PAPERS OF THE SOUTHWESTERN EXPEDITION NUMBER TWO PUEBLO POTTERY MAKING & Courtesy Wesley Bradfield MARIA MARTINEZ The most skillful potter of San Ildefonso. DEPARTMENT OF ARCHAEOLOGY PHILLIPS ACADEMY - ANDOVER + MASSACHUSETTS PUEBLO POTTERY MAKING A STUDY AT THE VILLAGE OF SAN ILDEFONSO BY CARL E. GUTHE LecSPon\ NEW HAVEN PUBLISHED FOR THE DEPARTMENT OF ARCHAEOLOGY PHILLIPS ACADEMY - ANDOVER - MASSACHUSETTS BY THE YALE UNIVERSITY PRESS 1925 COPYRIGHTED 1925 BY YALE UNIVERSITY PRESS PRINTED IN THE UNITED STATES OF AMERICA BY THE ANDOVER PRESS , TABLE OF CONTENTS INTRODUCTION : : : : : 3 : Raw MarTeriaAzts; COLLECTION AND PREPARATION... INGREDIENTS Rep cuay. : WHITE CLAY... : ; ; . : TEMPER : COOKING VESSEL CLAY SLIPS AND PAINTS NATIVE SLIP : Santo DoMINGO SLIP. Rep SLIP ORANGE-RED SLIP BLACK WARE PAINT Buack or GUACO PAINT FUEL MANURE KINDLING. : : : ; : : PARAPHERNALIA ; . PRIMARY PARAPHERNALIA. Mou.tps MOowvLpDING SPOONS SCRAPERS POLISHING STONES PAINT BRUSHES SECONDARY PARAPHERNALIA : : CARRYING AND STORING RECEPTACLES . MIXING SURFACES Boarps WATER CONTAINERS Mors : PAINT RECEPTACLES . : ; : ; WIPING-RAGS_. : : : oi “ FIRING ACCESSORIES Movu.Lpinc . F : 2 : : ‘ : BowLs OLuas... : : ; : f ; 5 COOKING-VESSELS . ! ; : : : PRAYER-MEAL BOWLS : é : ‘ DOUBLE-MOUTHED VASES HANDLES : : ; : : : ; vill PUEBLO POTTERY MAKING PAGE Sun-DRYING . : . . ; : : ' ; : : : ; 52 SCRAPING : ‘ ; ; ; : : , : ; : : , 54 SLIPPING AND POLISHING : ; F : 4 , : ; 57 WHITE SLIP. ‘ : ; : , : ; ; ; ; ; 57 ORANGE-RED SLIP. : ; ; ; } ; ; ' ; : 59 Rep sLip : : : : : : : d ; : 59 DARK-RED SLIP ; ‘ : : ; < : : : E 62 PAINTING . Z ; : : : ; : ’ : ; ; ? 66 FIRING . 5 : : E . : ? ; é ‘ : : 70 PREPARATION : ; : : : : : : : : 70 BUILDING THE OVEN : ; ; , : : : ? 70 BURNING ; : 7 : ; ‘ ; i 3 : : fee ACCIDENTS. A ; z : ; : ; ‘ : :. ‘ 76 TREATMENT AFTER BURNING : : : aT PAINTING OF DESIGNS . ‘ : ; ? ; : 78 SYMBOLISM . < : : : 85 BIBLIOGRAPHY . } : ; : ; 89 ae as gaa el oe i a vcore ee aL onl aN a LIST OF ILLUSTRATIONS PLATES PAGE Maria Martinez, the leading potter of San Ildefonso . : Frontispiece Fragments of ancient corrugated wares : : : ; : Old decorated vessels from the Pueblo villages : . : : 8 Old San Ildefonso vessels. : , : : : 8 Old San Ildefonso vessels : ; ‘ 10 Modern polychrome ware by Maria Martinez . F ; : 10 Modern polychrome and black-on-red wares : ; ; : : 12 Modern plain and decorated Opt black ware : : ; 14 Winnowing clay ; : : 16 a, Digging tempering material. b, Guaco plant . : 20 Gourd spoons ,; 26 a, Kneading clay. b, Primary stages ‘of bowl moulding : ; 32 Method of building vessels é 32 a, Work on rim of unfinished bowl. b, Shaping vessel : 36 Successive stages in the moulding of an olla 42 a, Moulding an olla. 6, A typical potter : 44 a, Finishing touches. 6, Application of handle . ; 46 Sun-drying. ; : 52 Scraping ; , ; 54 a, Cutting down an olla. “s Applying slip ; ; 58 a, Applying slip. 6, c, Polishing ’ : ; 60 Decorating small vessels ' : ; : 66 Decorating ollas_ , : , ; 68 a, Drying the oven site. 6, Preparing the oven . : : 70 Oven-building : ; 72 Firing . ; : : : : 3 : ; . : 72 a, Smothered fire. b, Wiping fired vessels ’ f 5 ; 74 Zufii potter preparing clay ; : ; : : f 76 Zufii potter moulding a vessel . ‘ . Q . ; 76 Zufii potter finishing a vessel. ; : : : 76 Zufii potter decorating and firing a vessel ; } : ; : 76 Design by Maria Martinez ; : : : : 81 Design by Maria Martinez : ; ; : : : : 82 Design by Maximiliana Martinez . ; ‘ ; : ‘ 82 Design by Antonita Roybal. : F : ; : ; : 84 FIGURES IN THE TEXT Outlines of post-Basket Maker vessels ; 3 : : ; : ; 6 Pre-Pueblo pottery ; i , ‘ : : i Decorations of ancient Pueblo bowls. ; : : : 9 Bad examples of modern pottery : ; : ; : f 13 Paint brushes ; : : ; ; 28 Sections of a bowl during building ; 5 : ; : 4 34 Method of terracing a prayer-meal bowl. : : : wi : 48 Angles of paint brush during stroke ; : 2 : : : : 68 Growth of a polychrome gorien ; : : : : : ee Raincloud design : : ‘ ‘ : , 3 ; Elements of design . : ; : ; ; ; : : A : 87 INTRODUCTION The present paper is a careful study by Dr. Guthe of pottery making at San Ildefonso, a typical Pueblo Indian town on the Rio Grande, north of Santa Fe, New Mexico. The field-work was undertaken in 1921 as part of an archaeological survey of the Southwest, that has been carried on for a number of years by the Depart- ment of Archaeology of Phillips Academy. From prehistoric archaeology to modern pottery making may seem a far cry, but in the Southwest the past merges almost imperceptibly into the present, and the Pueblos of today live in almost exactly the same way, and practise almost exactly the same arts, as did their ancestors of a thousand years ago. In the Southwest, therefore, the archaeologist has the in- valuable opportunity of observing, and of studying at first hand, the life whose earlier remains he unearths from the ancient ruins. When one considers what such a privilege would mean to the excavator in, for example, the mounds of the Mississippi Valley, or the Neolithic village-sites of Europe, it becomes obvious that the South- western archaeologist should devote a not inconsiderable part of his time to the study of that industrious, kindly, hospitable, and thoroughly charming folk, the Pueblo Indians. Living a sedentary, agricultural life in an arid country it was inevitable that the Pueblos should early have developed into expert and prolific potters; and so pottery, in the form of sherds scattered about their former dwellings, and of vessels piously interred with their dead, is the most striking, the most abundant, and the most readily accessible form of evidence to be dealt with by the Southwestern archaeologist. The value of pottery to the student of the past cannot be more happily expressed than in the words of the historian Myres: ‘‘ When with the soft clay which has, so to say, no natural shape or utility at all, the human hand, guided by imagination, but otherwise unaided, creates a new form, gourd-like, or flask-like, or stone-bowl-like, but not itself either gourd, or skin, or stone, then invention has begun, and an art is born which demands on each occasion of its exercise a fresh effort of imagination to devise, and of intellect to give effect to, a literally new thing. It is a fortunate accident that the material in question, once fixed in the given form by exposure to fire, is by that very process made so brittle that its prospect of utility is short; consequently the demand for replacement is persistent. The only group of industries which can compare with potmaking in intellectual importance is that of the textile fabrics; basketry and weaving. But whereas basket-work and all forms of matting and cloth are perishable and will burn, broken pottery is almost indestructible, just because, once broken, it is so useless. It follows that evidence so permanent, so copious, and so plastic, that is to say so infinitely sensitive a register of the changes of the artist’s mood, as the potsherds on an ancient site, is among the most valuable that we can ever have, for tracing the dawn of culture.” Myres wrote of arid Egypt, and in many ways conditions in the likewise arid Southwest, where a primitive people were also building up for themselves through agriculture a new type of civilization, closely parallel those of the Nile Valley in 2 PUEBLO POTTERY MAKING predynastic times. And the analogy, naturally enough, holds good in the matter of archaeological methods. The rise and spread of the predynastic cultures of Egypt are being traced out in large part by studies of ceramic types and of their stratigraphic relation one to another. The same methods are applicable, and in- deed are now beginning to be applied, to the problems of the Southwest. To understand the trend of recent archaeological work in the Pueblo field it is necessary to take a bird’s-eye view, so to speak, of the region. Over a vast area in New Mexico, Arizona, Utah, Colorado, and the state of Chihuahua in Old Mexico, are found the remains of the prehistoric Pueblos. Their villages, now in ruins, were built in all sorts of places, on the tops of mesas, in open plains, in narrow canyons, on the ledges of great cliffs, and in the shelter of caves. They range in size from one- or two-room houses of the roughest construction, to great communal buildings of five hundred or even a thousand rooms, compactly built of excellent masonry and terraced to a height of three, four, or five stories. The artifacts, too, found in them vary bewilderingly, both in degree of perfection, and in type. All Southwestern houses, however, and all Southwestern artifacts, have a certain family resemblance that allies them to each other and makes it evident that they are all the product of a single culture, a culture distinct, for example, from that of Central Mexico or that of the Mississippi Valley. To reconstruct the history of that culture, to trace its origin, to follow its growth, and to explain how and why it developed in the peculiar way it did, are the tasks which confront the Southwestern archaeologist. As in any scientific problem, the first step must be to collect and classify the data; and although Pueblo sites are numbered in thousands, and an overwhelming amount of merely descriptive work must still be done, the outlines of a classification have been achieved. We know, for example, what sort of ruins are found in the San Juan drainage of northern New Mexico; what kinds of pottery occur along the Gila river in southern Arizona. But what relationship, genitically and in time, there existed between, say, Pueblo Bonito and Casa Grande, we do not know. The time element, or in other words the historical sequence of our material, remains in large part to be determined. To set up an historical outline we must first determine the relative ages of the different ruins, and then estimate the size and distribution of the Pueblo tribes from the earliest times to the present. At the top, so to speak, of our series the problem is simple enough — we are acquainted with the present location of the tribes, and the various Spanish accounts tell us where they have been living during the past three hundred and fifty years. But for the prehistoric period (and everything in the Southwest prior to 1540 is prehistoric) we must rely almost wholly on such evidence as may be turned up by the archaeologist’s shovel, for of native written records there are none, nor can native legendary testimony be safely depended upon. This, of course, throws a heavy burden upon the archaeologist, a burden which is made heavier by the fact that stratigraphy of remains is so rarely found in the Pueblo country. Stratigraphy, in other words the superposition of the more recent upon the more ancient, has been the Open Sesame to all the reconstructive sciences. The very frame- work of geology, for example, has been built up from stratigraphic observations. INTRODUCTION 3 In archaeology, too, stratigraphy has revealed the sequence of the Stone Ages; made clear the development of the early Mediterranean cultures, and the rise of predynastic civilization in Egypt. Therefore, as has just been said, the general lack of stratigraphic conditions in the Southwest renders the task of the student a particularly hard one. For some reason, not yet clearly understood, the Pueblos ancient and modern were very prone to shift from one dwelling place to another, and a site once abandoned was seldom reoccupied. Although their houses were of the most permanent construction, and their agricultural life should have tended to render them solidly sedentary, they moved about to a surprising extent. The result of this is that one seldom finds a ruin which was lived in for more than a few decades or, at most, centuries; and few have so far been discovered to contain super- imposed remains illustrating any long period of development. Where such evi- dence is so rare, what can be found naturally becomes of the greatest importance; hence the recent diligent search for, and excavation of, such sites as show signs of long occupancy. The choice of Pecos for investigation by Phillips Academy was due to the above considerations. The ruin was a large one, was occupied at the time of the Discovery and was not abandoned until 1838. A surface examination also showed that it must have been tenanted for a long time prior to the Conquest because its mounds were scattered over with potsherds not only of recent date, but also of several distinct prehistoric types, each one well enough known to students, but whose relative ages were entirely a matter of conjecture. It was hoped, therefore, that excavation might disclose some definite cases of superposition, and that several prehistoric periods might thereby be arranged in their proper chronological order.! The results have been more than satisfactory. Pecos proved to have been built on the edge of a sharp-sided mesa, a fact not suspected before digging began, because the rubbish from the town had heaped up to such an extent against the original cliff as completely to mask its steepness. The first inhabitants naturally threw their refuse over the edge of the mesa, their descendents added to the accumu- lation, and the process continued down the centuries until there grew up a midden of enormous extent and, for the Southwest, of unusually great depth. It is stratified as neatly as a layer-cake. When the exploratory trenches revealed the size and probable importance of the Pecos rubbish heap, all other projects were postponed, and two full field-seasons were devoted to the meticulous dissection of large areas of the deepest deposit. At frequent intervals stratigraphic tests were made, in which all the specimens from each successive stratum were kept separate and shipped to the Museum for study. It was found that many changes in culture had taken place during the long occu- pancy of Pecos; in the stone and bone implements, in the pipes, and in burial customs. But the most abundant, the most easily gathered, and the most readily interpreted evidence of cultural change was offered by the thousands of pottery fragments that filled the mound from subsoil to surface. 1 A brief history of Pecos, and a description of the work so far done at the site, are contained in “An Introduc- tion to the Study of Southwestern Archaeology, with a Preliminary Account of the Excavations at Pecos’’, by A. V. Kidder; No. 1 of the present series. 4 PUEBLO POTTERY MAKING We have been able to recognize about twenty distinct wares, to arrange them into eight chronological groups, and to determine the exact sequence of these groups. This information, derived from the stratigraphic study of the pottery in the mounds, has been of the greatest value. Its application has been both local and non-local. In the excavations that we have since carried on at Pecos it has enabled us to date relatively to each other the various kivas, cemeteries, and small refuse mounds that occurred on the mesa top, and also to unravel much more confidently than we would otherwise have been able to do, the extraordinarily complex jumble of ruined, torn- down, stone-robbed, rebuilt, abandoned, and reoccupied rooms that we encountered when we attacked the pueblo itself. As helpful as has been the knowledge of the sequence of the pottery types in working out the details of local archaeology, its usefulness in that regard is small as compared with the flood of light which has been thrown on much larger and more vital problems. It has just been stated that some twenty types of pottery were identified; the majority of these are not peculiar to Pecos; many of them occur throughout large areas in the Rio Grande drainage; and so we are now able, in most cases by a hasty examination of the surface sherds, to assign to its proper place in the chronological series any ruin at which our types are present. Thus mere reconnaissance (a cheap and rapid undertaking) now serves to make clear the major outlines of Rio Grande archaeology. But the usefulness of the stratigraphic studies at Pecos does not end with the territory in which the Pecos types of pottery are found, for Pecos, because of its size and because of its situation on the main route between the Pueblo country to the West and the buffalo ranges to the East, was an important trade centre. From its mounds we have taken potsherds from almost all parts of the South- west, shells from the Pacific, spindle-whorls from Central Mexico, as well as pottery and stone objects from the Mississippi drainage. The importance of such finds is evident; every sherd from an outside culture found in a datable stratum at Pecos helps to fit into our general chronological scheme the culture from which it came; as conversely, does every Pecos or even Rio Grande sherd that turns up beyond the limits of the Rio Grande. Only a start has been made, but enough has already come to light at Pecos and at such stratified sites as have been excavated by other institutions, to provide us with a surprisingly full knowledge of the rise and growth of the Pueblo civilization. Ten years ago it would have been hard to believe how much could be accomplished by the stratigraphic work carried on by Nelson in the Galisteo Basin, Hodge at Hawikuh, Judd at Pueblo Bonito, Morris at Aztec, Guernsey in the Kayenta country, and the writer and his associates at Pecos. The work, as I have said, has just begun, but the prospects are bright. Success will depend, as in any such endeavor, upon intelligent excavation, careful collection of data, and accurate observation of specimens, but the investigator cannot hope to derive the best results from his labors if he does not hold to a very broad view of his field. He must familiarize himself not only with the material of the locality he is working in but must also know as much as possible about that of other regions, for it is of the last importance that trade-objects be recognized wherever they occur. Of all trade-objects, vessels and potsherds are likely to be the commonest and most easily recognizable. INTRODUCTION 5 When the members of the Pecos expedition realized how vitally important was to be a close knowledge of the pottery, not only of that particular site, but also of the Rio Grande in general, and, indeed, of the entire Southwest, they devoted a large part of their time, both in the field and at the Museum, to the study of ceramics. A difficulty was at once encountered in our ignorance of the technique of Pueblo pottery making. We were constantly obliged to compare the paints and slips of different wares, to decide whether observed variations were technically fundamental, or were merely accidents of clay-mixing or firing. No full published accounts existed, nor had any of us had the opportunity for more than casual obser- vation of potters at work. Dr. Guthe, accordingly, spent the month of August, 1921, at San Ildefonso in making detailed studies. His results are published in the hope that they may be of use to Southwestern archaeologists and ethnologists, and also to students of the primitive pottery of other areas who may be in need of material for comparative purposes. In order that the reader may envisage the long history that lies behind the work of the modern potters, I give a summary of our present knowledge of the origin and development of pottery in the Southwest. To go back to the very beginning, it is not yet certain whether pottery making was introduced into the region from Mexico, or whether it was a local invention. There is evidence in favor of each theory. As will presently be shown, there can be traced in the Southwest an almost unbroken development from the earliest and crudest forms, through intermediate stages, to the perfected styles of later times; nor can Mexican influence be seen in the wares themselves at any period from beginning to end. Hence it might appear that the art was of purely local origin and growth. On the other hand, Mexico was the breeding ground for all the higher elements of native American culture: corn-growing, the cultivation of cotton, the use of stone masonry, the true loom, etc., and it is practically certain that all these traits worked into the Southwest from Mexico. It would thus seem reasonable to suppose that the concept of pottery came from the same source, particularly as pottery does not appear in our area until some time after the introduction of corn, and the mere presence of corn proves contact of one sort or another with Mexico, where presumably pottery had been in use for a considerable period. My present feeling is, however, that the importation consisted of no more than the bare idea that vessels could be made of clay, and that the subsequent development of the art was entirely unaffected by outside influences. This question, so important for its bearing on general problems of dissemination versus independent origin of culture traits, can only be settled by work in the archaeologically still unknown field of northern Mexico. The earliest inhabitants of the Southwest of whom we have certain knowledge were the Basket Makers, so called by their discoverer because basketry rather than pottery was buried with their dead. They lived in southeastern Utah and northern Arizona, were an agricultural or semi-agricultural people who built no permanent houses, and who had no true pottery. In some of the caves that they occupied, however, there have been found a few fragments of crude, unfired clay dishes whose thick, bungling sides bear the imprints of the fingers of their makers. Save for 6 PUEBLO POTTERY MAKING occasional hesitating lines of incised marks, or straggling daubs of black paint, these vessels are undecorated. They bear no slip, nor, as was said above, were any of them subjected to the burning which would have converted them into true pottery. In the course of time, though whether that time should be counted in tens, or hun- dreds, or even thousands of years, we have at present no way of telling, the Basket Makers began to build houses of stone slabs, to group their hitherto scattered dwellings together into small communities, and, most important of all from the point of view of our present inquiry, to make hard, thin-walled, thoroughly fired vessels, in other words real pottery. The culture stage characterized by these OCse SEO Fic. 1. Outlines of Post-Basket Maker vessels. (Courtesy S. J. Guernsey.) remains and further distinguishable from the classic Basket Maker on the basis of house structure, sandal form, and other traits, was first identified by S. J. Guernsey, and named by him “‘post-Basket Maker’”’. Post-Basket Maker pottery is simple in form and in decoration. It is normally light gray in color. The vessel forms most commonly found are bowls (fig. 1, d, e), globular vessels with restricted orifices (fig. 1, a), and water jars, the latter often having a swollen neck (fig. 1, b). The body of the ware in cross-section has a markedly granular appearance, due to the large size of the bits of tempering material included in it. A small percentage of the bowls bear a thin white slip on the interior PLATE 2 ANCIENT CORRUGATED WARES a. Pre-Pueblo. b. Early Pueblo. ec. Classic Pueblo period. INTRODUCTION 7 and are ornamented with irregularly drawn designs in black paint (fig. 1, e). Many of the patterns suggest basketry prototypes. All in all, post-Basket Maker pottery, judging from the few specimens so far recovered, is surprisingly well made; so well as to raise the suspicion that an earlier stage still awaits discovery. Hints of such a stage have, indeed, been found in the form of heavy clay dishes, tempered with shredded juniper bark, unbaked but dis- tinctly superior in size and workmanship to the Basket Maker product. These specimens have turned up in post-Basket Maker sites, but in caves stratigraphically so confused that it is still uncertain whether they antedated, or were contempo- raneous with, the more highly-perfected post-Basket Maker wares. They are too crude, however, to be considered the direct forerunners of post-Basket Maker pottery. If the development took place in the San Juan, one step at least is still lacking. These questions will be answered by further work of the sort now being carried on by Guernsey in the Kayenta country and by Morris in the Canyon del Muerto. Fic. 2. Pre-Pueblo vessels. From post-Basket Maker times down to the present day, however, the develop- ment of Southwestern pottery can already be outlined with considerable confidence. The next stage is usually called the pre-Pueblo. It is marked by further improve- ments in house-building, by the introduction of cranial deformation, and by certain innovations in ceramics. It had been the custom with the post-Basket Makers (as among many primitive people) to build up their vessels by adding to the growing walls successive rings of clay. When the process was complete and the sides had reached the requisite height, all trace of the rings was obliterated by rubbing down the surface. In the interiors of some post-Basket Maker pieces, however, with orifices so small that a smoothing tool could not be introduced, there were left the telltale junction-lines between the structural rings. In pre-Pueblo times it became the fashion purposely to leave unsmoothed the last few rings at the necks of certain small cooking vessels (fig. 2, a; pl. 2, a). This was the beginning of the elaborate coiled or corrugated technique, later so widely used. Pre-Pueblo black-on-white ware takes the form of bowls, pitchers, ladles, small jars, and ollas. Its paste is hard, is less heavily tempered than post-Basket Maker 8 PUEBLO POTTERY MAKING paste, and the surfaces of the pieces are better smoothed. The decoration is characterized by boldness and dash, the brushwork being correspondingly hasty. The lines are of irregular width, nor was care exercised that the junctions of strokes should be accurate. As is shown by the accompanying drawings (fig. 2, b, c), the commonest elements are the stepped figure and the triangle, both often emphasized by sets of widely spaced thin lines which follow the outer edges of the basic patterns. The transition between the pre-Pueblo and the Pueblo was evidently a gradual one. There was no violent break, either in culture or in physical type; and so it is hard to say just where the dividing line should be drawn. The introduction of indented corrugated pottery, however, forms a convenient milepost on the road of ceramic progress. The change was brought about as follows: the plain, broad rings of pre-Pueblo ware were replaced by a continuous thin fillet of clay applied spirally; the junctions between the successive laps of the fillet were left unobliterated, not only at the neck, but over the entire vessel; and the fillet itself was also notched or pinched or otherwise indented to produce various ornamental effects (pl. 2, b, c). Thus was made the well-known coiled or corrugated cooking-ware so characteristic of all the archaic true Pueblo ruins, a style introduced at about the same time as the development of the above-ground rectangular living-room, the clustered method of building, and the use of horizontally coursed masonry, all elements that are com- monly recognized as typical of true Pueblo culture. The earliest varieties of Pueblo pottery are imperfectly known, for little work has so far been done in the small and often nearly obliterated mounds that mark the house-sites of the first pueblo- dwellers. It is certain, however, that in the San Juan and Little Colorado drainages there was a strong growth in corrugated ware. This technique was experimented on and played with. The variety and even virtuosity of the results are extraordinary: waved coiling, pinched coiling, incised coiling, and all manner of indenting were practised (pl. 2, b). The black-on-white ware evidently did not advance so rapidly, the vessels, to judge from the sherds, were not particularly symmetrical as to shape or notable as to finish. The decoration ran to hachure in wavy lines and to poorly drawn spiral figures. As I have just said, little is known of the early Pueblo sites. The period which they represent, however, was undoubtedly a long one. The date of its beginning is entirely problematical, nor can we even say with any assurance when it ended, but the probabilities are that as early as the opening of the Christian era the Pueblos had begun to gather together into larger settlements, to develop the closely-knit community life, and the many-storied terraced style of architecture which typify the golden age of their existence. Between that time and 1000 or 1100 A.D. the more or less uniform early culture split up into distinct and often highly specialized local sub-cultures, each of which followed its own line of growth in house-building, pottery-making, and the minor arts. It was during this general phase of Southwestern history that there came into being the great pueblos and _ cliff-dwellings that housed entire villages: Pueblo Bonito and the other Chaco Canyon towns; the cliffhouses of the Mesa Verde and of the Kayenta country; the enormous adobe constructions such as Casa Grande on the Gila and Casas Grandes in Chihuahua. PLATE 3 OLD MODERN DECORATED WARE a. Acoma. b. Zufii. c. Sia. d. Hopi. e. San Ildefonso. f. Tesuque. g. Santo Domingo. h. Cochiti. "ORT poysyod “pO ynq-uo-yorg *q ‘e OSNOJHGTI NVS WOUA SHOHId ATO ~ ALVId i ) a INTRODUCTION 9 To describe the many different wares of the classic Pueblo period would entail far more space than is available in this introduction. Brief accounts of the more important styles are included in the first paper of the present series,! and a handbook of Southwestern pottery will, it is hoped, appear as a subsequent number. A single ALY Fic. 3. Black-on-white bowls of classic Pueblo period. a. Chaco Canyon. b. Mimbres Valley. c. Upper Gila River. d. Mesa Verde. illustration (fig. 3) must suffice to show the bewildering variety and the high artistic perfection which were reached at this time. It seems ordained that periodsof high achievement shall be followed by periods of slackening and even atrophy. So it was with the Pueblos. The years between about 1 Kidder, 1924. 