Polyethylene Partitioning and Diffusion Coefficients for Trace Organic Contaminants and Implications for Its Use As a Passive Sampler Diffuse pollution by persistent organic pollutants as measured in plastic pellets sampled from various beaches in Greece Eroded plastic pellets as monitoring tools for polycyclic aromatic hydrocarbons (PAH):Laboratory and field studies Plastic pellets, meso-and microplastics on the coastline of Northern Crete: Distribution and organic pollution Spatial variability in persistent organic pollutants and polycyclic aromatic hydrocarbons found in beach-stranded pellets along the coast of the state of São Paulo, southeastern Brazil Desorption kinetics of hydrophobic organic contaminants from marine plastic pellets Long-Term Field Measurement of Sorption of Organic Contaminants to Five Types of Plastic Pellets: Implications for Plastic Marine Debris Partitioning of polycyclic aromatic hydrocarbons in the polyethylene/water system Polymer-water partition coefficients of hydrophobic compounds for passive sampling: Application of cosolvent models for validation Isothermal Cold-Crystallization of PLA/PBAT Blends With and Without the Addition of Acetyl Tributyl Citrate Effect of the high-density polyethylene melt index on the microcellular foaming of high-density polyethylene/polypropylene blends Crystallization behavior of fully biodegradable poly(lactic acid)/poly(butylene adipate-co-terephthalate) blends Long-term aging and degradation of microplastic particles: Comparing in situ oceanic and experimental weathering patterns Plastics and beaches: A degrading relationship Study of crystallization behaviour of electron beam irradiated polypropylene and high-density polyethylene Thermal characterization of the oxo-degradation of polypropylene containing a pro-oxidant/pro-degradant additive Biodegradation of polylactide in aerobic and anaerobic thermophilic conditions Ribes-Greus, A. Influence of substrate and temperature on the biodegradation of polyester-based materials: Polylactide and poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) as model cases End-of-life evaluation and biodegradation of Poly(lactic acid) (PLA)/Polycaprolactone (PCL)/Microcrystalline cellulose (MCC) polyblends under composting conditions Biodegradation of biopolymeric composites and blends under different environmental conditions: Approach towards end-of-life panacea for crop sustainability Abiotic and biotic environmental degradation of the bioplastic polymer poly(lactic acid): A review Environmental degradation of biodegradable polyesters 1. Poly(ε-caprolactone), poly[(R)-3-hydroxybutyrate], and poly(L-lactide) films in controlled static seawater Biodegradation in Soil of PLA/PBAT Blends Compatibilized with Chain Extender The authors thank the Italian Istituto Zooprofilattico Sperimentale del Piemonte, Liguria e Valle d'Aosta that, through the project "Chemistry and genomics: a synergistic strategy for the detection of contaminants associated with microplastics in food", enabled some of the materials useful for the setup of the experiment to be obtained. Other thanks are to DLTM, that made available the LabMARE coastal underwater platform to host the cages, to Andrea Bordone and Giancarlo Raiteri (ENEA) for the calibration of the CTD probe and the correction of temperature data of the seawater, and to Dipartimento Polizia di Stato-Centro Nautico Sommozzatori of La Spezia (Italy) that give their precious support to sampling of the plastic material contained in the cages. The authors also thank the Win on Waste group, at Area della Ricerca CNR of Pisa (WoW, https://wow.area.pi.cnr.it/, accessed on 7 February 2022) for their helpful discussions on environmental safety and the circular economy. The authors thank Luca Pardi (IPCF-CNR) for revision of the English language of the manuscript. The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.