10 PUEBLO POTTERY MAKING 1000 A.D. and the Spanish invasion of 1540 were evidently a time of tribulation. The formerly prosperous communities of the North and the South were abandoned, the population shrank, the arts degenerated, and when Coranado entered the Southwest he found the Pueblos occupying a mere fraction of their former range. What brought about this decline is not surely known, droughts, intertribal wars, pestilences, inbreeding, may all have been in part responsible; but its principal cause was probably the ever-increasing attacks of nomadic enemies. At all events Pueblo culture of the sixteenth century was not what it had been in the past, and pottery making suffered with the other arts. By that time the beautiful and elaborate, but difficult, corrugated technique had been given up, and cooking vessels had become mere unornamented pots; black-on-white ware with its hand- some, intricate geometric decoration had long been extinct, replaced by various local styles, few of which equalled it in technical excellence or artistic perfection. As a matter of fact the ceramic products of the historic period are very little known. In old times pottery formed an essential accompaniment of the dead, hence at nearly every prehistoric ruin may be found a burial place richly stocked with mortuary vessels. With the arrival of the priests, however, missions and Catholic cemeteries were established, all interments took place under the supervision of the Padres, and no more bowls or ollas went into the graves. Pottery, of course, is short-lived, few vessels, other than reverently guarded ceremonial jars, can be expected to escape breakage for more than a generation or two, and so we have practically no material to illustrate the changes which took place between the Conquest and the present day. Much will eventually be learned in regard to seventeenth and eighteenth century Pueblo pottery, but the work will have to be done largely on the basis of sherds from the rubbish heaps of the older towns, and such broken pieces as may be found under the fallen walls of abandoned dwellings. We can, however, supplement this research by working backwards, so to speak, from the modern wares. If we can acquire a thorough knowledge of them it will be much easier to understand the fragmentary material we shall have to deal with in studying the early historic period. We should accordingly collect all possible data as to the wares turned out in recent years at the various pottery-making Pueblos. The term pottery-making Pueblos is used advisedly, for, queerly enough, no pottery is manufactured at a number of the towns. If this condition had come about within the last decade it would be easy to account for, as tin oil cans for holding water, enamelled pots for cooking, and china dishes for serving food have lately been pushing native pottery out of use. But no pottery, other than rough cooking ware, has been made for a long time at Taos, Picuris, San Felipe, Jemez, and Sandia; while the art is practically or wholly extinct at Laguna, Isleta, and Santa Ana. Potters occasionally marry into these towns and continue to exercise their craft, but they seem to have no disciples among their daughters or among the local tribeswomen. At all the other Pueblos, however, potting is still carried on, but in most cases with a decreasing output and a lamentable degeneration in technique. The vessels, being mostly made to sell to tourists or curio dealers, are carelessly fashioned, crudely decorated, and insufficiently fired, Good contemporary pieces PLATE 5 OLD MODERN SAN ILDEFONSO WARES a, ce, d. Polychrome. b, e. Black-on-red. PRESENT-DAY POLYCHROME WARE BY MARIA MARTINEZ PLATE 6 Courtesy K. M. Chapman INTRODUCTION 11 are becoming rare, and the older vessels, which are naturally the best material for study, are now almost gone from the villages. Some pieces, however, are still left, and many more are in the hands of Mexicans and Americans living in the South- west. These should be got into the custody of museums as rapidly as possible, for pottery is fragile stuff and every year sees the breakage of many unreplacable old vessels. Excellent work in collecting and preserving the older pieces is being done by certain residents of Santa Fe, who have organized the ‘Southwestern Pottery Fund’. In spiteof limited resources they have got together a most remarkable collec- tion from the Eastern pueblos, and are constantly adding to it as specimens come into the market. A plate showing a typical example of old modern decorated ware from each of the pottery-making pueblos is here given, in order that the reader may appreciate the striking differences which obtain (pl. 3); San Ildefonso vessels of this period are illustrated elsewhere (pls. 4, 5). In closing this introduction something should be said of the older San Ilde- fonso wares, and of the remarkable renaissance which has led to the high artistic achievements of the present-day potters. Of the pottery made at San Ildefonso during the early historic period we have as yet no definite knowledge, but from the fact that the sherds at the ruined pueblo of Cuyamongé, a Tewa village only a few miles from San Ildefonso which was abandoned in 1698, are closely similar to the seventeenth century wares of Pecos, we may conclude that the San Ildefonso product of that time also bore resemblance to that of Pecos. The Pecos wares in question have as yet been but briefly described.! The following are the leading varieties: rough black cooking ware; polished red; polished black; and decorated ware of two varieties, black-on-buff, and black-and- red-on-buff. The ornamentation is in heavy black lines, for the most part sloppily drawn, but the designs are bold, free, and effective. Although these styles all differ to some extent from the ceramics of late nineteenth century San Ildefonso, the artistic and technical relationship of the two groups is evident at a glance. The principal differences lie in the much greater amount of polished red found at Pecos, and in the absence from Pecos of a black-on-red decorated ware made at San Ildefonso. What we know of nineteenth century San Ildefonso pottery is derived from pieces found in the pueblo when collecting began about 1870; and from vessels secured between that date and 1900. The oldest examples we have were thus probably not made much before 1850, and the great bulk of the specimens now in museums and in private hands were presumably turned out during the last third of the century. This material (aside from cooking pots, of which the older collections contain practi- cally no examples) is divisible into five types, two plain and three decorated. The plain wares are polished black and polished red; the decorated are black-on-buff, black-and-red-on-buff (usually called polychrome), and black-on-red. The polished black and polished red are, as Dr. Guthe brings out in greater detail below (p. 74), merely variants of the same ware — the red being produced by a preliminary burning in a more or less open fire — the black by smothering the 1 Kidder, M. A. and A. V., 1917, p. 330. 12 PUEBLO POTTERY MAKING fire with pulverized manure at a late stage in the burning. Vessels of both sorts were evidently made at San Ildefonso during the period under discussion, the red rarely, the black fairly commonly. It is usually supposed that the making of these wares, particularly the polished black, was confined to the nearby town of Santa Clara, and vessels of the latter type are ordinarily referred to as “Santa Clara black’. This is a natural enough error as the Santa Clara turn out nothing but the polished wares, and until the last ten years they led all the other pueblos in the excellence of their manufacture. The Indians of San Ildefonso, however, say that they have always made polished black pottery, and while its production may have partly or wholly lapsed during the 90’s and early 1900’s, there is little doubt that many of the older specimens, such as the ones here illustrated (pl. 4), are actually from San Ildefonso. The majority of the examples of old black are large storage jars with full, round bodies and relatively small orifices; there are also capacious bowl-like vessels (called by the Mexicans cajetes), which were used for the mixing of dough. The old pieces are less meticulously finished than are those of today, but their deep, velvety black lustre is of even greater beauty than the extremely high polish of the modern pieces. The black-on-buff decorated ware was evidently the commonest variety of nineteenth century pottery. It took the form of prayer-meal bowls (small open vessels with terraced sides) ; medium-sized pots (pl. 3,e); and large storage jars (pl. 4). The ware, like all San Ildefonso work, is thick and heavy, giving a “woodeny” sound when tapped. The surface color is a creamy buff and the decoration is in deep black pigment. The bottoms of all the pieces, and the interiors of the necks of the jars, are painted red. The general nature of the elaborate designs is best brought out by the illustrations. Black-and-red-on-buff or polychrome was apparently not an abundant style in old times. Its occurrence at Cuyamongé and at Pecos, however, seem to indicate that it was always made at San Ildefonso. There are also in museums and private collections pieces which appear to be as old as any of the examples of non-poly- chrome. The style was seemingly limited to bowls and small jars (pl. 5). The ware itself is the same as the foregoing, but various areas in the decorations (which them- selves seem to differ from those of the black-on-buff) are filled in with a purplish red paint of very characteristic shade. The red-on-black, like the polychrome, was not common. As was said above, it is absent from Pecos and Cuyamongé, therefore it is apparently of fairly recent origin in the Rio Grande. Its introduction or invention may, indeed, date from as recent a time as 1850. It differs from the buff wares in having a dark red slip, much more highly polished than are the buff slips. The decoration is in deep black. No large pieces, as far as I know, were made, most specimens being small globular jars without necks. One of these and a vase-like vessel are illustrated (pl. 5). Such was the pottery of San Ildefonso during the second half of the nineteenth century. ‘Toward the end of that period, however, a marked degeneration set in. 1 A searching study of San Ildefonso decoration has been made by K. M. Chapman of Santa Fe. When this is published it will throw much light on the morphology of Pueblo design, and upon the relation of San Ildefonso symbolism to that of other Rio Grande pueblos. PLATE 7 Courtesy K. M. Chapman c PRESENT-DAY SAN ILDEFONSO POTTERY a, b. Black-on-red by Antonita Roybal. c. Polychrome, by Maria Martinez — one black-on-red piece by Maximiliana Martinez. INTRODUCTION 13 This was due to the substitution for native pottery of American utensils for cooking, food-serving, and containing water; and to the growing tendency to produce pottery for sale to curio stores and tourists rather than for home use. The black-on-buft ware and the polished black were given up entirely, the potters concentrating on the more showy black-on-red and particularly on the polychrome. In the case of the black-on-red the high gloss of the older pieces was no longer produced, and the paint, being neither carefully mixed nor sufficiently aged (see p. 26) developed on firing a dull, bluish cast. The polychrome also fell off in technical perfection and in artistic excellence. The old, dull, purplish reds were replaced by brighter colors, the designs became flamboyant, and many ugly non-Indian vessel shapes were introduced (fig. 4). This state of affairs went from bad to worse until, in 1907, the potter’s art at San Ildefonso was in a thoroughly bad way. A few women, however, Fig. 4. Bad examples of modern pottery — un-Indian shapes and slipshod decoration. retained something of the old craftsmanship and were ready to profit by the oppor- tunity which was about to present itself. In 1907 Dr. E. L. Hewett of the School of American Research began a series of excavations in the ancient ruins of the Pajarito Plateau. The diggers were all Tewa Indians from San Ildefonso. They proved to be excellent shovelmen, who took a keen interest in everything they found. They helped us identify many specimens which would otherwise have been puzzling, and their comments on the pottery, and especially on the designs, were most illuminating. The women of the Pueblo, when visiting camp, often held animated discussions as to the vessels from the ruins, and it was suggested to some who were known to be good potters, that they attempt to revive their art, and try to emulate the excellence of the ancient wares. While the response was not immediate, there was observable, during the next few years, a distinct improvement in the pottery of San Ildefonso. Realizing the importance of 14 PUEBLO POTTERY MAKING this, the authorities of the Museum of New Mexico and the School of American Research threw themselves heartily into the task of stimulating the industry. They urged the women to do better and better work, and in particular induced them to return to the sound canons of native art. Some old pieces remained in the pueblo, many others were in the Museum, of still others photographs were obtained. These were all brought to the attention of the potters. The undertaking was not an easy one, however, for it was difficult to get most of the women to go to the trouble of making good pieces when the tourists, who were still the principal purchasers, were equally or even better pleased with imitations of china water-pitchers, ill-made raingods, and candlesticks. The problem thus re- solved itself into one of supplying a market. The Museum bought many good pieces, and Mr. Chapman, who from the beginning had been a leading spirit in the attempt at rehabilitating the art, himself purchased large amounts of pottery, never refusing a creditable piece, never accepting a bad one. Progress was slow, but eventually certain women, becoming interested in their work, made real progress both technically and artistically. Their products began to sell more freely and at better prices than did those of others. Antonita Roybal, Ramona Gonzales, Maximiliana Martinez, and Maria Martinez all turned out fine vessels, the two latter being greatly aided by their husbands, who developed into skillful decorators. Maria especially shone. By 1915 she had far surpassed all the others, her pots were in great demand, and at the present time she has a ready market, at prices which ten years ago would have seemed fantastic, for everything she can find time to make. Her income is probably not less than $2,000.00 a year, and following her example, many other women are now doing fine work and are earning substantial amounts. The beneficial effect of this on the pueblo has natur- ally been great. New houses have been built, new farm machinery, better food, and warmer clothing have been bought, and, best of all, there has been acquired a wholesome feeling of independence and of accomplishment, the value of which cannot be gauged in dollars and cents. From the point of view of ceramics the development has been most interesting. Maria began with the manufacture of polychrome ware, as that was the style most commonly being made at the time. The shapes were improved, the finish of the surfaces was given greater attention, and the decorations were applied with a surer, more delicate touch (pl. 6; pl. 7, ¢). Black-on-red ware was taken in hand, the old- time polish was restored, the vegetable paint properly prepared and aged (pl..7, a; b). Polished black was also reintroduced; pieces of this sort, with their simple, graceful shapes and high black gloss sold so well that they soon became an important product (pl. 8, b). In 1921, as Dr. Guthe records (p. 24), Maria discovered how to apply to polished vessels dull designs which give the appearance of being etched (pl. 8, a). This method was in its infancy when Dr. Guthe made his study, but it has since proved so remarkably successful that it bids fair to drive out completely the making of plain polished ware. Late in the past autumn there appeared at the Indian Fair in Santa Fe, some pieces of a warm pinkish color, an entirely new de- parture in San Ildefonso pottery making, and one which promises much of interest. Developments and changes in design have kept pace with the improvements in PLATE 8 eee = Courtesy K. M. Chapman PRESENT-DAY POLISHED BLACK WARES INTRODUCTION 15 technique, yet the developement has been purely Indian, and the basic processes of today are essentially the same as they were a hundred or a thousand years ago. A somewhat similar revival has taken place at the Hopi towns in Arizona. In 1897 Dr. J. W. Fewkes of the Bureau of Ethnology was excavating the ruin of Sikyatki near First Mesa. Nampeo, a woman of Hano, the wife of one of the workmen, observed the beautiful old bowls that came from the graves, skillfully copied their designs and then searched out beds of clay that could be burned to the exact shades of the ancient pieces. Her work was a direct imitation of a lost style rather than a development, such as Maria’s, of a current one; but the effect has been no less extraor- dinary. Nampeo’s bowls and ollas were so attractive that they sold well; they were copied by other women for sale and for their own use, and thus the potter’s art of the Hopi was not only greatly stimulated but also radically changed. In addition to their economic importance, the cases of San Ildefonso and Hopi are of great interest as anthropological phenomena. The stimulus at both places was of course partly commercial, but it could scarcely have acted without an inher- ent capacity for rapid artistic and technical progress among the Indians themselves, nor could it possibly have brought about such great results without the inspiring example of exceptionally gifted leaders. It is, therefore, quite conceivable that other stimuli, as the discovery of new clays of surpassing excellence, or of fine new pig- ments, may have proved equally potent in ancient times, and that some of the striking mutations in pottery making, which have so puzzled archaeologists, may have been originally started by such discoveries, and been brought to fruition by the genius of prehistoric Marias and Nampeos. A. V. KippER Director Pecos Expedition _ a _ Dian eon Pane Bp < - . ; a ve - wt oh : PUEBLO POTTERY MAKING By CARL E. GUTHE The Pueblo of San Ildefonso is a Tewa village of about one hundred people, situated on the east bank of the Rio Grande some twenty miles northeast of Santa Fe, New Mexico. San Ildefonso was chosen for the present study because its women have always been skillful potters, and under the wise and friendly encourage- ment of the authorities of the School of American Research at Santa Fe have of recent years been steadily improving in their work without, however, sacrificing any of their native methods. Furthermore, they make more varieties of pottery than are turned out at any other one village. Last, and in some ways most important, the men of San Ildefonso have for a long time been accustomed to work in the vari- ous excavations carried on by the School, cordial relations have been established, the confidence of the Indians has been thoroughly won, and I did not encounter that reticence toward strangers, so characteristic of the Rio Grande Pueblos, because I was known to be a friend of their friends. To the Pueblo woman pottery making is simply one of the mechanical house- hold tasks, just as dishwashing is among us. Nearly every woman at San Ildefonso is a potter, good, bad, or indifferent. In two cases, at least, women have developed into real artists, and are relieved of other household duties in order to devote their time to pottery making. Each potter of today watched her mother make innumer- able pots while she was growing up, and now with a family of her own, she makes pottery just as did her mother. Many steps and small details are carried out for no other reason than that the mother used to do likewise. Obviously every potter has her own technique, which differs slightly from that of others. The daughters in one family work in more nearly the same manner than outsiders, because they all have had the same teacher. In this report the attempt has been made not only to record the essential steps in the making of pottery, but also to note individual variations as an index of the amount of latitude a given process may permit. Because religion and ceremony play so important a role in the everyday life of the Pueblo Indians, it is certain that there must be involved in the making of pottery and particularly in its decoration, a mass of esoteric beliefs and practises. The Pueblos, however, are so loath to refer in any way to the mystical side of their existence, and, if it is even mentioned, at once become so suspicious, that it seemed best to steer clear of all allusion to such matters. The present report, therefore, 18 PUEBLO POTTERY MAKING confines itself to a description and discussion of the purely technical side of the potter’s art. The writer is indebted to the staff of the School of American Research, especially to Mr. Kenneth M. Chapman, for the facilities given for and the interest shown in the work; also to the Governor of San Ildefonso, Juan Gonzales, for his cordial codperation. Of the eight informants used, Maria, wife of Julian Martinez, and Antonita, wife of Juan Cruz Roybal, should specially be mentioned because of their constant patience, and their willingness to answer the many questions which to them must often have seemed absurd. Thanks are also due to the American Museum of Natural History, New York, for the photographs of pottery making at Zufi (pls. 28-31) which are introduced in this paper for comparative purposes. PLATE 9 WINNOWING CLAY a. Hand method. As the material is sifted through the uplifted hands, the wind blows the fine, pure clay upon the shaw] at the left, while the heavier impurities drop back on the pile. b. Basket method. The clay is repeatedly tossed upward from the basket, until all the fine particles have been blown out and have fallen upon the shawl. wan al Pe . WW. RAW MATERIALS; COLLECTION, AND PREPARATION INGREDIENTS Red Clay} The region most often visited for obtaining this clay is directly south of San Ildefonso, about a quarter of a mile from the village itself, in the arroyos of the low hills.2 The deposit lies directly under a sandstone ledge and spreads over a con- siderable area. The clay is in the form of soft earth, easily scooped up with the hand. In gathering it the Indians first scrape off the top half-inch or so, which contains impurities such as small pebbles and twigs. When an area from two to three feet in diameter has been cleared in this way, the clay itself is scooped into a loose pile in the centre of the space, and transferred by the cupped hands into a woman’s shawl or a gunny-sack, and so transported to the house on the back.? One method of cleaning the clay may be used either at the beds or at home. The material is winnowed like wheat to remove small pebbles and fine gravel, either of which will ruin a vessel. The larger impurities are of course picked out by hand. The cloth containing the clay is placed in front of the woman and a second cloth or shawl is spread on the ground to leeward of her. A gusty wind requires several shiftings of the shawl, to the woman’s evident annoyance. A double handful is lifted and allowed to sift through the fingers; the fine particles and dust are blown upon the shawl by the wind, while the heavier pieces fall again upon the pile of uncleaned clay (pl. 9, a). The height to which the hands are lifted, varying from three to five feet, the speed of the movements, and the rapidity with which the material is allowed to sift through the fingers, all depend upon the force of the wind. Sometimes, instead of lifting the clay in the hands, it is allowed to flow over the side of a shallow basket tilted toward the woman at the level of her shoulder; the coarser particles fall straight down in front of her on the pile of uncleaned clay. Another variation is to toss the clay into the air from a shallow basket (pl. 9, b). The movement is repeated quickly and rhythmically; the wind as before blowing the fine stuff on the shawl, while the coarse particles fall back into the basket. After this tossing has been repeated a dozen or more times, the residue, which consists mostly of coarse impurities, is thrown away. ‘The process occupies approximately half an hour, depending somewhat upon the amount of clay handled. The cleaned 1A vocabulary of the Tewa terms for clays, paints, and other ingredients; articles of paraphernalia; types of pottery; processes of pottery making, etc., was recorded by Dr. Guthe, and is available at Andover for consultation. 2 See Harrington, 1916, Map 19, point 63. Under the nearby point (60; p. 314) he says: “Clay . . . is ob- tained at this place; just where could not be learned.” 3 Stevenson, to whom with Mrs. Stevenson we are indebted for practically our only comparative material, wrote in 1879 of Zufi: “The clay mostly used by the Zufiians in the manufacture of pottery is a dark, bluish, carbonaceous clayey shale found in layers usually near the tops of the mesas”’ (1883, p. 329). Later, Mrs. Stevenson described at some length the ceremony of securing pottery clay (1904, p. 374). Among the San Ildefonso Indians of today there is no outward evidence of any such ceremony. 20 PUEBLO POTTERY MAKING clay, which is now ready for mixing, is by no means entirely dust; it contains no lumps, but flaky particles fully three-sixteenths of an inch across are often found in it. If at the time of gathering the wind is not strong enough for winnowing, the uncleaned clay is brought to the house. Here it may be kept for a windy day, or may at once be sifted through an ordinary kitchen sieve of medium large mesh. The clay, when cleaned, may be stored in a variety of receptacles (pottery vessels, sacks, or boxes), or, if it is the intention of the woman to use it within a few days, it is simply left in the shawl. During the fall the Indians gather great quanti- ties of clay, and pile it on the floor in the corner of a room for use during the winter when the clay beds are frozen. The preparation of the clay for use consists of two processes, mixing and kneading. The mixing, which as a rule immediately precedes the kneading, con- sists of the addition of temper (see page 21). This is done while both ingredients are dry. Different varieties of clay are not mixed together. The work is done on a piece of canvas, an opened cement-sack, or the inner side of a skin (usually that of a goat or dog).! Either the clay or the temper may be put on the mixing surface first; the other ingredient is then added, and the whole is sifted through the fingers until the mass is uniform in color. The Indians have no definite idea of the neces- sary proportions. They judge simply by the color of the resulting mixture. The proportions used by three different informants seemed to be about one-third temper and two-thirds clay. Before mixing, the clay is reddish brown; the addition of temper lightens the color several shades. The scrapings from partly finished vessels (see page 54) and the ground-up fragments of pots which have cracked badly in the course of sun-drying are used a second time. This re-used clay, since it already has temper in it, does not need to be mixed over again. It is mingled with newly mixed clay just before kneading, or is kneaded by itself, as occasion demands. The kneading is usually done on the same canvas or skin that was used for the mixing. If a large amount of clay is to be treated at one time, a quantity of water is poured into a hollow formed in the centre of the pile. Later, as the worked clay or paste approaches the proper consistency, water is sprinkled over it with one hand, just as clothes are sprinkled, at first copiously, later more sparingly. At the beginning, the entire mass is kneaded until the water has been thoroughly absorbed. When the paste is wet, it becomes of course considerably darker. It is then divided into masses which can easily be handled, about the size of two large loaves of white bread. The woman works the paste to a uniform consistency in exactly the same way that dough is kneaded (pl. 12, a), and piles the masses, now ready for use in moulding, on a board or canvas, covering then with a piece of cloth to keep them damp until they come under the potter’s hands. The consistency is that of putty, just dry enough to crack if pinched. The mixing and kneading can be completed in half an hour.? At Zuni the ingredients are ground and mixed, and the clay is kneaded on a stone slab. (See pl. 28, facing p. 76.) * Stevenson said, in speaking of Zufii pottery making: ‘“‘This carbonaceous clay is first mixed with water and kneaded as a baker kneads dough until it reaches the proper consistency”’ (1883, p. 329). Mrs. Stevenson de- scribes the preparation of clay at Zuni as follows: ‘‘The clay is ground to a powder and mixed with a small quantity PLATE 10 a. Indian digging material for tempering pottery from an outcrop near the village. b. Guaco, or Rocky Mountain Bee Plant, from the juice of which is made black paint for decorating pottery. | RAW MATERIALS 21 White Clay White clay is used interchangeably with red, but the two are never mixed. It is obtained in the bad-lands to the northeast of San Ildefonso, from the side of an arroyo at some distance from the village. The Indians dig it, bring it home, and prepare it in exactly the same manner as the red clay. The color, when dry, is greyish white; when wet, brownish grey. Temper The Indians of San Ildefonso obtain their tempering material from outcrops along the Santa Fe-Espafiola road, in the vicinity of the landmark known as Camel Rock. Near the crest of the first high hill crossed by the road north of Camel Rock, just west of the road, in the eastern bank of the cut of the old abandoned road, is a small cave made by the digging of this temper (pl. 10, a). There is another outcrop in the ridge of which Camel Rock is a part. This mineral is a very light grey in color. When freshly exposed to the air it is soft and crumbly — fragments as large as the fist can be crushed in the hand — but after being exposed for some time it hardens. When chopped out with an axe or hatchet it takes the form of small fragments and fine powder. There are veins and nodules of a hard yellow rock in the stratum, which are chopped out and thrown away. The source of the temper is at such a distance from the pueblo that trips to it are made only at long intervals when a large quantity is secured in cement-bags, and carried home in a wagon. Two cement-bags may be filled with from fifteen to twenty minutes’ work at the quarry. Some of the Indians, while still at the quarry, pound the temper with an axe or hatchet, or a stone, to break the larger pieces and remove the coarser impurities. Others wait to clean it until reaching the house. In the latter case the temper is spread on a cloth or skin; the skin being preferred as offering a smoother, more resistant surface. It is then broken up by trampling it with moccasined feet. Formerly the Indians ground the temper on their metates. The final step in the preparation is to pass the material through a sieve to remove the smaller impurities such as sand and crushed rock. Before the sieve was known, the Indians spread the temper in a very thin layer on a board or skin, and went over it carefully and pains- takingly with their fingers, feeling for any slight irregularities or rough places. The temper when cleaned is a fine powder, which looks and feels like dry cement. It is stored in old cement-bags ready to be mixed with the clay. The purpose of the addition of tempering material is to counteract the tend- ency of the pure clay to crack during the shrinkage that takes place in sun-drying and in firing. If, however, there is too much temper, the clay becomes “short”’ and loses its adhesiveness. The Indians understand this fully, for if vessels crack badly during sun-drying, they are ground up, and more temper is added to of pulverized pottery, fragments of the latter being carefully hoarded for this purpose. The powder thus com- pounded is mixed with water enough to make a pasty mass, which is kneaded like dough. The more care taken in pulverizing the material and the more time spent in working it, the finer becomes the paste. When the mass reaches such a state of consistency that the fingers can no longer detect the presence of gritty particles, it is still more delicately tested with the tongue, and when found to be satisfactory it is placed in a vessel and covered with a cloth, where it will retain the moisture until wanted for use” (1904, p. 374-5). 22 PUEBLO POTTERY MAKING the paste before it is used again; if, on the other hand, a pot will not retain its shape while being moulded, it is pulled down, more dry clay added to the paste, and the mass rekneaded.! Cooking-Vessel, or Apache, Clay This is very different from the two other kinds of clays used. It is light brown in color, with a large quantity of fine mica flakes in it2; it also has a distinctive odor. When wet it smells cleaner and fresher than the red or white clay, like a newly plowed field after a shower. Some of the San Ildefonso Indians obtain this clay from Las Truchas, a mountain district to the northeast of the village?; others get it from Santa Fe Canyon. It is dug either with the hand or with a small stick, and is brought to the pueblo in the form of small lumps. While still in this condition, it is stored in vessels or bags. The preparation for use is very different from that of the other clays. The lumps are put in a receptacle, such as an enameled washbasin, and sufficient water is added to saturate them. If too much water has been mixed in, the mass is put in the sun to dry out for a while. After the clay has been thoroughly softened by the water, the next step is to remove the pebbles. A small handful is carefully and slowly squeezed and kneaded in the left hand, while the thumb and forefinger of the right are used to pick out the numerous small pebbles as they are encountered. After most of these have been removed, the clay is put on a canvas or skin, and a small part of it at a time is flattened out with the heel of the right hand, pressing away from the body, and against the cloth or skin so as to produce a very thin layer, in which the smaller pebbles are readily felt and from which they can easily be elimin- ated. Finally when this has been done with all the clay, the whole mass is kneaded together, just as the red and white clays are kneaded. When a uniform con- sistency has been attained — that of putty—the mass is ready for use. The re- moval of pebbles and the kneading consume from one-half to three-quarters of an hour. The pebbles which have been removed are placed in a small lard-pail con- taining water, and when the clay adhering to them has dissolved, they are thrown away and the clayey water is used in the process of moulding the paste. ‘Stevenson (1883, p. 329) says: “‘ With this (clay), crushed volcanic lava is sometimes mixed; but the Zufians more frequently pulverize fragments of broken pottery, which have been preserved for this purpose. This seems to prevent explosion, cracking, or fracture by rendering the paste sufficiently porous to allow the heat to pass through without injurious effect.” And again: “The clays used by the Santa Clara Indians are of a brick-red color, con- taining an admixture of very fine sand, which, no doubt, prevents cracking in burning, and hence dispenses with the necessity of using lava or pottery fragments, as is the custom of the Indians of the western pueblos” (1883, p. 331). Binns, in “The Potter’s Craft”, describing the preparation of clay, says, “‘If the clay prove very sandy it must be washed, . . . but all the sand should not be removed. Clay with no sand in it will be apt to crack in drying and burning. Clay with too much sand will be short and brittle in working. If the clay is very smooth and shows no sand, a little fine builder’s sand may be added with advantage, a definite porportion being used and recorded” (1910, p. 40). 2 Stevenson, in his catalogue of Zufii collections, enumerated “ Tierra amarilla, or yellow micaceous clay, of which the Rio Grande Indians make many varieties of vessels” (1883, p. 368). * Harrington, in speaking of a clay-pit near the village of Las Truchas, writes: “It is said that at this place the best red pottery clay known to the Tewa is obtained. It is pebbly, but makes very strong dishes, and it is used especially for ollas. It is said that Tewa of various pueblos visit this place frequently and carry away the clay. The clay deposit is a mile or two southeast of Truchas town” (1916, p. 340). This may be the claypit referred to by the informant, although the clay, while pebbly, is by no means red. RAW MATERIALS 23 The most important difference between this clay and the others is that no temper of any kind is mixed with it; the clay, after being cleaned, is used in the vessels just as it came out of the claypit. The fine mica flakes probably act as temper. SuLIps AND PAINTS Natwe Slip} This is a white, flaky, fairly soft mineral, which is used in solution to give a white outer coating to the bodies of vessels. It is found at some distance from the pueblo, beyond the bad-lands which are visible to the northeast. When the Indians reach the place they pick up small sticks to use as digging tools, but if the deposit happens to be soft enough, the material is merely scooped out with the hand. It is carried home in shawls or bags, and placed in the sun to dry thoroughly; then stored in pottery vessels, usually ollas. It receives no further treatment at this time. When preparing it for use, the Indians simply place it in water as it is, in small lumps. The container is either a small pottery vessel or an enamelled basin. A sufficient amount is mixed with the water to give it the color of milk, but not to thicken it. Occasionally the consistency of thin cream is obtained. Undissolved lumps remain in the solution. Santo Domingo Slip This substance, known to the Indians of San Ildefonso either as “Santo Domin- go white” or “Cochiti white’’, is usually obtained from the Santo Domingo people; it is dug, according to some informants, in the same manner as the native slip. In color and general appearance it is exactly like the latter, but its surface feels more soapy. Santo Domingo slip has largely replaced the native product, because when applied it does not need to be polished with a stone, as does the native slip. It is prepared for use in exactly the same manner as the native slip. Red Slip This is a rather loose red earth, which is dug either with the hands or, if con- ditions demand it, with a small stick. The San Ildefonso Indians obtain it near Santa Fe, but not all of the women know the exact location of the beds. One in- formant said it was found in Santa Fe Canyon, east of the town, a short distance below the Apache clay beds, at a spot where the convicts from the Penitentiary get material for their bricks. There are three different colors of clay at this place, red, yellow, and white. The red is the clay under discussion. ‘The white is used to color the women’s moccasins. 2 1 Stevenson, writing of the Zufi, said of their white slip: ‘‘A paint or solution is then made, either of a fine white calcareous earth, consisting mainly of carbonate of lime, or of a milk-white indurated clay, almost wholly insoluble in acids, and apparently derived from decomposed feldspar with a small proportion of mica”’ (1883, p. 329). Mrs. Stevenson, in a later publication, said: “‘A white clay is dissolved in water and then made into cones which are dried in the sun. When required for use these cones are rubbed to powder on a stone, again mixed with water, and applied in a liquid state to the object” (1904, p. 375). 2 Harrington mentions this bed as “‘a deposit of bright red paint situated about two miles east of Santa Fe, the informants think north of Santa Fe Creek, in high land a few hundred yards from that creek. This paint was used 24 PUEBLO POTTERY MAKING This slip is handled in much the same manner as the other clays. It is brought home in the usual receptacles — either shawls or bags — and placed in the sun to dry thoroughly. It is then stored, usually in ollas or other earthenware vessels, without further treatment. There are two ways of preparing red slip for use, according to the kind of vessel for which it is intended. For polished black ware, it is simply mixed to a thin solution with water. For decorated red ware, the process is slightly complicated. At some previous time, equal parts of temper and native slip have been mixed in water and allowed to dry in cakes. When desired for use on a vessel, the cakes are broken and redissolved in water. A sufficient amount is put in to give the water an opaque, milky- color, but not to thicken it. To this mixture is added a thin solution of the red slip. There is, apparently, no definite rule in regard to the amount of the red solution to be added. The woman simply puts in enough to give to the slip, when applied to a pot, the proper shade of red. In some cases this mixing of the red and white is done once for all at the beginning of the application of the red slip. In other cases the woman has a bowl of each solution beside her, and from time to time, as she works, adds some of the red to the white. In each bowl lumps of the undissolved sub- stances still remain. Occasionally the slip is stirred to the consistency of cream, but nearly always it has that of water. Orange-Red Slip This substance is a yellow clayey earth, in texture somewhat like the two white slips. It occurs in the “Valle” to the west, beyond the first Jemez range, near Ojo Caliente. It is dug with a stick, in the same manner as the native white, and is carried home in shawls and bags. Before being stored it is put out in the sun to dry thoroughly, then placed in ollas and kept until needed. Like the other slips, it is prepared for use by being mixed with water. A saturated solution is made, but the consistency remains that of water. This material, which in solution is a brilliant yellow, is used for two purposes — as a slip to color the bases of bowls and ollas, and as a paint to supply the red elements of polychrome designs. After being fired it assumes an orange-red or burnt-sienna color. ! Black Ware Paint This is a paint used for making matte designs on polished black ware, a new departure in decorative technique first used by Maria and Julian Martinez of San Ildefonso, in June, 1921. The substance is a hard yellow stone, said to occur for body painting. It is said that Jicarilla Apache still go to the deposit to get this paint and sometimes sell it to the Tewa” (1916, p. 354). Stevenson, is speaking of the black ware of Santa Clara and other Rio Grande pueblos, mentions “‘a solution of very fine ochre-colored clay” (1883, p. 331), which was probably this same substance. Mrs. Stevenson also mentions “‘red ochre” (1904, p. 375). 1 Stevenson, writing of the Zufiis in 1881, said: ““The material used to produce the red or brown colors is a yellowish impure clay, colored from oxide of iron; indeed it is mainly clay, but contains some sand and a very small amount of carbonate of lime”; it “is generally found in a hard, stony condition, and is ground in a small stone mortar . . . and mixed with water so as to form a thin solution” (1883, p.330). Mrs. Stevenson added later: “Ferruginous clays which on heating burn to yellow, red, or brown are employed for decorating” (1904, p: 375). RAW MATERIALS 25 in the “Valle’’, west of the Jemez range, near Ojo Caliente, in the same district as the orange-red paint. The first step in preparing the paint for use is to scrape the stone with a knife. The resulting powder is mixed with water, and there is then added about one-fourth as much dissolved “‘guaco”’ (see below) as there is paint. It is said that the purpose of the guaco is to make the paint “‘stick”’ to the polished surface. This paint, when ready for use, is kept in a small earthenware or china dish. The con- sistency of the mixture, like the other paints, is that of water. Black or Guaco Paint This is the only vegetable paint used by the San Ildefonso Indians for the decoration of their pottery. It is obtained from a very common weed, known as the Rocky Mountain Bee Plant, or Guaco,! which grows in the moister flats of this district in great profusion. It flowers late in July and early August, and the seed- pods open toward the first of September. The Indians say it grows at a given place only in alternate years. In favorable spots the plants attain a height of five or six feet (pl. 10, b). The plant is gathered during April and May, when the shoots are only six to ten inches high, and therefore tender. Great quantities of it are carried home in shawls and bags. It is placed with water in Apache-clay cooking-pots, and is boiled over an open fire, never on a stove. As guaco has a bitter taste (“hot like pepper’, the women describe it) when not cooked sufficiently, it is necessary to boil it until this unpleasant flavor has disappeared. Over a hot fire half a day is long enough, but often a whole day is required. Then the liquid is drained into wide-mouthed earthen vessels and placed in the sun to harden into a solid, black, rather sticky, mass. Some women reboil the liquid until it thickens, before placing it inthesun. Metal containers are not used, because they are said to spoil the color. The informants stated that hardened guaco was not eaten. When it has become com- pletely solidified it is set away for future use in painting. It will keep indefinitely. 1 Peritoma serrulatum (Pursh); synonyms: Cleome serrulata, and Cleome integrifolia; (Wooton and Standley, 1915, p. 290). Stevenson wrote: “It is said that among the Cochiti, Santa Clara, and some other pueblos a vege- table matter is employed to produce some of their decorative designs; this, however, I was unable to verify, though some of the Indians assured me of the fact, and furnished me a bunch of the plant, which Dr. Vasey, of the Agri- cultural Department, found to be Cleome integrifolia, a plant common throughout the Western Territories” (1883, p. 331). Again, ‘‘That of the decorated class is ornamented with the juice of Cleome integrifolia, which is fixed to the ware in the process of burning” (loc. cit., p. 430). Harrington writes: ‘‘This is a very important plant to the Tewa, inasmuch as black paint for pottery decoration is made from it. Large quantities of young plants are col- lected, usually in July. The plants are boiled well in water; the woody parts are then removed and the decoction is again allowed to boil until it becomes thick and attains a black color. This thick fluid is poured on a board to dry and soon becomes hardened. It may be kept in hard cakes for an indefinite period. When needed these are soaked in hot water until of the consistency needed for paint. Guaco is also used as a food. The hardened cakes are soaked in hot water, and then fried in grease. The finely ground plants are mixed with water and the liquid is drunk as a remedy for stomach disorders; or sometimes fresh plants wrapped in a cloth are applied to the abdomen” (1916, a, pp. 58, 59). (It should be noted that the accounts cbtained by the writer from the informants of San Ildefonso do not agree in detail with the one given by Harrington.) Mrs. Stevenson wrote of Zuii: “‘ Water from boiled Cleome serrulata (Mexican name waco) is mixed with black pigment (a manganiferous clay containing organic matter) in decorating pottery”’ (1904, p. 375); and in more detail: ‘‘The entire plant, minus the root, is boiled for a considerable time, and the water in which it is cooked is allowed to evaporate. The firm paste secured from pre- cipitation is used in conjunction with a black mineral paint for decorating pottery” (1915, p. 92). 26 PUEBLO POTTERY MAKING The residue in the pot, after the liquid has been poured off consists of tender stems and leaves. This is eaten by the Indians, and is not unlike spinach. The hardened guaco juice is stored at least a year before it is used in painting; the longer it is kept the better black it produces. If it is used during the first year, the resulting color on the vessel is a streaky blue-black. Guaco is prepared for use in painting in the same manner as the other pigments. A chunk of the hardened mass is broken off and dissolved in water. One informant makes a solution which, although black, has the consistency of water. The others use a syrupy solution almost like thin molasses. The paint has a distinctive, not unpleasant, vegetable odor, and is rather sticky. Any small, wide-mouthed Indian bowl, not too shallow, is used as a paint-cup. In this bowl there is always a stirring- stick, usually a splinter from a board. FUEL Manure Both cow-manure and horse-manure are used for fuel in burning pottery, but sheep-dung, when obtainable, is preferred, because is it thought to make a hotter fire. The cow-manure is collected from the corrals, and while still soft is patted into large circular cakes, sixteen to twenty inches in diameter. These, after being hardened in the sun, are stored in a dry room until needed. Such circular cakes, with the hand-prints showing, are usually employed for making the top of the oven. The horse-manure is obtained from the corrals in the early spring, where during the winter it has been trampled down by the horses into a compact layer a foot or more thick. When the corrals are cleaned during April this deposit is cut with an axe into chunks roughly two feet square. After being removed, the squares are split with an axe into slabs several inches thick, which are then stood up against the bases of house or barn walls to dry in the sun, and later stored indoors until needed. Disused bread-ovens sometimes serve as temporary storage places. Further splitting of the slabs may be done at the time of firing. When used in the ovens the slabs are from one to two inches thick. Sometimes the slabs of manure are placed in the sun for a day or two before being burned, but often they are taken directly from the store-room to the fire, where they are supplemented by dried manure collected from the pastures. During the burning of polished black ware (see p. 74) the oven is smothered with loose manure, which is brought in galvanized washtubs directly from the stables and corrals, either at the time of burning, or on the preceding day. ! Kindling For starting the fire in the oven no wood but cedar is ever used. This is cut into pieces from six to eighteen inches long and is split into fine kindling at the time of burning. 1 Stevenson, in 1879, saw the Rio Grande Pueblo potters use “‘coarsely broken dried manure obtained from the corrals”, and added that for the polished black ware “another application of fuel, finely pulverized, is made”’ (1883, p. 331). PLATE 11 Gourd spoons, or kajepes, used to shape and smooth the walls of vessels. a ” PARAPHERNALIA PRIMARY PARAPHERNALIA Earthenware Moulds or ‘* Pukis’’ These moulds are usually the bases of broken bowls or ollas. Occasionally pieces of pottery are made especially for moulds; in such cases, although they are fired, they are neither finished carefully not decorated. When a mould is to be used, a small amount of temper or wood ashes is placed in it, so that the vessel being moulded will not stick to it.} Gourd Moulding Spoons or “‘ Kajepes”’ These spoon-like implements (pl. 11) are made from pieces of gourd-rind, usually from broken rattles or dippers. They vary greatly in size, ranging in diameter from a little over one inch to as much as four, or four and a half, inches. There are also many different shapes: round, several forms of ovals, and a few which have one concave edge. The various shapes are used for the different parts of the vessels. As a general rule the larger kajepes are used on the larger vessels. Each woman has from four to a dozen of these implements, which are distinctly individual, for one potter shows awkwardness in handling the spoons of another. It is said that potsherds were formerly used for the same purpose as these gourd spoons.? Scrapers Two kinds of scrapers are used at the present time. One is the top of a baking- powder can, which is popular because its shape makes it possible to apply it to any part of a vessel. The other scraper is an ordinary kitchen case-knife. The scraping of the vessels is done after they have been dried in the sun. It is said that pot- sherds, with edges sharpened on a piece of sandstone, were formerly used. Polishing Stones Very smooth, fine-grained pebbles of various colors are used to put the final finish on certain kinds of pottery. They vary considerably in size, from three- quarters of an inch long to three, or even three and a half, inches. It is impossible 1 Stevenson, in 1879, observed at Zuni that “the bottoms of old water jars and bowls form stands for the articles while being worked by the potter. The bowls are filled with sand when objects of a globular form are to be made” (1883, p. 329). At Pojuaque (a Tewa pueblo near San Ildefonso, now nearly extinct) he collected two ‘“‘pottery moulds for bottoms of vessels” (loc. cit. p. 439). Mrs. Stevenson also noticed these olla bottoms at Zuni (1904, p. 374). 2 Harrington writes: “‘Variously shaped section of gourd are used by women to smooth and shape pottery in the making” (1916, a, p. 102). Stevenson, in 1879, noted at Zufi “‘a small trowel fashioned from a piece of gourd or fragment of pottery, the only tool employed in the manufacture of pottery”’ (1883, p. 329). Mrs. Stevenson also speaks of these trowels (1904, p. 374). 28 PUEBLO POTTERY MAKING to classify them by shape, except that the larger ones are usually more flat than spherical. Most of the stones appear to be waterworn pebbles, without any acute angles or sharp edges. Usually two surfaces of the stone are highly polished, most frequently at the ends, where they come in contact with the vessel. Some specimens show signs of great wear. Each potter has several polishing stones, the number varying from seven to sixteen; they are distinctly the personal property of the potter, and apparently have a semi-sacred significance. For the most part they are heirlooms, handed down from mother to daughter, but additional stones are picked up from ruins which the potters have visited. One informant has four stones which her mother gave her, and three which she found at the ruined pueblo of Puyé. Another inform- ant uses a stone that belonged to her great-grandmother, although her favorite is a small one which she found herself at a nearby ruin. Stones are sometimes lent by one potter to another, but they very seldom find their way outside the family group.1 Paint Brushes These brushes are narrow slivers of the leaves of yucca or soapweed, from five to six inches long, and from an eighth to a quarter of an inch wide. For a distance Fig. 5. Slivers of yucca leaf with shredded ends, used as paint brushes for decorating pottery. of about an inch from one end, the fibres are chewed and thus separated. Most of the chewed fibres are then cut off, and the number remaining determines the fine- ness of the point (fig. 5). For very thin lines a brush of only one fibre is used. When out of service, the brushes are kept in some receptacle which will protect the shredded ends. When the implement is dry the chewed fibres become stiff and rather brittle, and must be handled with care ; before using they are soaked in water for two or three minutes in order to soften them.2 1 Stevenson, in speaking of the making of pottery at Santa Clara, mentions “‘the process of polishing — with smooth, fine-grained stones”. (1883, p. 331). In his catalogue of stone objects collected at Zufii in 1881, he differentiates between “small stones used in polishing pottery’’, “small stones used in polishing unburned vessels”, and the “small polisher for glazing and smoothing pottery”, giving three different Indian names for the three kinds. He does not, however, explain the difference (1884, pp. 525, 526). He also catalogues “fifteen rubbing or smoothing stones for pottery” obtained at Walpi (1884, p. 587). Mrs. Stevenson remarked: “Polishing stones are used to finish the surface’’ of vessels at Zuni (1904, p. 375). * Stevenson, in 1879 at Zufi, noted that the paint was applied to pottery “with brushes made of the leaves of the yucca. These brushes are made of flat pieces of the leaf, which are stripped off and bruised at one end, and PARAPHERNALIA 29 SECONDARY PARAPHERNALIA Carrying and Storing Receptacles The receptacles used for bringing clays and other ingredients from the pits to the village vary somewhat according to the distance that the material must be carried. If the beds are close at hand, the material is placed in a shawl spread flat on the ground. The shawl is then picked up, the corners are tied, and the bundle is carried on the back. Sometimes gunny-sacks and cement-sacks are used instead. If the beds are at some distance from the pueblo, the material is placed in sacks and brought home in the body of a wagon. As arule the ingredients brought home in shawls are transferred to sacks or boxes for storage. Paints are kept in ollas, with the exception of the guaco paint, which is allowed to remain in the bowl in which it is dried. Mixing Surfaces Whenever ingredients are to be mixed or crushed, the work is done upon some sort of extra surface laid upon the floor. This surface is about a yard square, and may be, apparently, of any suitable material — a bit of old canvas, an opened-out cement-sack, or a small skin such as that of a goat or dog. Similar surfaces also serve for mixing clay and temper, for cleaning temper, for mixing the paste with water and kneading it, and finally for holding the kneaded clay during moulding. Partly finished vessels are placed upon such a surface at various stages of con- struction. For winnowing clay, the women’s shawls are used. Boards No boards are placed beneath the pukis, or moulding trays, while they are being used on the hard floor of the house, but in the courtyard boards are used under them in order that holes may not be worn in the ground during the constant turning necessary in moulding vessels. When small vessels are completed they are placed in rows on a board, where they remain during the early stages of the drying process. Rectangular, flat-bottomed vessels are built directly on boards, or on low footstools made of short boards with legs at each end. Water Containers While the potter is at work, she always has beside her a small lard-pail partly filled with water, which serves to keep the kajepes damp, to moisten parts of the vessel, and from time to time to clean her hands. When the kajepes are not in use, they are usually placed in the pail. At San Ildefonso such a pail is now the only form of water-container; formerly pottery bowls were probably used. are of different sizes adapted to the coarse or fine lines the artist may wish to draw” (1883, p. 330). Mrs. Stevenson wrote, again of Zuni: “Yucca glauca Nutt. Soapweed . . . The brushes employed for decorating pottery are made from the leaves of this plant, which, for this purpose, are cut the proper lengths and fringed at one end’’ (1915, p. 82). 30 PUEBLO POTTERY MAKING Mops for Slips These mops are the same for all slips. Each consists of a rag, folded and refolded until it is about an inch or an inch and a half wide and from two to two and a half inches long. One end of the, rag or mop is held between the thumb and the first two fingers of either hand; the other end serves as a wide paint brush. The potters state that in former times a piece of leather or skin served the same purpose as the cloth mop.! Paint Receptacles Various receptacles hold the slips and paints that are ready for use. The white slips are usually mixed and kept in enamelled basins and pans, because a large quantity is prepared at one time. The red and orange-red slips may be in small pottery bowls, or in china sauce-dishes. The guaco is invariably in an Indian bowl. Undoubtedly at one time native bowls were used exclusively, and there may even have been bowls of special shapes or designs for this purpose; at present, however, no trace of such a custom remains. Wiping Rags Wiping rags or, more simply, the aprons of the potters are used at various stages of the work — after scraping, after polishing, after the slip has dried, and after burning. Apparently any convenient piece of cloth is satisfactory. Accessories in Firing When the vessels are to be fired, various accessories must be at hand. Four or more half-bricks or stones are needed upon which to set the grate. The latter may be either a discarded stove-grate, or a collection of strips of iron, metal barrel- hoops, and odds and ends, placed together to form a grill.2 Small stones and tin cans — such as small condensed milk cans and meat cans — are needed as props to keep the fuel from touching the vessels during the burning. Flat pieces of tin and the covers of large lard-pails serve at times to close spaces between the fuel cakes, and to cover the oven-top, to support which metal rods are often used. Lastly, pokers are needed to handle the fuel and to remove the hot vessels. These may be wooden or iron rods, broomsticks, old shovels, or even pitchforks. Each potter has her own collection of the above materials and implements, stored away ready for use. These collections of apparent refuse vary to a surprising extent. * Mrs. Stevenson says the Zufiis used a “rabbit skin mop” (1904, p. 375). > Mrs. Stevenson wrote of Zufii: “The pieces to be fired are placed upon stones to raise them a few inches from the ground”, implying the absence of a grate (1904, p. 376). MOULDING For the purpose of this report the vessels may be divided into four large groups: bowls, ollas, cooking vessels, and unusual shapes. With respect to size there are two classes of bowls: those less than four inches in diameter, and those larger than that size. In shape bowls may be either wide-mouthed (pl. 6, b, g) or constricted-mouthed (pl. 6, a, ce). The ollas all have full, globular bodies and relatively small orifices with or without flaring lips (pls. 7, 15, a). As a rule, the cooking vessels are shaped like small ollas. Under unusual shapes fall all the types and forms which are not of the first three classes, such as terraced (prayer- meal) bowls, double-mouthed vessels, double bowls or “‘baskets’’, and vessels with handles. The moulding of each of the above forms may be said to consist of four principal steps: the making of the base, the building of the walls, the shaping, and the finish- ing. Very briefly, the process is as follows: The potter first forms a pancake-shaped pat of paste from six to eight inches in diameter; this she presses into the mould, or puki, to form a base. Then the walls of the vessel are built up by the addition of successive ropes, or rolls, of paste laid one upon another. The small bowls are the only exception, for they are formed in the hands of the potter from a single lump. In some cases the building is done all at one time; in others, and always with the larger vessels, a few rolls are added, then the piece is set aside to dry a little before the addition of a few more rolls. The potter usually builds two or more vessels at once in order to permit work upon one while the other is undergoing a brief period of drying. The preliminary shaping of the vessel is done either in the course of the building or after the building has been completed. The obliteration of the junctions between the rolls and of finger-marks is accomplished with the kajepe, or gourd-spoon, and further use of this implement aids in giving the vessel its shape. The final step, the finishing, consists of going over the entire vessel carefully, first with the kajepe, then with the fingers, to remove slight irregularities to even the lip and rim. The finishing is a slow, exacting process, and the difference between the artist and the mere pot-maker comes out at this stage of the work. The moulding, although usually done in the house, may also take place in some shady spot outdoors. If a woman begins her moulding in the morning, she will commonly devote the entire day to it. By evening she will have completed from five to thirty vessels, the number depending partly upon the size of the pieces and partly upon the rapidity with which she works. The potter sits upon her heels on some kind of mat; it may be a sheepskin with the wool side up, a piece of canvas, or a small woven rug. Her attitude is changed only when stiffness requires it. Thereupon she sits with her feet out in front of her; or with one leg bent, the foot flat on the ground, the knee beside her shoulder, and with the other leg under her or fully flexed in front with both the 32 PUEBLO POTTERY MAKING knee and foot upon the floor. Toward the end of the day the potter usually sits against a wall to rest her back, for any one of the postures assumed is tiring. At the end of the day the women frequently complain of stiff backs and sore abdominal muscles, caused by the almost constant stooping posture. Some potters cover their laps with shawls, others wear aprons, and still others use no protection whatever for their clothing. When the potter is sitting upon her heels, the mould, or puki, is laid directly in front of her upon the floor. If she is sitting with her legs extended, it is either held in the lap or placed close to her right side. In the house the puki rests directly upon the hard earthen floor; outdoors, a short board is placed under it to prevent its constant turning from wearing a hole in the relatively softer ground. In the puki is sprinkled a thin layer of temper or wood-ashes to prevent the vessel from sticking to it. At the right of the potter, within arm’s reach, on a canvas or a piece of cloth, is a mass of prepared clay. Rarely this reserve paste is on the left. If the paste is in constant use, it is not covered unless exposed to the sun; when, however, the moulding is abandoned for even a few minutes, a corner of the canvas or cloth is thrown over it. A small lard-pail partly filled with water is an indispensable accessory during moulding. This is usually kept between the potter and the paste; occasionally it is on the left, sometimes near the puki beside the potter’s right knee. The gourd moulding spoons, or kajepes, are also placed within easy reach, on the floor near the puki, beside the waterpail, or in the pail itself. The potter is then ready to begin moulding. The first step is to ascertain by a little handling whether the paste is of the proper consistency. If it was kneaded the day before, it may prove to be too dry; in such a case the hands are well moistened and perhaps a little water is sprinkled on the paste; it is then rekneaded for a few minutes. Then a handful is scooped out of the mass with the right hand. If the first handful is not sufficient, a second scoop gives the required amount. It is next worked with the hands for half a minute to five minutes; if it is of just the right consistency, it is hardly worked at all; if it is too dry, the hands are occasionally dipped in water while it is being worked; if it is too wet, kneading continues until it is sufficiently dry. There are three distinct movements in this final working of the paste. First, the handful is pinched and squeezed by opening and closing the hands; if any gritty particle is encountered, it is picked out with the thumb and forefinger of the right hand and snapped upon the floor. The second movement consists in rolling the paste between the two flattened hands. When the roll is about six inches long, it is doubled and rerolled. This may be repeated from two to half-a-dozen times. Occasionally this step is entirely omitted, especially when a pat is being made. In the third movement the paste, now a spherical lump, is slapped back and forth between the cupped hands, which are held from six to eight inches paart. Sometimes this third movement precedes the second. The handful of paste is now ready to be made into a pat. There are two ways of forming a pat. In the first one, the spherical lump is held on the open left hand and pounded flat with the right fist; from time to time it is turned a few degrees by a slight tossing motion. It is then finished by patting PLATE 12 b a. Kneading clay preparatory to modeling a vessel. b. Bowl-moulding, primary stages. 1, Base formed in mould, edge crimped to receive first roll (cf. pl. 18, a); 2, Walls built to full height; 3, The same piece after shaping and smoothing. Tay ey rome heey ay ie Tht E> ~ Sa titans adel «eee we *[PSSAA BY} JO LOII9JUI Ot} WO [[OI ‘purty 7Yys14 oy} Jo siasug vy} Aq tuts oy} Jo opts ‘]JOl Mou B Suryeut st Ja}j30d oy} -Ul oy} ur soR]d OyUI peyourd pue pous}}eH st puev ‘puey ye] oy} JO S][OI MO} YOIYA 0} VsVq-[Moq VW UI PpPYy SI [[OI IY, “eseq oy} 07 AvIO Jo [[OI ys1g oy} ZurA;ddy q 24} Jo suorjount 94} 230N ‘peppe useq savy Aro SI, aLV Id MOULDING 33 it with the flat right hand until it is fairly smooth and of uniform thickness; in doing this the pat is turned by slapping it from the left hand to the right and back again. During this interchange, through the natural placing of the hands, the pat is turned through an angle of ninety to one hundred and twenty degrees. When the pat has been completely formed by this method, it is like a large pancake, six to eight inches in diameter and from three-eighths to half an inch thick. It is then pressed firmly into the puki, and the edge is turned up and crimped with the thumb and first two fingers of each hand to form a slight rim (pl. 12, b, 1). In the second method, the spherical lump of paste is first pounded with the heel and then with the upper knuckles of the right hand; it is turned meanwhile by the tossing motion of the left hand. The next movement is the same as in the corresponding stage of the first method, namely, patting the paste with the fiat right hand while turning it by transferring it to the right hand and back. Finally, before the pat is put into the puki, the edge is bent up and smoothed off a little, so that a shallow flat circular tray is formed instead of the slab obtained by the first method. This tray is then placed in the puki, where it is pressed down very firmly with either the heel of the hand or the balls of the fingers, in order to insure a solid uniform base and to expel any air-bubbles in the paste. Another handful of clay is now scooped out of the mass on the canvas to the right and worked to the proper consistency as before. From the resulting spherical lump the potter very skillfully forms a roll of uniform diameter by a backward and forward motion of her two hands placed palms together (pl. 13, b).1. There seems to be a tendency for the first part of the roll to be of slightly smaller diameter than the last part; if this occurs, the roll is reversed and partially rerolled. One end is then taken in the right hand, while the left hand holds it near the other at a point chosen to prevent too much sagging at the middle. The potter then places the end which is in her right hand against the inside of that part of the edge of the pat nearest her.?. The roll is pressed against the edge just enough to hold it in place (see pl. 13, a). The thumb is on the exterior, the fingers on the interior of the edge. Usually only the first two fingers are used, although the third finger is occasionally brought into contact with the paste. Then, as the puki is revolved counterclockwise,*? the rest of the roll is pressed against the edge of the pat. If the roll is not long enough completely to encircle the pat, another is made and placed on it in a similar manner. When the edge has thus been completely encircled, the unused remainder of the roll is pinched off and tossed back on the mass of paste on the canvas. The potter then pinches the roll more firmly to the edge of the pat. This is done with both hands. The thumbs, almost touching, are on the exterior, the fingers on the interior of the vessel. The puki is usually moved counterclockwise, although the same 1T use the words “‘very skillfully” advisedly. Repeated attempts on my part to imitate the process resulted in rolls of exceedingly variable diameter. At Zuifii the roll is made by the apparently simpler and more efficient method of rolling the clay back and forth on a flat stone slab with one hand (see pl. 29, a). 2 Zufii potters apply the roll to the outside instead of the inside of the growing vessel wall; otherwise the hand- ling of the roll is exactly as at San Ildefonso (see pl. 29, b). 3 Throughout this report, the puki is spoken of as moving “clockwise”’ or “‘counterclockwise”’ and the sectors worked in are referred to the numerals on the face of the clock, as, “the six-to-eight-o’clock sector’. The point of view taken is that of the potter with “six o'clock” referring to that part of the bowl nearest her. 34 PUEBLO POTTERY MAKING potter will sometimes revolve it clockwise. During this process of pinching, the roll is flattened until it assumes in cross-section the shape of a very much elongated ellipse (fig. 6, b). An attempt is made to keep the thickness of the side as nearly uniform as possible, and in order to accomplish this it is often necessary for the hands to be moved back over a part already flattened. The diameter of the rolls, except for cooking-pots, varies from half an inch to slightly over an inch, according to the size of the vessel being built, and the in- dividual doing the building. When a roll is pressed against the interior of the rim of the growing vessel,! from a half to three-quarters of it lies below the level of the rim (see fig. 6, a). Then, when the roll is flattened, the junction-plane between it and the preceding roll will not be horizontal, but will slope downward sharply a c b d Fic. 6. Diagramatic sections of a bowl on the mould. a. Base made and first roll applied to inner side of rim. ce. Second roll applied. b. First roll flattened and welded on. d. Second roll flattened and welded on. from the exterior (see fig. 6, b, d), thus producing a broad holding surface and minimizing the risk of the vessel’s cracking along the junction-plane. In other words, the junction-line between any two rolls on the outside wall of the vessel is considerably higher than the corresponding line on the inside. The flattened rolls, in all but cooking-pots, are from an inch and a half to two inches wide, but because of the overlapping just described the distance between the junction-lines is con- siderably less (see pl. 13, b, and pl. 15, a). During the process of flattening the roll, some potters obliterate the junction- line on the exterior by rubbing it with the first and second finger of the right hand, and by the addition of small pellets of paste in the more conspicuous indentations. Others consider it unnecessary to obliterate this line during the building of the 1 The “rim” of an unfinished vessel means the upper edge of the last roll added to it. MOULDING 35 vessel, in spite of the fact that the roll may break away because of not being firmly welded. Certain women smooth the temporary rim after flattening each roll, others do not. When the flattening has been finished, the puki has made a second complete revolution, and the junction of the two ends of the roll is again directly in front of the potter; but if a few additional touches are required she may again shift the puki in one direction or another. No potter pays any attention whatever to the location of the junction points of the ends of the rolls; in successive rolls, therefore, they may lie directly above one another, or they may be distributed about the circumference of the vessel (pl. 13, b). When one roll has been completely welded on, flattened out, and incorporated into the vessel, another roll is formed, and is applied in exactly the same manner. Thus the building proceeds to the height at which the shaping is begun. The steps so far enumerated are the same for both bowls and ollas. The further treatment of the vessel varies slightly, according to the shape desired. Stevenson, describing the moulding of vessels at Zufii, in 1879, wrote: “‘When the clayey dough is ready to be used, a sufficient quantity is rolled into a ball. The dough, if worked by a careful artist, is first tested as to its fitness for molding by putting a piece of the paste to the tongue, the sensitiveness of which is such as to detect any gritty substance or particles, when the fingers fail to do so. The ball is hollowed out with the fingers into the shape of a bow] (see pl. 29, a), this form constituting the foundation for all varieties of earthenware, and assumes the desired form by the addition of strips of clay; all traces of the addition of each strip are re- moved before another is added,! by the use of a small trowel fashioned from a piece of gourd or fragment of pottery, the only tool employed in the manufacture of pottery. The bottoms of old water jars and bowls form stands for the articles while being worked by the potter” (see pl. 29).? Mrs. Stevenson, writing later, also of the Zunis, said: “In beginning the work a sufficient quantity is first made into a ball and then hollowed out with the fingers until is assumes a conventional bowl shape, which serves as the foundation to be afterward built up and elaborated into any desired shape. The vessel is then formed by the successive additions of strips of the paste long enough to encircle the bowl, each layer being pressed on the brim with the fingers and accurately fitted, the trowel being then skillfully used to finish the joining and to remove all traces of the original separation of the strips. Most of the work of remodelling the vessel into its final shape is done on the inside with a trowel, this implement being used on the outside chiefly to smooth the surface. The clay, if it has been properly worked, possesses sufficient tenacity and plasticity to admit of being pressed and scraped without cracking.” The following quotation is of interest as showing how closely modern studio- practice, undoubtedly evolved experimentally, resembles Pueblo Indian methods: “The clay for building should be rather soft as it is apt to dry quickly on handling. A plaster bat (mould) should be made. It is first necessary to roll out the clay into 1 See, however, pl. 29. b; the Zufii potter in this case has not obliterated the preceding rolls. 2 Stevenson, 1883, p. 331. 3M. C. Stevenson, 1904, p. 375. 36 PUEBLO POTTERY MAKING cords which should be a little thicker than the proposed walls are to be. These cords should be as uniform as possible and should be rolled quickly to avoid undue hardening. It is best to roll them as required. A roll of clay is taken, one end laid in the center of the bat and the rest is coiled around it in a spiral line. When the disc so formed has reached the proper size, the coils are gently rubbed over with the fingers until they have thoroughly united and the lines of the spiral have disappeared. The clay disc may now be turned over and the rubbing continued on the other side. The circle is cut true and a new coil is laid on the outer edge, thus making a shallow circular tray. In raising the walls it is best to pinch off the roll of clay when one circle has been completed, and the new roll should be begun at another point so that all the joints will not be at the same place. This plan is better than coiling a long roll in a spiral, for in this case one side of the piece will be higher than the other. “After three rolls have been laid in position, the wall, both inside and out, should be worked like the bottom so that the rolls will disappear and the clay be welded uniformly together. This should be done without water or with as little as possible. The use of water is very tempting. It makes the clay so smooth and seems to help, but it will inevitably make the work sloppy and will tend to soften the walls. “After three or four rolls have been worked in, the piece should be laid aside for some hours to stiffen. If this be not done the weight of the second building will cause the work to sag and fall out of shape. For this reason it is well to have two or three pieces in hand at once so that there need be no waiting. When the cylinder is of sufficient height it should be allowed to become quite stiff and then the irregularities should be corrected with a little soft clay which is worked into the joints. The whole surface may now be gone over with tools and brought to the required finish.”’! Before describing in detail the moulding of the various sorts of vessels, the accidents which are associated with this process should be discussed. These may result from one of two causes, the presence of foreign matter in the paste or imperfect moulding. If the clay has been carefully sifted, as it usually is, there should be very little foreign matter in the paste. It is, however, impossible to remove entirely all gravel or stones fragment. If gravel is allowed to remain, it will cause the vessel-walls to scale during firing because of the difference in the rates of expansion under heat of stone and paste. In order to prevent this, the potter while moulding is con- stantly on the lookout for these small particles, which may be discovered at any stage of the work. They are at once picked out of the vessel, even if it is all but finished. The irregular hollow formed is then filled with a small pellet of fresh paste and smoothed over. The women say that a bit of hard clay does not cause flaking as does a piece of gravel or a stone splinter. Another kind of foreign matter is an air-bubble, which if left in the vessel will cause the same form of accident, because of the difference in the rates of expansion of air and clay. In order to eliminate these small air-bubbles, the pat is pressed down hard upon the puki 1 Binns, 1910, pp. 69-71. ‘prvaut yt sassaid Apua8 pur jem oy} Jo doy oy} [Te orseyd ogy qzoddns 07 puv Surusny soord ay} daax 04 SUI} ‘puvy ZYSIA oy} Ut prey ‘odoley oy} apy “UIYQIA [TBA Oyy SdAdos puvy yo] oy, ‘woods panos Jo ‘odafey oy} YyyIM podeios sjioddns puvy jJe] 91} ‘jessaa v surdeys ut odolfey ot} Jo asy—) U9Eq SBY HI J9}Je [MO VB JO UII oY} SuIyJOOUs pue Suypoaory q e PL ALVId MOULDING 37 and the rolls are carefully pinched at every point about the vessel. A_ skillful potter is able to feel an air-bubble even if it is covered with a layer of clay: such a bubble is pricked and the resulting hollow is filled as before. If the moulding is imperfect, that is, if the rolls are not carefully welded, a weak spot occurs at the junction, which probably contains a thin layer of air. When the vessel is fired, it cracks along this line and is ruined. Such accidents seem to occur most commonly at the bases of large vessels, either because the first roll was not sufficiently welded to the base, or because the pat itself was not pressed into the puki with sufficient force. Since flaws between the rolls cannot be dis- covered until the firing, they cannot be corrected as in the case of foreign bodies in the clay. Bowls From two to eight rolls may be used to form a bowl, according to its destined size and shape. When the building has been completed, the piece is in the form of a cylinder, with sides either vertical or very slightly flaring (pl. 12, b, 2, and pl. 13, b). As a rule the fingerprints and the irregular horizontal junction-lines may be seen both on the interior and exterior. The next step is the finishing of the temporary rim. This is done with the right hand, the fingers of which assume much the same position that they would for holding a pencil (pl. 14, a). The thumb is on the interior of the rim, the forefinger on the top, and the middle finger on the outer edge. The thumb and middle finger are used as guides to help keep the rim uniform in thick- ness. The forefinger removes the paste from the higher parts of the rim and trans- fers it to the hollows. The fingers do not move with respect to each other except to exert slight pressure. The play of the right hand during this process is a gliding backward-forward motion repeated many times, while at the same time the puki is usually kept revolving counterclockwise by the left hand, which also is generally but not always, used to steady the side of the vessel. Occasionally the same potter will turn the puki clockwise. In the former case the right hand is kept in the twelve-to-two-o’clock sector; in the latter in the six-to-eight-o’clock sector. If the rim is smoothed hastily, as it sometimes is at this stage, the puki may not be turned at all. This completes the building of the bowl, which is then set aside for a few minutes, while another is begun. The next step is the shaping. This is done with a kajepe, or gourd spoon. The kajepe should always be damp when used, and for that reason is often kept in the water-pail. It is somewhat difficult to describe in detail the use of the kajepe, for no two potters work with it in exactly the same way. Often the same potter will show variations in her method of handling the tool. Each woman has from four to a dozen kajepes beside her while she is moulding. These implements vary much both in size and shape (pl. 11). Most of them are circular or elliptical with all edges convex, although every potter has at least one with a concave edge. Generally the smaller, circular kajepes are used on the interior of bowls, the oval ones on the exterior, and the one with a concave edge on the exterior at the shoulder, where it would be difficult to use the other types. As a rule the larger kajepes serve for the larger vessels. A potter occasionally changes 38 PUEBLO POTTERY MAKING kajepes in the midst of her work, usually because of the edge, which may be rougher on one than on another. The kajepes are held at an angle of from thirty to sixty degrees to the tangent of the bowl at the point of contact, according to the curva- ture of the part of the vessel being worked upon. The kajepe is always used first on the inside. This is done in order to press out the sides and to give the bowl something of its final shape before the paste becomes too dry. The work begins at the bottom of the vessel and slowly advances toward the top; the bowl gradually assumes a spherical shape, the sides being forced farthest out about half way between the base and the rim. During this process the outside surface, since it is being expanded, begins to show innumerable small cracks. The strokes of the kajepe on the interior are short and always nearly horizontal, the implement being pulled towards the body. During this first use of the kajepe all traces of the junction-lines between the rolls are removed from the inside of the vessel. The tool is always held in the right hand, and the left hand, which is constantly used on the exterior as a brace and stop, is placed directly opposite the spot on the inside which is being worked. One woman scrapes in the seven-to-ten-o’clock sector, turning the bowl clockwise; that is, working from the scraped to the unscraped surface. The vessel is turned through about sixty degrees at each change of position, and about a third of the surface just scraped is gone over again by the strokes on the new sector. Another works in the nine-to-twelve- o'clock sector, turning the bowl counterclockwise, that is, working from unscraped to scraped surface; in doing this she turns the puki five or six times through an angle of between sixty and eighty degrees for each turn, before the entire interior has been gone over. The kajepe is then applied to the exterior of the bowl (pl. 14, b). The concave surface of the kajepe is preferred for the first of the exterior scraping, although the convex surface is not infrequently used. The strokes begin again at the base. At first, when the kajepe comes in contact with the puki, the strokes are very nearly vertical. A little higher on the bowl they become diagonal. Near the rim the strokes are almost horizontal, but still have a perceptible downward slant. The kajepe is always pulled toward the body. The stroke on the exterior is from four to five inches, generally a little longer than that on the interior. During this step one woman turns the puki counterclockwise, working in the two-to-four-o’clock sector; another turns it in the same direction, but works in the four-to-six-o’clock sector. In both cases the strokes are from the scraped to the unscraped surface. Although the larger portion of the actual shaping of the bowl is done from the interior, the drawing in of the upper part to form a constricted mouth is done with the kajepe on the exterior, when the step last described is nearing completion. As when working on the interior, the left hand again acts as a brace and a stop, but this time on the inside of the bowl! Usually only the ends of the fingers rest against the side. Upon the completion of the use of the kajepe on the outside for the first time, all traces of the coil-marks and of the fine cracks developed during the interior scraping are removed, but the surface is still rather rough (pl. 14, b; also 12, b, 3). After both surfaces have been gone over for the first time with the kajepe, the rim is once more 1 The process is identical at Zufii, see pl. 30, a. MOULDING 39 trued up in the manner already described. Then, depending upon the stiffness of the paste, the piece may be set aside to harden a little or the work may continue without interruption. The women hold the kajepe with fingers either slightly bent, or nearly fully flexed; in the latter position the tool is grasped between the thumb and bent fore- finger. Just before using, the kajepe is dipped in water; and the edge is then drawn across the palm of the left hand to remove excess water before it is applied to the bowl. After perhaps a dozen strokes, the paste which has collected on the tool is removed by a dexterous motion: the inner side of the thumb of the left hand is run along the edge of the kajepe to collect the paste; then the inner side of the fore- finger of the same hand is run from the base to the tip of the thumb. This brings the paste to the ends of the two fingers in the form of a pellet, which is thrown upon the mass on the canvas. Since the paste has a tendency to stick to the fingers, the potter must throw it with a jerk or snap. When the kajepe has been used once over the entire surface, it is usually re- versed so as to present its convex side to the bowl, made a little damper than for the previous scraping, and the whole process repeated in detail for both the interior and exterior. This results in better symmetry and a smoother surface. The rim is again finished in the manner already described. The walls of the bowl have by this time been thinned to about one-half or two-thirds of their original thickness, all major irregularities and rough spots have been removed, the vessel is fully shaped, and only the finishing touches are needed before it is ready to be sun-dried. The paste now has the consistency of soft thick leather. The first step in the finishing sometimes consists in again going over both sur- faces with a wet kajepe, to smooth them still more. Occasionally only the exterior is so treated. Then the bowl is turned repeatedly, while the potter touches small areas with the convex surface of the kajepe. At this point particular attention is given to the bottom of the interior; it may be retouched with the kajepe, or simply smoothed over with the ball of the thumb or forefinger. If the surface seems slightly uneven, small pellets of paste are rubbed into the bottom and then levelled down with the kajepe. The bowl on the puki is then placed upon the palm of the left hand, held at eye level, and revolved slowly, while the potter examines it for rough spots and slight irregularities of contour, which when found are smoothed over with the forefinger of the right hand. After being replaced upon the floor, the bowl may be gently pressed between the hands in order slightly to improve its symmetry. Finally the rim is smoothed for the last time, little pellets of paste being added, if necessary, to fill in shallow depressions, and great care is taken to make it as regular and smooth as possible. It is obviously impossible to describe in detail the exact procedure followed in this finishing process, for the method adopted is chosen according to the needs of the individual vessel. After all this is done, the piece is ready to be sun-dried. Its present appearance is very different from that which it had when the building was completed (compare pl. 12, b, 2, and b, 3). The moulding of bowls less than four inches in diameter is a very simple matter compared with that of the larger ones, for there is no use of puki, rolls, or kajepe. After working the paste in the hands the resulting lump is formed into a flat spheroid. 40 PUEBLO POTTERY MAKING The forefinger of the right hand is inserted in the centre of this, the clay held horizontally and slowly revolved by a slight tossing rotary motion of the left hand. The forefinger of the right hand enlarges the hole and gradually shapes the mass into the desired form, thinning the sides at the same time. If the resulting bowl is too high, the rim is pinched off with the thumb and fore-finger of the right hand. When the proper shape and thickness have been attained, the little bowl is held up- right in the left hand, while the fingers of the right smooth the sides and the rim. When completed it is set on a board to dry. Sometimes one of the larger of these bowls is placed in a small puki and reshaped with the kajepe. One woman used the kajepe on the interior of the vessel while it rested upon her left hand. The bowl, when treated in this way, and finished in the same manner as the larger bowls, was noticeably a better piece of moulding than the average small piece. The time consumed in moulding bowls is variable, depending on the dexterity and speed of the potter and to a somewhat lesser degree upon the sort of vessel being moulded. Comparisons between potters are apt to be misleading, for no two make bowls of exactly the same size or exercise the same amount of care in finishing, which, from the point of view of time consumed, is the most variable phase of the moulding. One potter moulded a wide-mouthed bowl of four rolls in twenty min- utes; another finished two spherical bowls of six rolls each in forty-eight minutes; a third potter, the swiftest of the three, finished a wide-mouthed bowl of two rolls after it had been under her hands just fourteen and one-half minutes. The first potter moulded six of the small bowls (less than four inches in diameter) in fifty-five minutes, averaging nine minutes to each, but to refinish one of them with a kajepe she took thirteen minutes. The third potter moulded one of the small type of bowls in four minutes. In considering in detail the time consumed in moulding, the work of Maria Martinez was studied. She is the swiftest and most dexterous potter of San IIlde- fonso, and moulds in a quarter to a third less time than the slowest of the others. In three hours she turned out ten bowls, averaging about seven inches in diameter, of the constricted-mouthed and similar types; this is an average of one in eighteen minutes. She was working constantly, first on one, then on another. Subsequently she moulded six two-roll constricted-mouthed bowls in one hour and twenty- six minutes, an average of fourteen and a third minutes each. The various steps in the moulding of two bowls are recorded in Table I, which gives the actual time con- sumed in minutes and seconds from the beginning of the first of the pair until the two were finished and set aside. In Table II the growth and treatment of a single bowl are given in more detail, with the time in minutes and seconds that it was under the hands of the potter. This piece was one of five constricted-mouthed bowls of three rolls each which were moulded in sixty-four minutes, an average of twelve minutes, forty-eight seconds for each vessel. MOULDING TABLE I Bowl A, constricted-mouthed bowl, diam. 8 in.; Bowl B, wide-mouthed bowl, diam. 7 in. Min. Sec. 0.00 Bowl A — clay picked up from pile 2.00 — pat in puki and pinched up 4.30 3.00 ae — first roll on and pinched flat 4.00 ** “second roll on and pinched flat 4.30 ** ** rim smoothed and bowl set aside (no pause) 4.30 Bowl B — clay picked up from pile 5.30 — pat in puki and pinched up 6220. 7 a — first roll on and pinched flat 7.10 ** “second roll on and pinched flat 7.20 ““ **__ rim smoothed and bowl set aside (pause of 40 seconds) 8.00 Bowl A— picked up again | 8.30 ** __ interior scraping stopped 9.15 ‘“* ** __ exterior scraping stopped 9.45 ““ “* __ first rim smoothing stopped 11.00 ““ “__ first interior smoothing stopped 8.00 Pie3o “ “* __ first exterior smoothing stopped 12.45 ** **__ second rim smoothing stopped 13.45 ** ** __ second interior smoothing stopped 14.30 ** **__ second exterior smoothing stopped 15.15 “ “__ third rim smoothing stopped 16.00 ** “ __ finishing touches stopped; bowl completed (pause of 15 seconds) 16.15 Bowl B — picked up again | 16.45 — interior scraping stopped ; 17.00 ** “__ exterior scraping stopped 18.00 “* ** __ first rim smoothing stopped 18.30 ** “* __ first interior smoothing stopped 5.05 19.00 *“ **__ second rim smoothing stopped 19.45 ** ** __ second interior smoothing stopped 20.45 * **__ touching up stopped 21.00 “third rim smoothing stopped 21.15 ““ “third interior smoothing stopped 21.20 “bowl completed Total, Bowl A — 12 minutes, 30 seconds Total, Bowl B— 7 minutes, 55 seconds 42 PUEBLO POTTERY MAKING TABLE II Small, constricted-mouthed bowl Min. Sec. 00.00 — clay picked up from pile 00.15 — pat put in puki 01.00 — clay for first roll picked up 01.15 — one end of first roll pinched on pat 01.50 — first roll flattened, and clay for second roll picked up 02.10 — one end of second roll pinched on pat 02.40 — second roll flattened, and clay for third roll picked up 02.50 — one end of third roll pinched on pat 03.30 — third roll flattened, and rim smoothing begun 03.50 — bow] set aside (14 minutes, 10 seconds, elapsed) 03.50 — interior kajepe-scraping begun 04.25 — exterior kajepe-scraping begun 04.55 — rim smoothing begun 05 .20 — bow] set aside (18 minutes, 30 seconds, elapsed) 05.20 — interior kajepe-smoothing begun 06.00 — small roll placed around edge of interior base and patted down 06.40 — interior kajepe-smoothing begun 06.55 — exterior kajepe-smoothing begun, lip turned in 07.45 — rim smoothing begun 08 .50 — exterior kajepe-smoothing begun 09.25 — interior kajepe-smoothing begun 10.05 — rim smoothing begun 10.50 — bowl held at eye level, exterior kajepe-smoothing begun 11.17 — bowl placed on floor, interior kajepe-smoothing begun 11.45 — moulding completed, bow] set aside OLLAS In the moulding of ollas the first step is the building of the lower part of the body to a height of four or five rings in the same manner as in bowl-construction. Since ollas have a larger diameter than bowls, more than one roll is needed to form a complete ring about the growing edge. The number of rolls per ring varies from one and a half to four, depending upon the size of the olla and the part worked upon. When this first building has been completed (pl. 15, a), the rim is smoothed some- what and the scraping and shaping are at once begun. The use of the kajepe in the shaping of ollas is identical in all details with that described above in discussing the moulding of bowls. The roll-junctions and the fingerprints are entirely removed and the sides of the vessel are flared a little. Great care is taken not to flare the sides too much, for the paste at this stage is still rather soft, and if the sides are flared unduly they collapse outward of their own weight. When the preliminary shaping has been finished the rim is smoothed a PLATE 15 SUCCESSIVE STAGES IN THE MOULDING OF AN OLLA a. Lower wall built up of rings of clay. b. Sides smoothed and flared by use of the kajepe. ec. Sides further flared and more carefully smoothed. d. Shoulder partly formed. e. Shoulder finished. f. Neck built. g, h. Neck flared and final smoothing completed; the vessels have been shifted inthe moulds to allow work on lower sides. i ' “ Smit = ‘ > . f < os , . ‘ MOULDING 43 little, and the olla is placed in the sun to stiffen. The moulding has now reached the second stage (pl. 15, b). The vessel remains in the sun from twenty to thirty minutes. This period may be extended to as much as an hour and a half, if the vessel is in the shade or if other things occupy the potter’s time. During all the drying periods, at intervals varying from five to fifteen minutes, the potter dips her right hand in the water of the lard- pail, and moistens the rim of the partly finished olla in order to keep it soft enough to permit perfect welding when additional rolls are added. While one vessel is drying, the potter is usually occupied with another. In case the work on the latter is finished before the former is dry enough, the potter simply waits, or finds some other work with which to occupy herself until it is ready. The test of the condition of the olla after this short drying is to pat the side gently with the balls of the fingers. The clay is now very much like soft leather. The degree of resistance offered by the side indicates the condition of the paste. Of course the value of such a test depends entirely upon the knowledge and sense of touch possessed by the potter, two qualities which can be gained only through long experience. When the paste in the olla, which now has the shape of an open-mouthed bowl, has reached the proper degree of firmness, the vessel is brought in and the shaping continued. By using the kajepe first on the interior and then on the exterior, the sides are flared still more until the desired shape for the lower part of the olla has been obtained. Then, after a hasty smoothing of the rim, the vessel, now in the third stage (pl. 15,c), is again set aside to dry. When it has become firm enough to support the weight of the new rolls to be added, the building is con- tinued. The temporary rim has been kept soft by the application of water from time to time. The method of preparing this rim for the application of the rings varies slightly with different potters. The rim may be pinched into scallops be- tween the thumb and forefinger of either hand, usually the right, or it may be roughened by vertical strokes of the kajepe on the exterior. In the former case the scallops may touch one another (pl. 16, a), or they may be separated by a quarter to a half inch of unpinched rim. When the kajepe is used, it also destroys the original smoothness of the rim, producing an irregular, broken surface to which the new roll can easily be welded. The potter must now build that part of the olla which has the greatest diameter. Each new ring of clay must therefore be of greater diameter than those which pre- ceded and those which will follow. Three or four rather slender rolls are used to make such a ring. After two complete rings have been placed on the vessel and flattened, the shaping is begun. Gradually the new rim is drawn in until the shoulder of the olla has been formed. Again the rim is smoothed before the vessel is set aside. The moulding of the olla has now reached the fourth stage (pl. 15, d). The olla is once more allowed to dry for about the same length of time as before. During these successive dryings the presence or absence of wind plays a considerable part in the length of time the vessel is allowed to remain in the sun; for a stiff breeze will dry the paste almost as quickly as the sun itself. The potters do not like to mould ollas when there is much wind because the paste dries so quickly 44 PUEBLO POTTERY MAKING that the vessel is ready to be taken up again before the second vessel, upon which the potter is working, is ready to set aside. Occasionally, but by no means always, the drying olla is turned so as to present a fresh section of the side to the sun. After testing with the hand the newly built part of the olla, to determine its firmness, the vessel, if sufficiently dried, is taken to the work-board and the building continued. The pinching of the rim is done as before, two more rings are added, and their shaping is begun. The rolls decrease very slowly in diameter. In shap- ing with the kajepe only the newly added section of the vessel is treated. At this stage the work becomes more difficult, for the two rings just added form the lower part of the neck of the olla, and therefore constrict the mouth of the partly finished vessel. If the paste is a little too soft, the newly built section will sag when the shaping is begun. The vessel must then be set aside at once until it reaches the proper degree of stiffness. While using the kajepe on the exterior, during this stage of the construction, the left hand is held inside the vessel not only as a brace or stop, but also as a support for the incurving side. When the scraping and smooth- ing have been finished, and the side has been given the proper curve, the rim is smoothed a little before the vessel, now in the fifth stage (pl. 15, e), is again set aside. Half an hour or so later the building of the olla is completed by the addition of one more ring. The rolls composing this ring are distinctly more slender than the first rolls used in the vessel. When this ring has been applied the rim is cursorily smoothed and the last shaping begun. The final delicate contour of the vessel depends to a large extent upon this final shaping near the rim. The kajepe is used with painstaking care, and the work progresses slowly. Stevenson in speaking of the polished black pottery of the Rio Grande pueblos says: “A solution of very fine ochre-colored clay is applied to the outside and inside near the top, or to such parts of the surface as are to be polished. While this solution thus applied is still moist, the process of polishing begins by rubbing the part thus washed with smooth, fine-grained stones until quite dry and glossy. The parts thus rubbed still retain the original red color of the clay. The vessels are again placed in the sun and allowed to become thoroughly dry, when they are ready for baking”’ (1883, p. 331). Mrs. Stevenson also gives an account somewhat similar: “In many of the pueblos the pottery is undecorated, the surface being finished in plain red or black. The ware is made of a yellowish clay, in the manner heretofore described, and the vessels are placed in the sun, where they remain for hours. They are then washed with a solution of red ochre, and while wet the process of polishing begins, the woman with untiring energy going over the surface again and again with her polishing-stone, every little while passing a wet cloth over the vessel to keep the surface moist. When the polishing is completed, the vessel is again placed in the sun for a short time before receiving its final baking in the oven” (1904, p. 375.) PLATE 21 Cc a. Applying orange-red slip with a cloth mop; the beginning of the stroke may be seen just above the lap of the potter. b. Polishing a bowl with a small stone after red slip has been applied. The marks of the stone are visible at first, but quickly disappear as the slip dries. c. Women working with the polishing stone. Note the light line about the shoulder of the large olla, where a space is always temporarily left unpolished. + SLIPPING AND POLISHING 61 which a little lard has been rubbed. The lard may be kept near the potter in any convenient receptacle, like a sauce-dish or the bowl of a spoon. A clean cloth is then immediately used to distribute the lard evenly upon the surface, and to remove any surplus. Some potters do not use this second cloth at all; others apply the lard to the vessels with their fingers, wiping it immediately afterwards with a cloth. In some cases, the application of the lard is withheld until the polishing is entirely completed. The polishing is then continued in exactly the manner just described. The surface is covered more carefully and more slowly, the areas worked upon often overlapping considerably. A cloth, sometimes a part of the potter’s apron, is now between the left hand and the vessel in order to protect the smooth surface. A considerable pressure is exerted. Some women use a short, very quick stroke; others a somewhat longer, slower stroke, hence taking more time for the work. In this way the surface is covered several times. Finally the routine treatment is dropped, and finishing touches are given by polishing small areas here and there which do not show the required amount of lustre. The strokes used at the end are usually slightly longer than the previous ones. Finally, after the stone has been laid aside, the surface is wiped once with a clean cloth before the vessel is set aside; it is usually placed upon a mat or cloth in order that the base may not be scratched by contact with the earthen floor. When the polishing of several vessels has been completed, they are gathered in a corner of a room on a mat or rug, and covered with a cloth to keep the flies and dust away, for it is said that fly-specks leave a black mark upon the burned vessel. In the case of large ollas one half of the vessel is doubtless coated with slip and polished before the other half is slipped. This is the process employed in polish- ing large ollas slipped with dark-red (see p. 63). No opportunity presented itself to see a large polished olla being made. In polishing the interior of a shallow bowl, the vessel is held in its normal position, tilted slightly to the right, and resting upon the right knee and the palm of the left hand, which in turn, rests upon the left knee. The polishing is done from the lip to the centre of the vessel. As the work advances, the bowl is turned counter- clockwise. The degree of polish obtained by different potters varies considerably, and yet in even the very finest examples of polishing the marks left by the stone may be faintly seen in certain lights in the form of exceedingly low ridges, generally running roughly parallel to the rim and too low to be felt with the fingers. The surface has a lustre almost equal to that of burnished metal. In pieces which are not as well polished, the ridges are higher and may be felt with the fingers; indeed they are often prominent enough to make the lustre uneven. Maria Martinez, who does the best polishing, is also the swiftest worker in the village. From the moment the vessel is picked up to apply the slip until the completion of the polishing, it is not laid down for an instant. Her strokes are quicker than those of the other potters; she covers the surface in much less time and therefore polishes a given area more often before the slip dries. Continued polishing tires the wrist and hand very quickly and is apt to produce cramps. Other potters are inclined to rest for a few 62 PUEBLO POTTERY MAKING minutes from time to time, especially after the application of the slp and again after the lard has been put on. One woman complained of the humid weather, because it did not allow the slip to dry quickly enough. The potters themselves say that streaky polish is due to lack of persistence on the part of the polisher. Maria attributes her success to the fact that she uses a faster stroke and puts on a little more lard than the others. Large vessels usually have a poorer polish than small ones. The secret of good polishing seems to lie in the ability of the potter to go over her work as many times as possible after the slip has been applied and before it becomes too dry. The time during which the vessel being polished is actually in the hands of the potter is given in Table VII. The first column (A) represents a constricted-mouthed bowl, about eight inches in diameter at the shoulder and four inches high, which was polished by Maria. In one hour and fifteen minutes elapsed time three such bowls were done, an average of twenty-five minutes for each. The second column (B) represents the polishing by another potter of the interior of a shallow wide-mouthed bowl. The actual time from the moment the bowl was picked up for the application of the slip until the polishing was done was forty-one minutes. A rest of one minute was taken after the slip had been applied, another of thirteen minutes after the application of the lard, in order to let the bowl “dry”, and a third of one minute when the final polishing was about half done. The interior of this bowl was a very fine example of polishing. TABLE VII Min. Sec. Mazin. Sec. First application of the slip 00.00 00.00 First polishing begun 02.50 03.00 Slipping of rim begun 04.45 Polishing of rim begun 05.30 Application of lard begun 06.05 10.00 Wiping with dry cloth begun 06.40 Final polishing begun 07.05 11.00 Polishing finished 24.05 26.00 DARK-RED SLIP The dark-red slip is a mixture of red slip, native white slip, and tempering material. It is applied to vessels which are later to receive a black design (see pl. 7, a, b). It is mopped on with a cloth in exactly the same manner as the red, and is also polished with a stone but never acquires as high a lustre as does the red. There seems to be a tendency for the first coat of this slip to dry more readily than the first coat of the red slip. While applying the slip to small ollas about six inches in diameter, the vessel is held by the rim with the left hand. Either the entire exterior may be slipped, or the base may remain uncoated, to be covered later with the orange-red slip. The slip is first applied to the rim, the forefinger being used instead of a mop. During this process the vessel is right-side up either in the lap or on the floor. The body is then slipped with the cloth mop, and the polishing done in two parts, with the SLIPPING AND POLISHING 63 shoulder as the dividing line. In polishing the lower part the strokes begin at the base, or at the lower edge of the slip in case the base has not been coated, and pro- ceed upward to the shoulder. The direction of the strokes is practically parallel to the rim. The upper part is polished from the shoulder to the lip. On the base, if it has been slipped, the strokes are first made in one direction, then at right angles to that direction. From time to time, as the polishing proceeds, the vessels are set aside in order to allow the slip to dry somewhat. They may even be placed in the sun or near a fire on the hearth. The potters explain that if the work is completed while the slipped surface is very damp, the resulting polish will not be as high as when the slip is just drying. Apparently, the work done just before the surface becomes dry plays an important part in securing a high lustre. One of the potters working on this ware applied a little lard to the surface after the polishing had been completed. Another potter used no lard whatever for this class of ware.1_ When the polishing has been completed the vessel is placed in the sun or near a fire to dry thoroughly before it is put away to await decoration. While the olla is drying it is covered with a cloth to protect it from flies. In polishing larger ollas one half of the vessel is coated with the dark-red slip and polished before the other half is slipped. Either the half above the shoulder or the half below the shoulder may be polished first. Rather quick strokes, three or four inches long, are made with the stone. Sufficient pressure is exerted to cause motion in the entire body of the worker. The strokes, as before, are usually parallel to the rim. Because of the larger surface to be covered in these vessels, the position of the olla on the lap of the potter is changed frequetly. It is supported with the left hand, which is placed palm down upon the exterior surface. While the lip is being polished, the mouth is turned toward the body and to the right, making an angle of about sixty degrees from the horizontal. In polishing the upper part of the shoulder the potter turns the mouth to the left and away from the body (pl. 21, c). Usually the mouth is more nearly horizontal in this position than in the former. Before applying the slip to the lower half of the olla, a faint line is drawn with the polishing-stone around the lower part of the body to define the lower edge of the body-slip. During the slipping and polishing of this portion of the surface, the olla is held with the mouth nearly vertical and to the left, directed away from the body. When the polishing proper is completed, the finishing touches are given to the entire exterior by rubbing small areas here and there which do not entirely satisfy the potter. As in the case of the red slip, the polishing must be completed before the slip becomes too dry. When there is a large surface to be polished, as in the case of these ollas, it is of course necessary that the work upon any given section of the surface be completed as quickly as possible. Therefore when two potters are working together, the swifter of the two does the polishing on the larger vessel, regardless of which of the two applies the slip. After the polishing proper has been completed, the olla may be turned over to the slower worker for the finishing touches. This necessity for speed in polishing is probably the reason for slipping only a part of the surface at one time. ' This second potter, however, did use lard in polishing vessels to which the red slip had been applied. 64 PUEBLO POTTERY MAKING Now and then, as the polishing proceeds, the potter changes stones. An important factor in this change is the desire to rest the fingers through the slight alteration in grip afforded by the different shapes of the stones. Occasionally the change is due to a wish to obtain a stone with just the proper shaped surface for the section of the olla being worked upon. There is also a tendency to use a larger, rougher stone at the beginning of the work, for which is substituted later for the final finish a smaller, finer-grained, and therefore smoother, stone. Because of the practice of slipping and polishing only half the surface at a time, there develops around the shoulder a narrow line of dried slip, which is natur- ally lighter in color than the worked areas. (This line may be seen encircling the olla in pl. 21, c). After the polishing of the upper and lower areas has been com- pleted, the potter’s attention turns to this line, and since dry slip cannot be polished, the rubbing stone is either wet with the tongue or dipped into the liquid in the slip- container before being used on the line. The latter method appears to give the best results, but in either case, the moistening of the stone is done very frequently, and the process of eliminating the lighter line is a painfully slow one. Even when the best results have been obtained, the line is not entirely obliterated. Occasionally the stone is moistened with the tongue while giving final touches to other parts of the surface. When the polishing with the stone has been entirely completed, a little lard is rubbed on the surface either with the forefinger or with a greasy cloth; the surface is then vigorously rubbed with a chamois.! This distributes the lard evenly and very noticeably improves the lustre. Then the vessel, after being covered with a cloth, is put in the sun to dry thoroughly. The great difference in the time required for polishing large and small ollas requires two tables to present the details. Table VIII gives the time during which a large olla, about fourteen inches in diameter at the shoulder, was under the hands of the potters. The time devoted to obliterating the light junction-line, about fifteen to twenty minutes, was considerably longer than usual. Table IX gives the time required for three small globular ollas, about six inches in diameter at the shoulder. The surface of each of these was approximately the same as that of the polished black constricted-mouthed bowl recorded in Table VII. 1 The substitution of the chamois for a cloth was inaugurated by the potter using it. SLIPPING AND POLISHING TABLE VIII Hrs. Min. Sec. 00.00 — Drawing of line about lower part of body begun 01.00 — Slipping of lower half of olla begun 08.30 — Slipping finished, polishing begun 23.30 — Vessel transferred to a slower worker 40.00 — Set aside 04.45 — Time out 40.00 — Polishing by slower worker continued 47.45 — First application of lard begun 48 .45 — Polishing with chamois begun 50.45 — Lower part finished ? — Time out 50.45 — Slipping of upper half begun 55.15 — Slipping of body done, slipping of rim begun 56.45 — Polishing begun 1.00.45 — Vessel transferred to the swifter worker 1.20.45 — Vessel transferred to the slower worker, obliteration of junction-line 1.53.45 — First application of lard begun 1.55.45 — Polishing with chamois begun 1.59.45 — Polishing of vessel completed TABLE IX Min. Sec. Min. Sec. Min. Sec. Slipping begun 00.00 00.00 00.00 Slipping completed 03.00 Time out 01.00 omitted Polishing begun 03.00 04.00 04.00 Set aside (second one beside fire) 27.30 31.30 Time out 03.00 34.30 omitted Polishing continued 27.30 omitted Lard first applied, chamois used later 30.30 31.30 32.00 Work on vessel completed 31.45 32.00 36.00 PAINTING Three varieties of paint are employed in making the designs — the black, or guaco, which is used on red and polychrome wares, the orange-red (also used as a slip), which serves as a paint in filling certain spaces in the designs upon polychrome ware, and the black ware paint which produces the designs upon polished black ware. ! The consistency of the guaco, when dissolved in water and ready for use, varies from that of water to that of thick cream. The solution is sticky and has a char- acteristic odor. A thin solution when applied to the surface of a vessel is yellowish- green, and has much the same appearance as a fresh coat of the orange-red paint. After drying the two are easily distinguishable. A thick solution of guaco is dark brownish-green when applied to the vessel, and on drying has a noticeable “body’’, so that the lines appear slightly raised and glossy. It is not possible to draw as fine a line with the thick solution as with the thin one. The orange-red is never used in painting lines, but only for filling areas, and is therefore always applied with a medium or heavy brush. In preparing the black ware paint, a slight amount of guaco is added as an adhesive, and the solution is often stirred with the fingers in order to insure com- plete dissolving of the coloring matter. When first applied to the vessel, this paint is almost transparent; as it dries it becomes yellowish. The principal precaution taken when painting is begun is to guard against flies. They eat the moist guaco, causing blank spaces in the lines, and also make fly-specks on the slip which turn black in the firing. The room is therefore cleared of flies as far as possible, and great care then exercised to keep the door shut. The painter watches the pot constantly, and often interrupts her work in order to brush a fly from the design. If it is necessary to do the painting out of doors, the services of an assistant are required to wave a cloth back and forth across the top of the vessel to keep the flies away.2. When the work has been completed the vessels are immediately covered with a cloth. The receptacle for paint may be either a small open-mouthed pottery bowl or a china sauce-dish. During the painting it is on the right side of the potter within easy reach, either on the floor or on a low stool. In it is always a stirring-stick. 1 The use of this paint for producing designs upon polished black ware was discovered by Maria Martinez in June, 1921. On inquiring why other potters did not copy the process, it was learned that because of certain taboo- like restrictions the secret of making this kind of ware would not be disclosed until a year after its discovery. Al- though the matter could not be further investigated because of the unwillingness of the Indians to discuss such things, it would appear that we have in this case a sort of primitive patent-right. At the present time (1925) prac- tically all San Ildefonso potters make this ware, which has proved extraordinarily popular; Maria, however, still produces by far the finest pieces (see pl. 8, a). 2 Occasionally such precautions are disregarded, apparently through laziness. One potter did her painting in the same room in which some meat was being cooked. The combined odors of the cooking meat and the guaco attracted all the flies in the neighborhood, but fortunately screens kept some of them out of the room. PLATE 22 b Painting designs on small vessels. The decorator’s right hand does not come in contact with the pot, and the tip of the brush is trailed rather than stroked across the surface a. Maria Martinez. b. Maximiliana Martinez. PAS EN UN.G 67 The brushes are usually kept in the paint, or occasionally beside it, and sometimes a pencil is also near at hand (pl. 23, a). In decorating the exterior of a constricted-mouthed bowl, the vessel is held upright and inclined very slightly towards the body; it rests on the left knee and is steadied by the pressure of the left hand against the interior of the rim (pl. 22, a). The potter sits in a position which allows the light to come over her right shoulder directly upon the section of the bowl being painted. As the work proceeds the vessel is turned counterclockwise. When the design extends slightly below the shoulder, the bowl is inclined to the left and away from the body. If a considerable portion of the design is below the shoulder, the vessel is inverted and is supported by the fingers of the left hand against the interior base of the bowl. If the interior of an open-mouthed bowl is being painted, the enclosing lines near the rim are made first. During this process the bowl is held with the mouth vertical and to the right, while the lines are drawn on the lower part of the interior rim. The vessel moves counterclockwise. The bottom of the interior is painted with the bowl standing in its normal position on the left knee, the mouth inclined to the right and toward the body. When a large vessel, such as an olla, is to be painted, it is placed upon a box or table of the proper height, which has previously been covered with a rug or mat to protect the base (pl. 23). The painter chooses her position so that the light will fall over her shoulder upon the vessel. During the painting of the upper part of the vessel it is touched with the left hand only when it needs to be turned. In working below the shoulder the vessel is tilted slightly to the left, and away from the painter. The paint-brushes are made of slivers of yucca (fig. 5). They may be roughly grouped into three weights — fine, medium, and heavy.! The fine ones are used in making outlines on the smaller vessels; the medium ones either for line work or for the filling of small areas; and the heavy ones for filling only. During the painting there are from three to six brushes in the paint vessel. These brushes are of such durability that the potters have no definite idea of the length of their usefulness. Since the fibres are brittle when dry, brushes are occasionally broken by accident; to prevent such breakage they are soaked in water for a few minutes to soften them before they are used. The brush is held in the right hand, with the fingers in the position used in holding a pencil or pen. The ends of the fingers are two or three inches from the tip of the brush (pl. 22, a, b.; pl. 23, a). The fingers of the right hand do not rest upon the surface of the vessel and the entire right arm is unsupported (pl. 23), although at times the elbow may be unconsciously steadied against the body. The straight- ness and evenness of the lines drawn under these conditions are remarkable. 1 Stevenson gives no details of the painting at Zufii; “‘When the pigment is properly reduced, and mixed with water so as to form a thin solution, it is applied with brushes made of the leaves of the yucca. These brushes are made of flat pieces of the leaf, which are stripped off and bruised at one end, and are of different sizes adapted to the coarse or fine lines the artist may wish to draw. In this manner all the decorations on the pottery are pro- duced” (1883, p. 330). Mrs. Stevenson is just as brief: “After a thorough drying of this foundation, the slip, the designs are painted with brushes made of yucca needles, the pigments having been ground in stone mortars and made into a paste with water to which a syrup of yucca fruit is added” (1904, p. 375). The stone mortar for pigment grinding may be seen in pl. 31, a. 68 PUEBLO POTTERY MAKING There is a slight personal variation in the method of contact of the brush with the vessel. One potter uses only the tip of the brush; another first places the tip upon the surface, and then makes the line with the body of the brush; a third places the body of the brush upon the vessel at the first contact. In making a line a trail- ing stroke is invariably used; its direction is usually toward the body, but occasion- ally away from it. The brush is always moved slowly, and the angle at which it is held varies according to the part of the surface over which the line is being drawn, and upon the part of the stroke which is being made. At the beginning of a stroke the angle is an acute one, varying from forty-five to seventy degrees (fig. 8, a); about the middle it approximates ninety degrees (fig. 8, b); while at the end it is often an obtuse angle of as much as one hundred and twenty degrees (fig. 8, c). On small vessels the strokes seldom exceed four inches in length; on larger pots they are sometimes as much as six inches long. After each stroke the brush is dipped into the paint vessel; it is then always drawn across the stirring stick, which is kept Fic. 8. Angles at which paint-brush is held during a long stroke; a. Beginning. b. Middle of stroke. c. End. there, in order to remove excess paint before being applied again to the surface. Even after this precaution more paint occasionally remains on the brush than is needed; in such a case the excess is removed by touching with the tip of the brush various larger areas which will later be covered with paint. The width of the lines drawn is largely dependent upon personal variation, although the type of design also governs their width to some extent. Exceedingly fine lines, for example, would obviously look out of proportion in a bold design upon a large olla. The lines vary in width from one-thirtieth to one-tenth of an inch; the great majority are between one-fifteenth and one-twentieth. Lines one- eighth or one-quarter of an inch wide are in reality double, that is, they actually consist of two lines painted so close together that they touch along their entire length. Still wider lines are made by two parallel lines, with the space between filled up. Some potters simply make the line once, retouching it only in small sections which most plainly require such treatment. Others go over each line at least twice in order to insure a constant width. *(jeqAoy epIUOJUY) soysniq v1j}x9 pur Yoys-Surdys YW dno-jured vy} st yMOIJ UI YOUaq ey} UG “Ysnaq aq} Jo YAZUe] oY} pue JoJUIed 94} Jo UI po}toddnsun 94} 9]0N “seI[O aBae] SuryeI1000q q e 66 ALVId PAINTING -69 From the point of view of technique, the lines upon the exteriors of small vessels, such as constricted-mouthed bowls, may be divided into two groups — the long enclosing lines and those within panels. In forming the enclosing lines, especially the long horizontal ones, the vessel is turned while the brush remains almost stationary. There are two methods of forming such long horizontal lines, which of necessity are made of a series of relatively short strokes. In one case the growth of the line is in the same direction as the strokes, that is, each stroke begins at the point at which the previous stroke ended. In this method the vessel is turned counterclockwise. In the other case the growth of the line is opposite to the direc- tion of the stroke, that is, each stroke is begun a short distance beyond the end of the line and is drawn to meet the beginning of the previous stroke, the vessel being turned clockwise. In either case the fingers of the left hand, which hold the pot by the interior of the lip, are spread far apart in order to insure the constant and regular motion of the vessel. When the lines within a panel are being drawn, the procedure is just the reverse. The bowl remains stationary while the brush is drawn across it. Occasionally lines which are nearly horizontal are drawn first in one direction, then in the other. In some cases, when long diagonal or curved lines are being made, the vessel is turned very slightly counterclockwise. Large vessels, such as ollas, remain stationary while the brush is being drawn across the surface, and are turned only when a new area is to be worked upon. Lines within panels are usually made with a single stroke of the brush, for it is seldom that a diagonal or curved line within a panel is more than four or five inches long. In large open designs the long lines, both straight and curved, are often drawn in two parts. Crosshatching is made by two sets of parallel lines crossing each other. Dotting is done with the tip of the brush touched lightly to the surface. Spaces are filled with a heavier brush by means of many short strokes. As a rule the strokes begin at the upper right hand corner of the area and proceed downward. In filling spaces, as in drawing lines, some women go over their work only once, others apply two or three coats in order to insure even distribution of the paint. Some potters exhibit much sureness of touch and confidence in their own ability; their designs are executed without hesitation, but at the same time slowly. Others make hard work of the painting, seem uncertain, and occasionally stop to rest and inspect the symmetry of the pattern. There are two general points in the painting of vessels which should be empha- sized. The first is the remarkable steadiness of the painter’s hand. It seems almost incredible that such straight, unwaving, even lines can be drawn by a hand which is supported only by a completely free arm, and guided merely by the end of the brush. The second is the fact that the men often assist in the painting of designs. They may either execute a complete design upon a vessel, or relieve the painter from time to time during the construction of large patterns. This is the only phase of the actual manufacture of pottery in which the men of the village take 1 part. 1 On pp. 78 to 84 will be found notes on the actual painting of several typical designs. FIRING The firing of the vessels is not only the last major step in the making of pottery, but it is also the most critical one. The supreme test of the potter’s work is to subject it to the fire, for many forms of accident occur during the process, some of them due to careless handling of the vessels or of the firing materials, others to defective workmanship or to hidden flaws in the paste. It is only natural that the potters should exhibit considerable excitement and nervousness during the firing. Some women proceed calmly and methodically, and take occasional accidents as part of the day’s work; others are exceedingly nervous, and show exasperation when things go wrong. The latter, as a rule, have more accidents than the former. One potter, in six burnings, lost two large ollas through breakage, and had innumerable smoke-clouds, several of them rather severe ones. The firing falls naturally into four distinct phases: the preparation, the build- ing of the oven, the burning, and the treatment after burning. Each of these phases will be considered separately. PREPARATION The oven is usually situated behind the potter’s house. All that is required is a level space free from vegetation; no attention is paid, as a rule, to the position of the sun or to the direction of the prevailing wind, and the same spot is used time after time. If on the evening before the firing there are any signs of rain, or if a heavy dew is expected, the area on which the oven is to be built in the morning is covered with a thick layer of dead ashes to protect it from moisture. It would be a fatal mistake to make the oven on ground which would give off steam during the burning. About six o’clock the next morning a fire is started on the area over which the oven is to be built. While this preliminary fire is thoroughly drying the ground, the accessories are collected (pl. 24, a). Slabs of dung are brought out from the storage places; some of them are placed against the house wall to dry in the sun, others remain in the washtubs in which they have been carried. The material for the grate, and other iron bars, are placed nearby. Pokers of wood and iron, shovels, and sometimes pitchforks, which are to be used later in handling the burning fuel and hot vessels, are placed within reach. When a collection of small tin cans, pail-tops, and small stones saved for this purpose has been added, the workers are ready to begin the burning. Usually a supply of cedar kindling has been split, but sometimes this is done as the wood is needed. BUILDING THE OVEN When the preliminary fire has died down to a mass of coals, these are levelled to form an area of hot ashes about three feet in diameter. On this the oven is built. The surface upon which the vessels are placed must be raised a few inches PLATE 24 b a. Drying the oven site with a preliminary fire before burning the pottery. At the lower right-hand corner are an old iron grate which will later support the vessels, two iron rods to hold up the roof of the oven, and a wooden poker. Cakes of dung for the oven walls are drying in the sun against the house. b. The vessels on the grate, and the oven wall of dung cakes begun. Small tin cans support the cakes and keep them from touching the vessels. The grate rests on stones, and split cedar kindling is placed below it on the embers of the preliminary fire. FIRING 0 above the ground to permit the introduction of fuel below the pottery. Such a surface is usually formed of iron rods of one kind or another. One potter built up a grate of a varied assortment of iron junk supported on tin cans and odd-shaped iron fragments. Another potter used a worn-out stove-grate supported on four half-bricks. The vessels are then placed upon the grate in an inverted position. No attempt is made to keep them from touching one another. In fact, they are crowded to- gether in order that the greatest possible number may be burned at once (pl. 24, b). In firing red ware and polychrome ware only one layer of vessels is placed upon the grate. When polished black ware is to be burned, two layers may be made. The vessels in the second layer are always placed carefully between those of the bottom layer, in order that there may be free circulation of air on both the interior and exterior of all the vessels (pl. 25, a). As a rule the larger bowls are placed in the lower layer. The number of polychrome vessels burned at one time varies from half-a- dozen to twenty, according to the area of the grate and the size of the vessels. At one burning there were eleven pieces, eight medium-sized and three small; in another there were twenty, eight of which were medium-sized, and the other twelve very small. It is possible to burn as many as thirty-five polished black bowls at once. Some potters burn both polychrome and red pottery in the same oven; others insist that this should not be done, because red ware requires far less time and heat than does polychrome. After the pots have been placed on the grate, pieces of split cedar six to fifteen inches long are inserted underneath it. Pifion is never used, but the potters could not explain this, saying they had never tried it. A wall-like ring of dung-cakes, placed on edge but not set as snugly together as they might be, is then built around the grate (pl. 25, b). Small tin cans, held in place by the weight of the dung, are used to prevent the cakes from touching the vessels (pl. 24, b, shows one of these cans very clearly). Sometimes small stones and broken bricks are used in place of cans. While the ring is being completed more kindling may be added. The Zuni oven differs from that of San Ildefonso in being built of smaller pieces of manure which are laid up horizontally instead of on edge (see pl. 31, b, ¢). The fire may now be lighted before the oven is finished, but sometimes the potters wait until the roof is nearly complete. Cedar-bark shreds are generally used to start the fire. The lighting is done through the spaces between the dung- cakes, usually at more than one place, sometimes in as many as five. No attention is paid to the wind in this process. If the fire does not start quickly enough, cloths are used to fan the flames. The roof or vault of the oven is then built. Some potters place iron bars across the top of the dung-ring, keeping them from touching the vessels by inserting tin cans and stones. On these bars flat cakes of dung are laid, and the larger holes are covered with smaller pieces of dung. Other potters dispense with the bars and rest a large circular cake of dung upon cans and stones set in the centre of the pile of pottery. The space between this central cake and the top of the dung-ring is bridged by other cakes which rest on the dung alone. In this manner a low vault of dung-slabs is formed, roughly square in shape, two and a half to three feet on a 72 PUEBLO POTTERY MAKING side, and about a foot and a half high (pl. 25, ce). There are still left numerous spaces, both large and small, between the cakes. These are covered with smaller pieces of dung, and with old tin tops of lard-pails or discarded tin plates (pl. 26, a). Even after this, however, there remain enough small spaces to allow free circulation of air, and to prevent the smothering and consequent smoking of the vessels. Through these smaller spaces the flames and pots may be seen. The building of the oven is now complete; by this time the fire has usually been started, and the flames are well under way. As arule more than one burning is undertaken during a morning. ‘The building of the oven for the second burning differs slightly in its preliminary stages from that described above. After the previous oven has been destroyed, the ashes are smoothed out, and the grate set straight and carefully dusted so that no ashes re- main (pl. 26, b). The bowls are than placed on it as before. Partly burned cakes of dung, which remain from the first burning, are re-used. If, in placing them on the oven, ashes drop on the vessels, care is taken to blow them off. Some potters stand the vessels which are to be burned on the warm cakes of dung for a few minutes before placing them on the grate (pl. 2€, b), a process which is supposed to heat them slightly and thus prevent breakage during firing. Other potters would not think of doing this, for vessels treated in this manner always have discolored bases, where the warm dung has touched them. Ollas twelve to fourteen inches in diameter are burned in pairs, with a few smaller pieces beside them. The oven is built in the same manner as before. Very large ollas are usually fired one at a time; the oven, except for its greater size, is said to be of the usual type. BURNING As was said above, the firing of the pottery is done in the morning. The Indians say that they wish to get it over with “before the sun grows hot”. Their own personal comfort probably plays a more important part in this than does the effect of the sun upon the pottery. As a rule the firing is withheld until a sufficient number of finished vessels have accumulated to permit three or four burnings in one morning. The entire forenoon is spent at this work, and sometimes it drags over until early afternoon. The actual burning of the vessels occupies a period of about half-an-hour for each oven; it is said that the length of time has not been appreciably shortened in the past forty or fifty years. The black ware is always saved for the last oven, since the process employed completely precludes the possi- bility of rebuilding the oven at once. At the beginning of the burning white smoke is apt to be given off, but too much smoke is regarded as a bad sign, since it signifies that the dung cakes are not sufficiently dried. After fifteen minutes or so, that is when the process is about half finished, the amount of smoke has greatly diminished (pl. 26, a). About this time more kindling is added through openings made by temporarily removing a piece of tin, and new cakes of dung are added where necessary, usually on the top of the oven. The Indians say that they judge of the condition of the pottery in the oven by its color; the paste and slip must be of just the proper shade before the vessels are PLATE 25 c The building of an oven. a. A double layer of bowls is on the grate; the woman is placing a can between a dung-slab and a bowl. b. The wall of dung-cakes completed. c. The oven finished, but the chinks not yet filled. H | PLATE 26 a. The oven fired. The chinks between the dung-slabs have been partly closed by smaller pieces of dung. b. A firing completed and a grate prepared for a second firing. Two vessels to be burned are warming on hot dung- slabs; the pots that have just been taken from the fire are cooling in the shadow of the house. * FIRING 73 thoroughly burned; if they are too dark the burning must continue.!_ Some potters seem to pay little or no attention to the color of the vessels in the oven. When the potter considers that the burning has been completed, the cakes of dung on the top of the oven are lifted off with a pair of pokers, and those in the ring around the grate are tipped outward. Thus the vessels on the grate are exposed, and their removal is begun at once. Some are tipped on shovels or hay forks; pokers are inserted under and into others. They are then deposited upon tins which have been placed on the ground within six or eight feet of the oven, and are left there from ten to twenty minutes to cool. The women often complain about the heat from the oven during the removal of the vessels. As soon as the grate has been cleared, preparations are begun for the next burning (pl. 26, b). In one instance a potter decided that a certain vessel which had been removed from the grate was not sufficiently burned. Another fire was already in progress, but when the third was built the vessel was replaced on the grate and burned again. When it came out, however, one side was badly overfired. The time occupied by various burnings is given in the following table. The first four columns represent burnings by Maria Martinez; the last three by Antonita Roybal. The seventh column records the oven in which the partly fired piece was reburned, and in which a cooking vessel was also placed. TABLE X (12) IS) Aye 5) (G7) Minutes Preparation and building of oven begun 00 00 00 00 00 00 00 Fire started 2 15 06 12 15 15 #409 More kindling and dung added ADT 255 5 25 57 Oven broken up 52) oie 36 eel ae 1 2a0 402 T, Last bowl removed from grate 58 41 42 47 77 °45° 30 The time required for burning the different wares varies only slightly. Some potters say that red ware takes less fuel, less heat, and less time than polychrome ware; others place both wares in the same oven. The difference in the time required for these two wares is probably no greater than the chance variations in the length of burning as given in Table X. Cooking vessels need to be fired only from one-half to two-thirds as long as the two wares just mentioned (cf. Table X, column 7). The polished black ware will be considered later. The changes in color before and after firing, and when hot and cool, are very noticeable in some pigments and slips. The orange-red paint is yellow before firing, firing turns it orange-red, almost the color of burnt sienna; cooling produces no noticeable change in this shade. Burning has only a fugitive effect on the red and dark-red slips. While still hot, upon removal from the oven, these are both a dark chocolate shade. As the vessels cool the different reds gradually reappear, until when cold they are the same color as before firing. In some cases, these pigments seem to be just a shade darker after firing than before. The two kinds of white slip are a dead white when applied; after firing they take on a slight pinkish- brown tinge, more cream than white. Cooling produces no further change. 1 One woman tried her best to teach me how to tell these shades apart, but it proved utterly impossible for me to distinguish the darker from the lighter. 74 PUEBLO POTTERY MAKING The most interesting change caused by firing is in the black vegetable pigment (guaco). It has already been pointed out (p. 66), that when this paint is laid on thickly, the line made is a little raised and glossy, like a glaze. This “body” to the paint is probably formed by vegetable matter in suspension in the solution. When the vessels with such decorations are removed from the oven after burning, these lines are seen to be white or grey. The material which formed the body of the pigment has been reduced to white ash, which adheres to the surface, but can be rubbed off with the finger or a cloth, while the black color itself has been burned into the clay. Where a thin layer of the pigment was applied, the line, after burning, is light grey, because the black under the thin coat of ash shows through. In those vessels on which a thick solution of pigment was used, the decorations are dead white, and the surface of the ash is often crackled. The thickness of this ash seems to have some effect upon the manner in which the black pigment is burned into the clay, for in decorations covered with a thick layer of ash, the black is of an irregular color with streaks of grey in it. When the thin pigment is used, the resulting black on the finished vessel is of a uniform shade. The glossiness and raised character of the pigment is of course completely destroyed during burning. Guaco lines do not change in shade while the vessel is cooling. The color of the paste is little affected by burning. In both the red and the white clays, the change is simply one of tone, that is, the clay is lighter after burning than before. The cooking-vessel clay before burning is greyish yellow, but after it has been removed from the oven it is a rich orange-yellow. These cooking vessels eventually become blackened by use over an open fire. Vessels destined to be polished black ware are treated in quite a different manner during the firing stage, for they are to be subjected to a smothered fire, which will result in the deposition of carbon, thus turning them from red to black. The oven is built in the same way, but greater care is taken to fill gaps, so that more of the heat may be retained. Enough spaces remain, however, to permit free circu- lation of air. More kindling is used, for a hotter fire is necessary. When the fire has reached the stage at which other wares are removed, it is smothered with new, pulverized, loose manure. Just before the smothering the vessels have the dark chocolate color typical of the red wares while hot. The potter always attempts to smother the entire oven at once by dumping upon it a whole washtubful of fine loose manure. If there is a wind, flames are apt to break out in one or two places. They are, however, hurriedly extinguished. When the loose manure is added, the arch of the oven is, of course, broken, and both cakes and loose manure come in contact with the vessels. For this reason the potter does not exercise particular care in building the oven to keep the cakes from touching the vessels, as they are to be entirely black in the end and a little premature smoking does no harm. After the manure has been added, the mound is continually prodded with a poker to redistribute the loose manure and make certain that all the pieces are equally covered. An extra supply of loose manure is at hand, and this is added in large and small quantities from time to time, as occasion demands. ‘Two washtubsful are generally used, sometimes three. The mound of manure gives off a dense white smoke after the smothering has begun (pl. 27, a). Great care is taken to prevent flames from appearing, since these would remove the carbon from the vessel. PLATE 27 a. A fire smothered with loose manure to produce polished black ware. b. Wiping vessels that have become cool enough to handle. One woman wipes off the ashes with a dry rag, then passes them to her companion, who goes over them with a slightly greasy cloth. = ‘ ‘ ‘ =, -" , » 5 : = ; = + e ’ Ps " , 4 bd . Es ' a - . , «. ; : . : ‘ ie ‘ ] . / . ~ ’ ! ‘ 7 toy ot A ' \ FIRING 75 Ten or fifteen minutes after the smothering the first piece is dug out of the mound with the poker. It is placed a foot or two from the oven and hastily wiped with a dry cloth to remove all manure. The surface of the vessel is a beautiful shiny black color, which does not change at all on cooling. If black ware paint (see p. 24) has been used, it changes from the greenish-yellow color that it had before burning to a dead matte black which contrasts very effectively with the polished surface of the vessel (see pl. 8, a). At first the vessels come from the smoking mound slowly, and all holes left in the pile by the removal of vessels are carefully filled again, but later they are taken out as quickly as possible, and toward the end no attempt is made to keep the pieces still in the pile thoroughly covered. If, when a vessel is removed, its condition does not quite suit the potter, it is replaced in the smoking manure and completely covered. Certain polished black vessels are further manipulated in such a way as to produce an irregular red blotch upon them! Specimens destined to receive this red blotch, which is usually placed near the rim, are reburied in the hot manure lying round the edge of the pile with that portion which is to have the blotch left un- covered. Against this exposed portion is placed a smoking fragment of a dung- slab. The action of the heat and air results in the removal of the carbon from the surface, so that that part of the vessel which is not covered with manure and ashes regains its former color, the red of the pigment. Since the pot is pushed about a good deal during this process, the line between the red and the black surface is not always very definite, which improves the appearance. The Indians themselves cannot tell beforehand just what shape the blotch is going to take, and must there- fore watch the vessel continually. Sometimes burning shreds of cedar bark are placed against the exposed surface to hasten the process, but actual flames are not necessary in order to obtain the desired result. If the red blotch is too large, part of it is simply recovered with hot manure-ashes, and a few minutes later will again become jet black. So far as looks are concerned the success or failure of this red blotch upon black ware depends largely upon the artistic sense of the potter making it. In one group of thirty-three polished black vessels fired together, sixteen were given a red blotch; eight or ten of these were excellent pieces. The time consumed in burning polished black ware is shown in Table XI. It should be noted that before the loose manure was added, the vessels were sub- jected to the fire about the same length of time as those of other wares. TABLE XI Minutes Preparation and building of oven begun 00 00 Fire started 16 $18 More fuel added Al 39 Oven smothered with loose manure 46 45 First bowl removed 59 59 Last bowl removed 74 99 1 This variant in polished black ware is a new departure. It was discovered, probably accidentally, by one of the San Ildefonso potters early in the summer of 1921. The process by which the red blotch is made has not as yet been brought completely under control. 76 PUEBLO POTTERY MAKING ACCIDENTS The accidents which may occur in firing are of two general classes—those which result from faulty treatment during the construction of the vessel itself and those which are due to careless manipulation in burning. The latter are the more frequent. A vessel may crack or flake badly in the oven; often the entire base breaks off. The fault in this case lies in the original moulding, because small stone fragments or air-bubbles were allowed to remain embedded in the paste. Since the rate of expansion under heat varies for different substances, a great strain develops about such stones or air-bubbles during firing, and the natural result is cracking or flaking of the clay. In some larger vessels the slip flakes away around the shoulder, where the two areas of the surface met when the polishing was done (see p. 64). In the potter’s opinion these flakes, which are exceedingly small, are probably caused by minute air-bubbles that had lodged under the slip while the line about the shoulder was being polished. A third type of accident is merely a blemish; it is due to flies settling on a vessel before burning; the resulting fly-specks are burned into the clay, and the surface of the pot is sprinkled with dots quite as black as guaco decorations. The most common form of blemish caused by careless manipulation during firing is the “‘smoke-cloud” or “fire-cloud”’, a circular blackened area, the darkest part of which is at the centre. There is no question but that this is caused by con- tact between the vessel and a dung-cake, and the result is probably due to moisture in the dung which brings about a deposit of carbon on the surface. If, during the burning, a cake of dung falls, it will probably come in contact with the surface of some bowl. If it is removed at once there is little danger of a smoke-cloud, and the potter, when she notices such an accident, immediately tries to secure the fallen cake with two pokers. With much skill she carefully extricates it from within the oven without disturbing the other cakes about the place from which it fell. Fire- clouds may be produced upon the bases of vessels by setting them on hot cakes of dung before firing; or upon damp, or relatively damp, ground immediately after firing. Excessive dampness, such as steam from wet ground under the oven, may in addition to discoloration, produce warping of the vessels. Another sort of blem- ish is occasionally caused by rust from a tin can resting upon a vessel during firing; such a spot is usually reddish brown in color, and covers a very small area. If light areas appear on polished black ware, it is safe to assume that they were brought about by lack of proper ventilation within the oven during the pre- liminary burning, such as would occur if two vessels were so close together as to prohibit the free passage of air. If white slip is touched just before burning, the oil from the fingers is apt to be fired in, thus ruining the uniform appearance of the surface by the potter’s indelible fingerprint. To avoid such an accident, poly- chrome vessels are usually handled only by the interior of the rim on the day they are burned. Underfiring and overfiring, with consequent damage to the ware, are usually due to gross carelessness on the part of the potter in the irregular placing of kindling. The wind also has something to do with it. If there is a stiff breeze blowing, the probabilities are that the windward surfaces of vessels within the oven will be underfired, while those in the lee of the vessels will be overfired. PLATE 28 Courtesy Amer. Mus. Nat. Hist. ZUNI. PREPARING CLAY a. Pulverizing dry ingredients on flat stone slab with a mano or hand stone. b. Wetting, mixing, and kneading clay; water-container in foreground; prepared clay in bowl. PLATE 29 tigen panei? _asgpoine Courtesy Amer. Mus. Nat. Hist. ZUNI. MOULDING a. Lower part of vessel completed; potter forming roll of clay with which to continue building. b. Applying roll of clay; left hand guides roll; right hand welds it to side of vessel. PLATE 30 Ceourtesy Amer. Mus. Nat. Hist. b ZUNI. SURFACING a. Going over outside of vessel with moulding tool to smooth out irregularities. b. Vessel has been removed from base-mould and covered with white slip from bowl in foreground. Potter now polishing slip with rubbing stone. PLATE 31 b c ZUNI. PAINTING AND FIRING a. Applying design with yucca-leaf brush. Black pigment in shallow stone mortar, red in small white bowl. b. Building oven of dung cakes — note kindling at feet of figure at right. c. Oven domed over and set afire. (Photographs from American Museum of Natural History). one FIRING 717 In underfired vessels the color of the pigments is not true, being usually mid- way between the unfired color and the fired color; as a rule the paste is also dark and friable. Overfiring is more easily detected than underfiring. A slight overfiring may be first noticed in the black guaco paint, which has a tendency to become bluish and light if burned too much. Other bad results follow in quick succession as overfiring is increased: at an early stage the white slip becomes smoky; in severe overfiring it may turn black, as in a smoke-cloud; the paint of the designs is apt to flake off; and finally, in a bad case, the guaco will turn nearly white. TREATMENT AFTER BURNING Polished black vessels, when removed from the fire, are set directly upon the ground within a foot or two of the oven. They are at once wiped hastily with a dry cloth to prevent any fragments of the new manure from sticking to the surface. When the vessels are sufficiently cooled they are again wiped with a clean dry cloth and taken into the house for storage. Occasionally the first wiping, while the bowl is still hot, is omitted. When pieces of polychrome ware or red ware are removed from the oven they are placed on the ground some six or eight feet from the fire, resting on tins in order to prevent possible discoloration from contact with the damp soil, as well as to prevent dust and dirt from sticking to their bases. The vessels are piled on these tins in any manner, often three or four on top of one another. When the pottery first comes from the fire, it is still much too hot to touch, and radiates heat copiously. Ten or fifteen minutes later, when the vessels are cool enough to handle, they are removed from the tins and collected at some convenient place to await wiping. First the pieces are gone over with a clean dry cloth to take off the guaco ashes and any dust that may remain from the oven (pl. 27, b). Each vessel is then wiped with a slightly greasy cloth, which gives a faint sheen to the surface and removes the blue tinge which is apt to be found in the black guaco-covered areas. Some potters have substituted a chamois skin for this second cloth. It took the two women shown in pl. 27, b, just fifteen minutes to wipe with the two kinds of cloths the twenty-two vessels figured. When the wiping is done, the pottery is carried to the house and stored in one of the rooms. The pieces are placed on the floor, usually with a carpet or rug under them, and covered with a sheet to keep off dust and flies. The time occupied in each of the individual stages of pottery making has been considered, but the total time, from the beginning of the moulding until the finished vessels are placed in the store room under a sheet, is far in excess of the mere sum of the separate hours and minutes used in each process. Household duties and other tasks are constantly interfering with the work. About nine o’clock on a certain morning one potter began moulding the first of a group of perhaps forty pieces. The scraping was commenced on the morning of the third day, and the polishing on the fourth morning. Nothing was done on the fifth day, but early on the sixth the painting began. A fiesta interrupted the work for two more days, and the burning was done on the morning of the tenth day, although it could have taken place on the seventh. Another potter finished burning several large ollas at noon on the ninth day. PAINTING OF DESIGNS By means of the decorations on the vessels the potter expresses her person- ality. The type of design used by any one potter is very constant, and is distinctly individual. It is a comparatively easy matter, by an inspection of the design alone, to distinguish the vessels made by one potter from those of another. The designs are planned in several different ways. Maria Martinez sits with the bowl in her hands for a few minutes doing nothing; apparently she is working out in her mind the combination of elements which she will use. Designs so con- ceived are generally simple. Maximiliana Martinez begins painting almost at once. While she is working ideas occur to her and are incorporated. Occasionally, after the painting has been completed and the vessel set aside, she will pick it up again to add some detail. This method of working is apt to cause somewhat involved figures. Antonita Roybal, in choosing her designs, refers to drawings of her own, or to photographs which have come into her hands, of old San Ildefonso vessels. This potter uses a pencil to outline very sketchily the design upon the vessel, as an aid in obtaining the proper symmetry. The figures obtained in this manner are usually very elaborate. 1 The first lines drawn in a design are almost without exception the enclosing lines under the rim. These are followed by the enclosing lines near the shoulder (in the case of an olla), or near the bottom of the interior (in the case of a bowl). When the design consists of panels, the vertical division-lines are then added. If there are to be four panels, one division-line is drawn, and then the one on the opposite side of the bowl, dividing the surface into halves. Each of these halves is then bisected. The next step is to double all the vertical division-lines. Occasionally each quadrant is judged by the eye only, and the division lines are drawn in sequence about the vessel. When there are to be either more or less than four panels, they are outlined one after the other. No measuring instrument of any kind is used. After the skeleton of the design has been completed, the outlines of the figure within each panel are drawn. All the lines are first placed in one panel, then the second panel is finished, and so on, until all have been filled with the outlines. All the areas on the vessel that are to be colored black are then filled, followed by the areas which are to be red. The strokes taken in outlining are not always made in the same order in the various panels. Such variation is entirely natural and should be expected in work done without the use of a visible pattern. When a design is attached to the lower enclosing line of a panel, it usually con- sists of a repetition of some small figure of one or two elements. The position of — such added figures has absolutely no relation in the mind of the potter to the panel-design. 1 It is interesting to note that in making the preliminary pencil draft, she uses entirely different strokes from - those made by the brush. PAINTING OF DESIGNS 79 When a design consists of a repetition of figures not enclosed within panels, the painter always refers, before adding another figure, to the amount of the surface as yet unfilled. The correctness of the painter’s judgment is therefore easily determined by the proportions of the last figure in the design as compared with the remaining figures. As a rule, with the product of the present-day potters of San Ildefonso, it is exceedingly difficult to determine in a finished vessel, which of the figures was the last one drawn. In designs which consist of a single figure, or of two or more figures, with several complex elements, the development of the design upon the vessel is necessarily at variance with that described above. As a general rule, each element is completed, including the filling of areas, before the next element is outlined. Similarly, each figure is finished before the next is begun. In considering generally the ornamentation of San Ildefonso vessels, a distinct group-similarity can be observed. The polychrome vessels are painted in black and orange-red upon a white base. The red-ware vessels are decorated only in black. The designs usually consist of several almost identical figures, each com- posed of a small number of rather simple elements, in which curved lines are com- mon. And yet, in spite of this almost indefinable similarity among the vessels, the differences between the designs made by different potters of the village are clear-cut and distinct. Maria Martinez specializes in constricted-mouthed and similarly shaped bowls of polychrome ware. Her lines are relatively narrow, and the black of the design is very uniform in color. She uses panelled designs almost exclusively. The ele- ments within the panels are simple, and few in number. Her work is easily recog- nized because of its simplicity and pleasing composition (see pl. 6). Maximiliana Martinez generally confines herself to red ware in the form of small ollas and small bowls with a slightly constricted lip. Her lines are somewhat wider and more uneven than those of Maria, and the black is of varying shades. As a result of her custom of developing the design as the work progresses, the figures are rather complex and intricate, or, as the Indians themselves say, ““mixed up”. The outstanding char- acteristic of her work is the use of one or more elements entirely detached from the figure proper. Antonita Roybal devotes most of her time to making large ollas of red ware. Her lines are relatively broad, often indeed of double width. Her blacks are also uneven. The designs upon her vessels are usually composed of two or four very large, complex figures, in which spiral curves are conspicuous. Dotting, crosshatching, and filling of many small areas characterize her work. The prod- ucts of a man painter, Julian Martinez, are easily recognized by the abundant use of very narrow lines. The figures, which are usually composed of many intricate elements, impress one with the amount of detailed and careful work lavished upon them. Julian has obviously been strongly influenced by the technique of modern Hopi potters, such as the famous Nampeo, whose work he of course often sees in the curio-stores and in the State Museum at Santa Fe. In the following pages typical designs of Maria, Maximiliana, and Antonita are discussed in detail, with the aid of figures upon which the direction and order of the strokes have been indicated. These drawings are given in order to amplify and clarify the general statements made above. 80 PUEBLO POTTERY MAKING Drawine No. 1 (fig. 9); original by Maria Martinez. This design was on a constricted-mouthed polychrome bowl, and consisted of four identical panels, each four and one-half inches long by two and one-half inches wide. The work was divided into four distinct sections, or stages, each of which was completed in all four panels, one after the other, before the next stage was begun. First stage (fig. 9, a); construction of the framing lines. Lines 1-4 are drawn completely around the bowl; then lines 5-8. The corresponding two pairs of lines are then drawn upon the other half of the bowl, thus dividing the space into four sections. Second stage (fig. 9, b); placing of the outlines within each panel. The first three lines drawn (9-11) divide the panel into three triangles. Then the details are Fic. 9. The growth of a polychrome design as painted by Maria Martinez (the shading indicates red). outlined in each triangle in turn. When the outlining of one panel has been com- pleted, each of the other panels is treated in turn in the same manner. The work of Maria is noteworthy in that the order and direction of the lines and the filling of spaces is hardly ever changed from one panel to the next. Third stage (fig. 9, c); filling certain areas with solid black paint. The largest area (1) is always filled first. No order is followed in filling areas H, II, and IV, and in making the dot (V). In one panel, IV is filled before II, in another V pre- cedes the other three. After this the dots (VI) are placed below line 21. In the different panels the number of these dots varies from six to eight. The last area filled in this stage is the triangle VII. When the first panel has been completed the other three are treated in like manner before the fourth stage is begun. Fourth stage (fig. 9, d); filling of areas with red paint (shown in the reproduction by shading). In some panels area VIII precedes area IX, in others the reverse is the o& ALV Id PAINTING OF DESIGNS 81 case. With the completion of this fourth stage in all the panels, the painting of this comparatively simple design is finished. The time consumed was twenty-five minutes. Drawine No. 2 (pl. 32); original by Maria Martinez. This design may be placed upon either a constricted-mouthed bowl or an olla-bowl. It is made up of five identical panels. During the painting the bowl is turned counterclockwise. There are eleven distinct stages. First stage (pl. 32, a); the enclosing lines of the panels are produced. Each panel is four inches long and one and a half inches wide. The horizontal lines (1-4) are drawn completely around the bowl before the dividing lines (5-8) are drawn. Second stage (pl. 32, b); lines 9 and 10 are drawn, dividing each of the five panels into a semicircle and two triangles. Third stage (pl. 32, c); the plumes are outlined in each of the panels by means of lines 11 to 20. Fourth stage (pl. 32, d); the two triangles (areas I and II) are filled with black pigment. Sometimes area I is filled first, sometimes area II. Fifth stage (pl. 32, e); when the triangles in all five panels have been filled, the dots are placed in two of the five plumes in each panel (areas III and IV). These dots are sometimes six in number, sometimes seven. They are painted from the base of the plume upwards. Sixth stage (p. 32, b); areas V to VII are filled with red pigment, thus com- pleting the panel-design. Seventh stage (pl. 32, g); now that the design in the panel has been finished, the second half of the figure, that below the bottom enclosing line, is begun. A series of small semicircles (lines numbered 21) are appended to the lowest enclosing line. The position of the semicircles bears no relation whatever to the series of panels. Three and a half to four semicircles fall below each panel or a total of from seventeen to twenty in the entire extent of the design as it encircles the vessel. Eighth stage (pl. 32, g); by means of lines 22 and 23, a triangle is outlined below each of the semicircles. Ninth stage (pl. 32, h); a very small semicircle (24) is drawn just below the point of each triangle. Tenth stage (pl. 32, h); another similar semicircle (line 25) is drawn just below line 24. Eleventh stage (pl. 32, i); the triangles (areas numbered VIII) are filled with black pigment. Although this figure is based upon the panel-design, it differs from pure panel- decoration in the use of a series of simple figures appended to the bottom enclosing- line of the panel. The time required to paint this design was thirty-five minutes. Drawine No. 3 (pl. 33); original by Maria Martinez. This design is of an entirely different type, in that there is no use of a panel. It was placed upon a con- stricted-mouthed bowl. First stage (pl. 33, a); the enclosing lines (1, 2) are drawn around the rim of the vessel. These are immediately followed by the three lines (3 to 5) which form the outlines of the five spirals composing the design. The proportions of the figures were 82 PUEBLO POTTERY MAKING determined by constantly watching the position of the first spiral as the bowl was turned counterclockwise. Second stage (pl. 33, b); the outlines of the details (lines 6 to 17 ) are drawn on each spiral in turn. Third stage (pl. 33, c); the outlining is completed by adding to each spiral a horizontal triangle at the base of the curve. It is interesting to note that line 18, the first of the group 18 to 21, was the first one drawn, although it was entirely de- tached at that time from the main figure. Fourth stage (pl. 33, d); the filling of areas is begun by painting the four small triangles on the upward curve of the spiral (areas I toIV). The order in which they are filled is apt to vary with the different spirals. Fifth stage (pl. 33, e); the large triangle at the base of the spiral (area V) is filled with black pigment. Sixth stage (pl. 33, f); the triangle at the bottom (area VI) is filled in each unit. Seventh stage (pl. 33, g); this consists in placing a series of dots along the median line of the leaf-shaped area in the base of the spiral. In the various spirals these dots vary in number from eight to ten. Eighth stage (pl. 33, h); the design is completed by filling the red areas (VIII and IX). In the first spiral so treated, area VIII was filled first, but in all the others area IX preceded area VIII. The base of each spiral is four and one-half inches long. The width of the design is three inches. Drawinc No. 4 (pl. 34); original by Maximiliana Martinez. This rosette was placed in the interior bottom of a small constricted-mouthed bowl of red ware. A cloud-design which was painted on the rim of the same bowl is described and illustrated in fig. 6. First stage (pl. 34, a); the outlines of one set of four leaves are drawn (lines 1-8). Second stage (pl. 34, b); the areas within these enclosing lines are hatched (areas I-IV). These four areas are filled in clockwise rotation. Third stage (pl. 34, c); the same areas (numbered V-VIITI) are crosshatched, starting at the tip of each area and working towards the centre. Fourth stage (pl. 34, d); four more leaves are drawn between the four already made. After lines 9 and 10 are drawn, the area between them is filled with black pigment, leaving an oblique white bar, before lines 11 and 12 are placed upon the vessel. Each of the four leaves is entirely completed before the next is begun. Fifth stage (pl. 34, e); this consists in the placing of four lines (17-20) at the end of each of the four longer leaves. These four groups of lines are drawn upon the design in clockwise rotation. Sixth stage (pl. 34, f); at this point Maximiliana glanced at the drawing which the writer was making in his notes. By accident the ends of the shorter leaves had there been made more pointed than the actual painting. When she saw this, she pointed the tips of these leaves with black to make them correspond in shape to the writer’s drawing. PLATE 33 a. X A Design by Maria Martinez PLATE 34 Design by Maximiliana Martinez i | oe ‘ 4 > s % ml i r 1 , PAINTING OF DESIGNS 83 This is an excellent example of the type of work done by a painter who develops her pattern while drawing it. The contrast between this and the simple strength of the first three designs (fig. 9 and pls. 32, 33) should be noticed. Drawine No. 5 (fig. 10); original by Maximiliana Martinez. This is a border decoration that was applied to the edge of the constricted-mouthed bowl on which was produced Drawing No. 4. First stage (fig. 10, a); this is the drawing of the two enclosing lines (1 and 2) about the lip of the bowl. These are followed at once by 3 to 5, which outline three small semicircles. Eight of these triple semicircles complete the circumference of the bowl. Second stage (fig. 10, b); the three semicircles are filled with dots of pigment, two in each of the upper ones, three in the lower. Third stage (fig. 10, c); the three small lines are added to the lowest of the three semicircles. The painting of the rosette (pl. 34) and the eight sets of semicircles took just sixteen minutes. Drawine No. 6 (pl. 35); original by Antonita Roybal. This elaborate decora- tion was placed upon a large red ware olla. Antonita, it may be noted, specializes a b Fie. 10. Raincloud design by Maximiliana Martinez in vessels of his sort, and her designs, while not slavishly repeated, all have a strong family resemblance, due to her bold use of scrolls and step-figures. The small upper drawing illustrates the method by which the design under consideration is applied to the vessel. In the larger one it is projected flat; the centre circle represents the mouth of the olla. The time taken for painting the various parts of the pattern is incorporated in the description; the total time at the end of each stage being given immediately thereafter. Framework lines. The heavy double-width line forming the middle of the central square is drawn first. Then two narrower lines are drawn, one inside and one outside, thus completing the square (sixteen minutes; 00:00-16:00). The two lines encircling the mouth of the olla are next produced (four minutes; 16 :00-20:00). Neck-design within the square. Each of the four corners of the square is orna- mented with a small scroll-ended element. Each element is first outlined and then filled with black before the next is begun (twelve and one-half minutes; 20:30-32:00). Small irregularly placed spots are then dotted into the remaining surface within the square (six minutes; 33:00-39:00). The medallions. Appended to each of the four corners of the original square is a flower-like medallion. The drawing of each is done as follows. The outer line is 84 PUEBLO POTTERY MAKING first traced, then the inner one. Next the inner part is filled with black, except for a narrow band across the middle. To the exterior ring are added the outlines of the nine radiating elements. As a last step these are filled with black. The olla is then turned counterclockwise and the next medallion is begun. Each medallion is completed more quickly than the last. The time: No. 1, ten minutes (39 :00-49:00); No. 2, eight minutes (49:00-57:00) ; No. 3, seven and one- half minutes (57 :00-64:30); No. 4, six and one-half minutes (64:30-71 :00). The side patterns. Each of the four sides of the square bears a design composed of two scrolls with a double stepped element and two long appendages between them. Each design is completed before the next is begun. The drawing proceeds as follows: 1. The outlining of the scrolls and the drawing of the crossbar between them. 2. The outlining of the central stepped figures. 3. The filling of the stepped figures with black. 4, The outlining of the two long appendages between the scrolls. 5. The filling of the appendages with black, leaving two narrow crossbars in the ground color. 6. The addition of the two small appendages between the stepped figures. 7. The outlining of a central streak ending in a small circle in each of the scrolls. 8. The filling of the scrolls with black, leaving the central streak and small circle in the ground color. As in the case of the medallions, each one of the side patterns is completed more quickly than the last. The time: No. 1, twenty-six minutes (71:00-97 :00) ; No. 2, twenty-two and a half minutes (97 :00-119:30); No. 3, twenty-one and a half minutes (119:30-141:00); No. 4, fourteen and a half minutes (141:00-155 :30). The entire time required for painting the design was thus two hours, thirty-five minutes, and thirty seconds. PLATE 35 Black design on red jar by Antonita Roybal (the small drawing above shows how this design is applied to the olla). SYMBOLISM! Symbolism of one kind or another, plays a very important part in the existence of the Pueblo Indian. It is generally agreed that even the minor acts of everyday life have a certain religious symbolic meaning. For example, the gourd spoons, or kajepes, used in moulding pottery, must apparently be consecrated before they may be used. Similarly, a new technique in pottery making must pass through a period of consecration before it becomes completely established. On the other hand, white men often overemphasize the importance of symbolism in studying any civilization whose customs and philosophy differ radically from their own. In the light of what is known of the mental attitude of the Pueblo Indian, it would not be unreasonable to assume that the designs on their pottery have some symbolical meaning. Whether this symbolism is in any sense religious, or is merely the symbolism of conventionalization of design, is an open question.? It is probable that vessels made before the time when pottery became to some extent an article of commerce between the Indian and the tourist, bore designs of symbolical mean- ing. It may be that the vessels made today for their own use also have such mean- ings, but there is every reason to believe that much of the ware now turned out by the San Ildefonso potters for sale to tourists bears designs of no special meaning. It is true that through bitter experience, the Indians have learned to guard carefully their religious and secular philosophy, and it would require many years of study, living with them, to gain an intimate knowledge of their beliefs. If, however, there are definite meanings associated with the designs upon commercial pottery, the inhabitants of San Ildefonso have become past masters of the art of conceal- ment. An attempt to obtain some idea of the general reason why vessels are decorated and of what was taking place in the mind of the painter while at work, proved wholly fruitless. Inquiries as to the meaning of whole designs, figures, and ele- ments met with three kinds of response. One family, who have enjoyed consider- able contact with investigators of Indian customs, were ready and eager with ex- planations of the meanings of various elements. They could not, however, explain the meaning of the entire design upon any vessel. Other potters met the inquiry with a frank statement of ignorance, such as “I don’t know’’, or “Ask the men, the women don’t know”. A third group exhibited great uncertainty. These people would usually translate the questions into Tewa for the benefit of the rest of the Indians present. Then, after much laughter and discussion, the potter would 1 The subject of symbolism is touched upon in this report only with the greatest diffidence. No two students of Southwestern ceramics seem to entertain the same theory, in all details, upon this subject. The statements made here are given for what they may be worth. The time devoted to the work did not permit of a careful and exhaustive study of the subject. 2 One potter, after glancing at a small vessel which was undoubtedly old, informed the writer that it had once belonged to the “summer people”, a social-religious division of the community. 86 PUEBLO POTTERY MAKING sometimes offer a meaning, at other times say nothing. One old man explained with great gusto that the design which he had just finished upon a small globular olla represented four small clouds sailing across the sky, one behind the other, from west to east. His manner was very similar to that which one of us might adopt in telling an improbable yarn to a particularly guileless listener. Some potters gave meanings for whole figures. Another potter, however, composed her figures as the work advanced, evidently with no clear idea, when she began it, of the ultimate form of the figures and therefore probably with no idea in regard to their meaning. It has been suggested that minor variation in similar figures on the same vessel have some meaning. The more probable explanation would seem to be that these variations are due to the lack of a visible pattern. At one time a potter was distinctly annoyed because she noticed, after completing a figure, that she had filled the wrong part of a small detail. It is equally fallacious to lay too great importance upon alternating figures in a panel design. For example, one potter in filling the areas in a four-panel decora- tion filled the same areas in the first and third panels, and different areas in the second. When she began to fill the areas of the fourth panel in the same way as the first and third, her attention was called to the areas in the second, the order of which she obviously considered a mistake. The result was that the fourth panel was filled as the second had been, thus giving the vessel a panel-design with alter- nating figures. The fact that in excavations no two vessels have ever been found with identical designs has been attributed to something in the Indian’s way of thinking. Yet one potter at San Ildefonso placed upon one constricted-mouthed bowl out of a group of vessels a design identical with that on a bowl of the same shape in the previous group made. Among older pots the “line-break’’, a small space left in the horizontal en- closing-line at the lip of the vessel, is a constant element. At San Ildefonso its use has become almost obsolete but one of the informants did employ it. Careful questioning on the subject with another potter as interpreter, brought out the fact that the line-break is called a “door’’, through which a spirit may enter or depart. Persistent questioning in regard to the nature of the spirit caused an animated discussion among those present. The potter was clearly puzzled by the questions. Then, after a single sentence by her, the Indians all laughed heartily. Finally, the interpreter stated that the potter had said, in effect, that if the door was going to cause all that trouble she would close it. The matter was finally settled by the interpreter, who pointed out a passage in the advertising pamphlet of a Santa Fe curio-dealer which explained that the line-break was a passage through which the spirits of the dead might pass. The ready answers given by some potters in response to inquiries as to the meaning of elements of a design, seem to show that the elements are actually conventionalized symbols of definite objects. In one instance the potter, on noticing a dance-costume lying on the bed, pointed out certain parts of it, and then drew the elements representing those parts. Other potters simply deny all knowledge of the meaning of elements. Still others by their hesitancy, seem to SYMBOLISM 87 grope for a plausible meaning and offer the first which occurs to them. Whether the elements do represent definite objects or not, it nevertheless remains a fact that the meanings given cause apparent contradictions. ‘To elements essentially the same widely different meanings are often given and, conversely, the same idea or object Fic. 11. Elements of design commonly used by the potters of San Ildefonso. is often represented by entirely different elements. This is also true of more com- plex figures. The elements illustrated in figure 11, give examples of the type of idea or object said to be represented, and incidentally illustrate some of the contradictions spoken of above. Numbers 1 and 6 both refer to hills. On the other hand, No. 7 88 PUEBLO POTTERY MAKING is a mountain, although it bears little resemblance to the “hills”. It resembles more closely No. 2 which one informant described as a pueblo and another as a kiva. The same regular zigzag appears in No. 12, which represents a tablita, or dance mask, with small feathers tied to the points of the zigzags. No. 17, in which the zigzag also appears, represents kiva-steps. Nos. 11 and 16 represent feathers, and No. 21 is a bunch of feathers on the end of a dance-pole. But No. 22 represents the poles of the kiva-ladder, and No. 3 is rain, which is falling a long way off. No. 10 represents fringed woolen armlets, and yet there is as close a resemblance between Nos. 3 and 10, as there is between Nos. 14 and 19, both of which represent the tassels on a man’s dance-belt. No. 8 is called rain-water, but a single spiral, as in No. 25, is a buffalo horn. The dots of No. 13 represent rain-drops in dust, but in No. 21 the dots are markings on feathers, and in No. 15 they represent a procession of bugs on the rib of a leaf. No. 18 represents water dripping through a hole in the roof and making a small cuplike depression in the floor, represented by a semicircle, or a whole circle with a dot in the centre of it; but No. 23, which is also a triangle, is called a leaf, as is also the case with No. 15. And yet No. 4 is also a leaf, although if placed horizontally it more closely resembles the clouds represented in No. 5. But No. 9 is also a cloud, this time a big black cloud with an open space in it through which a small cloud may be seen. Nos. 20 and 24 represent respectively the sun and a star. In the light of the small amount of material obtained on the subject of sym- bolism, all that can be said is that the evidence is purely negative. If the elements do represent definite ideas and objects, which seems to the writer improbable, the meanings are so deeply hidden that only an intensive specialized study will result in an acceptable solution. MEANING OF ELEMENTS (M.— Maria. A.— Antonita) 1] —“‘hillside’’, M. 14 —‘“‘tassel on man’s dance-belt”’, M. 2 —“pueblo”, M.; “kiva’’, A. 15 —“‘leaf with bugs on it”’, M. 3 —“rain falling far away”’, A. 16 —‘‘feather’’, M. 4 —“‘leaf”, M. 17 —‘‘kiva-steps, the two small points fire- 5 —“‘clouds’’,, M.; A. places’’, A. 6 —“hill”, M. 18 —‘“‘water dripping through holes in roof 7 —‘mountain”’, M. and making holes in dirt floor’, M. 8 —“‘rainwater’’, A. 19 —‘“‘tassel on man’s dance-belt”’, M. 9 —“black cloud with open space through 20 —“sun”’, A. which one can see a small cloud”, A. 21 —“‘feathers on dance-pole, spots aremark- 10 —“‘fringed woolen dance armlets”, M. ings on feathers”’, M. 11 —“‘feather’’, M. 22 —‘‘ladder-poles”’, A. 12 —“tableta (wooden headdress) with 23 —“‘leaf”, M. feathers on points’’, M. 24 —“star’’, A. 13 —“‘rain-drops on dust”’, A. 25 —‘‘buffalo horn”’, A. BIBLIOGRAPHY Binns, C. F. 1910. ‘The potter’s craft. New York, 1910. HarRINGTON, J. P. 1916. The ethnogeography of the Tewa Indians. Twenty-ninth Report of the Bureau of American Ethnology. Washington, 1916. 1916, a. Ethnobotany of the Tewa Indians (In collaboration with W. W. Robbins and B. Friere-Marreco). Bulletin 55, Bureau of American Ethnology. Washington, 1916. Hotes, W. H 1886. Pottery of the ancient Pueblos. Fourth Report of the Bureau of Ethnology, pp. 257-360. Washington, 1886. Kipper, A. V. 1924. An introduction to the study of Southwestern archaeology, with a preliminary account of the excavations at Pecos. Papers of the Phillips Academy South- western Expedition, no. 1. New Haven, 1924. Kipper, M. A. and A. V. 1917. | Notes on the pottery of Pecos. American Anthropologist, n.s., vol. 19, no. 3, pp. 325-360. Lancaster, 1917. STEVENSON, J. 1883. Illustrated catalogue of the collections obtained from the Indians of New Mexico and Arizona in 1879. Second Report of the Bureau of Ethnology, pp. 307-465. Washington, 1883. 1884. Illustrated catalogue of the collections obtained from the pueblos of Zufii, New Mexico, and Wolpi, Arizona, in 1881. Third Report of the Bureau of Ethnology, pp. 511-594. Washington, 1884. STEVENSON, M. C. 1904. The Zufii Indians, their mythology, esoteric fraternities, and ceremonies. Twenty-third Report of the Bureau of American Ethnology. Washington, 1904. 1915. Ethnobotany of the Zufii Indians. Thirtieth Report of the Bureau of American Ethnology, pp. 31-102. Washington, 1915. Wooron, E. O. AND STANDLEY, Paut C. 1915. Flora of New Mexico. Contributions from the United States National Herbarium, Vol. 19. Washington 1915. “ ~ GETTY RESEARCH INSTITUTE ITN 3 3125 01188 6914 = Sea . Re Rep ts eR > a :